Wear-resisting coating

A technology for wear-resistant coatings and raw materials, applied in the field of wear-resistant coatings, can solve the problems of low cost and high wear resistance, and achieve the effects of increasing wear resistance, improving scratch resistance, and increasing scratch resistance.

Active Publication Date: 2014-04-23
ANHUI JINDUN PAINT
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the research field of the global modern coatings industry and technology, wear-resistant coatings account for 25-35%, and have become the focus of research and development in the field of new coatings around the world. It has been unable to meet the demand. How to prepare a coating with high wear resistance, low cost and simple preparation method has become a technical problem that needs to be solved at present.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A kind of wear-resistant coating, its raw material comprises by weight:

[0015] 23.5 parts of vinyltriisopropoxysilane, 4.7 parts of silica airgel, 15.8 parts of trioxane, 8.4 parts of water, 3.3 parts of acetic anhydride, 15 parts of acetylcholine, polyoxyethylene sorbitan mono 0.13 parts of glyceride, 14.6 parts of crystalline silicon oxide, 8.4 parts of graphite powder;

[0016] Wherein, the porosity of the silica airgel is 75-79%, and the graphite powder is natural flake graphite.

Embodiment 2

[0018] A kind of wear-resistant coating, its raw material comprises by weight:

[0019] 20.9 parts of vinyltriisopropoxysilane, 3.8 parts of silica airgel, 17.4 parts of trioxane, 7.7 parts of water, 4.6 parts of acetic anhydride, 13.4 parts of acetylcholine, polyoxyethylene sorbitan mono 0.21 parts of glyceride, 13.5 parts of crystalline silicon oxide, 11.6 parts of graphite powder;

[0020] Wherein, the porosity of the silica airgel is 75-79%, and the graphite powder is composed of highly oriented pyrolytic graphite and graphite particles of 3-9 μm.

Embodiment 3

[0022] A kind of wear-resistant coating, its raw material comprises by weight:

[0023] Vinyl triisopropoxysilane 29 parts, silica airgel 4.8 parts, trioxane 19.4 parts, water 5.6 parts, acetic anhydride 6.2 parts, acetylcholine 10.8 parts, polyoxyethylene sorbitan mono 0.28 parts of glyceride, 10.4 parts of crystalline silicon oxide, 12.7 parts of graphite powder;

[0024] Wherein, the porosity of the silica airgel is 75-79%, and the graphite powder is composed of brushed graphite and natural flake graphite.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
porosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a wear-resisting coating. The wear-resisting coating comprises the following raw materials in parts by weight: 20-30 parts of vinyl triisopropoxysilane, 3-5 parts of silicon dioxide aerogel, 15-20 parts of trioxane, 5-9 parts of water, 3-7 parts of acetic anhydride, 10-15 parts of acetylcholine, 0.1-0.3 part of polyoxyethylene anhydro-sorbit monoglyceride, 10-15 parts of crystallizing silicon oxide, and 7-13 parts of graphite powder, wherein the porosity of the silicon dioxide aerogel is 75-79%, and the weight ratio of silicon dioxide aerogel to vinyl triisopropoxysilane is 1:(5-7). The wear-resisting coating can improve the degree of crosslinking of a coating and enhance the resistance to scratching, and has low cost.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a wear-resistant coating. Background technique [0002] With the development of modern science and technology, artificial satellites, spacecraft, high-speed trains, impellers of steam turbines and engines, propellers of ships, blades of hydroelectric generators, decks of ships, floors of buildings, road marking paint, etc. The erosion of high-speed airflow, sand and water flow and the action of mechanical force make the wear of the material very serious. In order to prolong the service life, the surface of the material needs to be coated with wear-resistant coatings. Wear-resistant coatings are the core of the new coating field. The development of technology plays an important role in promoting and supporting. In the research field of the global modern coatings industry and technology, wear-resistant coatings account for 25-35%, and have become the focus of research and develop...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/00C09D7/12
Inventor 朱恒横梅长林张国胜
Owner ANHUI JINDUN PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com