Low-temperature boron-free paper starch adhesive and preparation method thereof

A technology of starch adhesives and adhesives, applied in the direction of starch-derived adhesives, adhesive additives, adhesive types, etc., can solve problems such as poor adhesion of high-strength sizing corrugated paper, and achieve fast drying and long-term storage Long and simple production process

Inactive Publication Date: 2016-01-20
中山振兴纸品制造有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to overcome the deficiencies in the prior art, the present invention provides a method that can quickly bond corrugated cardboards at room temperature or low temperature during the production process, simplify the glue mixing process, solve the problem of poor bonding of high-strength sizing corrugated paper, and improve the adhesive strength. Non-toxic and harmless, low-temperature boron-free paper starch adhesive and preparation method thereof, low-temperature environmental protection, low-carbon and environmental protection, non-toxic and harmless, low-temperature boron-free paper starch adhesive

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-temperature boron-free paper starch adhesive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Example 1: Special adhesive for single-facer of corrugated cardboard production line

[0038] Components and parts by weight are: 100 parts of corn starch, 380 parts of water, 2.4 parts of potassium permanganate, 0.5 parts of sodium fatty acid, 2.2 parts of oxalic acid, 0.3 parts of tributyl phosphate, 11 parts of sodium hydroxide, sodium trimetaphosphate 1.7 parts and 5 parts of drier, wherein the drier is a mixture of 2 parts of melamine-formaldehyde resin, 1.5 parts of light calcium carbonate, and 1.5 parts of bentonite.

[0039] The preparation method of above-mentioned embodiment 1 formula adhesive is as follows:

[0040] 1. Add 130 parts of water (normal temperature) to the reactor, and add 100 parts of cornstarch under stirring.

[0041] 2. Add oxalic acid (H 2 C 2 o 4 ) 2.2 parts are stirred evenly, and 2.4 parts of potassium permanganate (KMnO 4) was dissolved in about 25 parts of hot water at 40-70°C to make a potassium permanganate solution, and the pot...

Embodiment 2

[0044] Example 2: Special adhesive for double-sided machine in corrugated cardboard production line

[0045] Components and parts by weight are: 100 parts of corn starch, 320 parts of water, 2.6 parts of potassium permanganate, 0.8 parts of sodium fatty acid, 2 parts of oxalic acid, 0.5 parts of tributyl phosphate, 8 parts of sodium hydroxide, sodium trimetaphosphate 1.2 parts, 3 parts of drier, wherein the drier is a mixture of 1 part of melamine-formaldehyde resin, 1 part of light calcium carbonate, and 1 part of bentonite.

[0046] The preparation method of above-mentioned embodiment 2 adhesive is as follows:

[0047] 1. Add 120 parts of water (normal temperature) to the reactor, and add 100 parts of cornstarch under stirring.

[0048] 2. Add 2 parts of oxalic acid and stir evenly. Dissolve 2.6 parts of potassium permanganate in about 25 parts of hot water at 40-70°C to make a potassium permanganate solution. Slowly drop the potassium permanganate solution into the react...

Embodiment 3

[0051] Example 3: Commonly used adhesives for mounting paper

[0052] Components and parts by weight are: 100 parts of corn starch, 400 parts of water, 2.3 parts of potassium permanganate, 0.5 parts of sodium fatty acid, 2.4 parts of oxalic acid, 0.4 parts of tributyl phosphate, 12 parts of sodium hydroxide, sodium trimetaphosphate 1.8 parts, 4 parts of drier, wherein the drier is a mixture of 2 parts of melamine-formaldehyde resin, 1 part of light calcium carbonate, and 1 part of bentonite.

[0053] The preparation method of above-mentioned embodiment 3 adhesive is as follows:

[0054] 1. Add 150 parts of water (normal temperature) to the reactor, and add 100 parts of cornstarch under stirring.

[0055] 2. Add 2.4 parts of oxalic acid and stir evenly, dissolve 2.3 parts of potassium permanganate in about 25 parts of 40-70 ℃ hot water to make a potassium permanganate solution, slowly drop the potassium permanganate solution into the reaction kettle, drop After entering, th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a low-temperature boron-free starch adhesive for paper products and a preparation method thereof. The components and parts by weight of the adhesive are: 100 parts of corn starch, 320-400 parts of water, and 2.3-400 parts of potassium permanganate. 2.6 parts, 0.5-0.8 parts of sodium fatty acid, 2-2.4 parts of oxalic acid, 0.3-0.5 parts of tributyl phosphate, 8-12 parts of sodium hydroxide, 1.2-1.8 parts of sodium trimetaphosphate, 3-5 parts of drier, The adhesive with this formula has a simple production process and does not require heating. It only takes 40-50 minutes from feeding to the finished product. The adhesive cartons dry quickly, have high strength, do not run rough, do not absorb moisture, do not flood, and do not pan-alkali , long storage period, the viscosity remains unchanged after storage for 3 months, no mildew and precipitation, initial adhesion is 1-1.5min, full adhesion is 5-10min, fiber damage is 30-50s, the relevant physical and chemical indicators are better than the national standard requirements, and can be widely used Corrugated boxes for general commodity packaging and corrugated boxes for food packaging.

Description

technical field [0001] The invention relates to an adhesive, in particular to a starch adhesive for corrugated cardboard production line, laminating paper, carton or cardboard and other adhesive paper products. Background technique [0002] my country's corrugated packaging industry is an industry with large scale, high energy consumption and large pollution sources. Traditional corrugated cardboard production needs to use high temperature to gelatinize starch raw glue for cardboard bonding. Usually, 8-12 kg of steam pressure is required. Most of the steam is supplied by coal-fired boilers, which not only consumes a lot of energy, but also pollutes the combustion emissions. environment. [0003] In addition, there are problems in the industry such as poor adhesion of high-strength sized corrugated paper, complex glue-making process, poor glue stability, slow drying speed, and poor moisture resistance of the glued film, which have become technical problems that the industry ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09J103/10C09J11/06C09J11/04
Inventor 李彭郑新张莉琼
Owner 中山振兴纸品制造有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap