Preparation method of maleic anhydride containing TPR (Thermal Plastic Rubber) surface treating agent

Inactive Publication Date: 2014-05-07
HANGZHOU DIANZI UNIV
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The toluene solution of trichloroisocyanuric acid can have a good bonding effect after treating TPR, but it is unstable and needs to be prepared temporarily, and it is easy to make the surface of the material turn yellow and affect the appearance.
Li Weiguang developed a TPR material surface treatment agent prepared with methyl methacrylate and graft copolymer solution with SBS rubber [Adhesive, 2002, 23 (3) 19], in which toluene is a moderately toxic Solvents can accumulate in the human body, long-term exposure can cause respiratory diseases, neurological diseases and even leukemia, etc., causing serious harm to the health of workers in production and use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-1

[0015] Add 100g butanone, 20g ethyl acetate, 20g methyl methacrylate, 3g maleic anhydride and 50g SBS rubber to the reaction flask equipped with a thermometer, a nitrogen-passing device, a mechanical stirring device, a vacuuming device and a condenser and stir, The control temperature was 60°C; after the SBS rubber and maleic anhydride were completely dissolved, nitrogen was charged into the reaction flask, and the temperature was raised to 80°C, and a mixed solution of 1.5g benzoyl peroxide and 20g methacrylic acid was added dropwise, Carry out the polymerization reaction for 3 hours; cool down to 50 ° C, remove 50% of the solvent of the system by vacuum distillation, then add 10wt% triethylamine aqueous solution to the pH value of the system to 6.5, and react for 0.5 hour; gradually add 600g deionization under high-speed stirring Water to obtain SBS grafted maleic anhydride copolymer emulsion.

Embodiment 1-2

[0017] 110g butanone, 30g ethyl acetate, 40g methyl methacrylate, 10g maleic anhydride and 30g SBS rubber were added to the reaction flask equipped with a thermometer, a nitrogen-passing device, a mechanical stirring device, a vacuum pumping device and a condenser for stirring. , the control temperature is 70 ℃; after the SBS rubber and maleic anhydride are completely dissolved, nitrogen is charged into the reaction flask, and the temperature is raised to 90 ℃, and the mixed solution of 2.5g benzoyl peroxide and 40g acrylic acid is added dropwise, and the Polymerization reaction 5 hours; Cool down to 60 ℃, remove the solvent of 80% of the system by vacuum distillation, then add 10 wt% dimethylaminoethanol aqueous solution to the pH value of the system to be 8.5, react for 1 hour; Under high-speed stirring, gradually add 800g to remove Ionized water is used to obtain SBS grafted maleic anhydride copolymer emulsion.

Embodiment 1-3

[0019] In a reaction flask equipped with a thermometer, a nitrogen-passing device, a mechanical stirring device, a vacuuming device and a condenser tube, a weight of 115 g of butanone, 25 g of ethyl acetate, 30 g of methyl methacrylate, 6 g of maleic anhydride and 40 g of SBS rubber was added to carry out Stir, and control the temperature to be 65 ° C; after the SBS rubber and maleic anhydride are completely dissolved, fill the reaction flask with nitrogen, heat up to 85 ° C and add a mixed solution of 2.0g benzoyl peroxide and 30g acrylic acid by dropwise addition, Carry out the polymerization reaction for 4 hours; be cooled to 55 ℃, remove 60% of the solvent of the system by distillation under reduced pressure, then add 10 wt% triethylamine aqueous solution to the pH value of the system to be 7.5, and react for 40 minutes; under high-speed stirring, gradually add 700g to remove Ionized water is used to obtain SBS grafted maleic anhydride copolymer emulsion.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of a maleic anhydride containing TPR (Thermal Plastic Rubber) surface treating agent. The method comprises the following steps of: preparing SBS (Styrene Butadiene Styrene) grafted maleic anhydride copolymer emulsion and chlorinated polypropylene grafted copolymer emulsion; uniformly agitating 100 parts by weight of SBS grafted maleic anhydride copolymer emulsion, 20 to 80 parts by weight of chlorinated polypropylene grafted copolymer emulsion, and 10 to 15 parts by weight of polyvinylpyrrolidone, so as to obtain the water-based surface treating agent for the TPR sole material. According to the preparation method, the SBS grafted maleic anhydride copolymer emulsion and chlorinated polypropylene grafted copolymer emulsion are compounded, and the obtained water-based surface treating agent shows high compatibility with the TPR material because of maleic anhydride and chlorinated polypropylene, also shows a good effect on surface treating of the TPR material, meets the adhering requirements of the shoes manufacturing industry, and also realizes the requirements on green and environmental protection.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and relates to a preparation method of a surface treatment agent, in particular to a preparation method of an aqueous surface treatment agent for a TPR sole material used with a shoe adhesive in cold-bonded shoemaking. Background technique [0002] Thermoplastic elastomer (also known as thermoplastic rubber) is made of symmetrical block styrene-butadiene rubber (SBS rubber) as the main body and processed with other materials. It is a polymer material with high elasticity and can be plasticized at high temperature. It is also the so-called third-generation rubber after natural rubber and synthetic rubber, abbreviated as TPR. Because of its wear resistance, easy processing and low price, it is widely used as The sole material, especially the middle and high-grade sports sole material. However, due to its weak polarity, in the cold-bonded shoe industry, in order to improve the bond...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L51/00C08L51/06C08L39/06C08F287/00C08F255/02C08F222/06C08F220/14C08F220/06C08J7/04
Inventor 聂秋林
Owner HANGZHOU DIANZI UNIV
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com