Boron-containing seamless pipe line pipe for ocean oil and gas exploitation

A seamless line pipe, oil and gas technology, applied in the field of seamless line pipe, can solve the problems of line pipe failure and scrapping, and achieve the effects of reducing the γ-α phase transition temperature, expanding the γ phase region, and improving toughness

Active Publication Date: 2014-05-21
JIANGSU CHANGBAO STEELTUBE CO LTD
View PDF2 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Commonly used X52 steel grade seamless line pipes are prone to internal and external corrosion, low-temperature impact and external force in...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Boron-containing seamless pipe line pipe for ocean oil and gas exploitation

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A boron-containing seamless line pipe for offshore oil and gas development, its chemical elements and their mass percentages are as follows:

[0022] C: 0.09%;

[0023] Si: 0.23%;

[0024] Mn: 1.6%;

[0025] Mo: 0.15%;

[0026] Ni: 0.15%;

[0027] B: 0.0015%;

[0028] Cr: 0.2%;

[0029] Nb: 0.06%;

[0030] P:0.012%;

[0031] S:0.003%;

[0032] Cu:0.25%;

[0033] V: 0.015%;

[0034] Al: 0.04%;

[0035] The rest is Fe and other unavoidable impurities.

[0036] A method for manufacturing a boron-containing seamless line pipe for offshore oil and gas development, the steps of the method are as follows:

[0037] a) Steel scrap, pig iron and ingredients are smelted and cast to obtain the tube blank, and in the process, ensure that the chemical elements of the boron-containing seamless line pipe for offshore oil and gas development meet the above mass percentage requirements: scrap steel, pig iron and The ingredients are first smelted in an electric furnace, followe...

Embodiment 2

[0043] A boron-containing seamless line pipe for offshore oil and gas development, its chemical elements and their mass percentages are as follows:

[0044] C: 0.13%;

[0045] Si: 0.35%;

[0046] Mn: 1.2%;

[0047] Mo: 0.25%;

[0048] Ni: 0.2%;

[0049] B: 0.0025%;

[0050] Cr: 0.23%;

[0051] Nb: 0.04%;

[0052] P:0.01%;

[0053] S:0.005%;

[0054] Cu:0.35%;

[0055] Al: 0.03%

[0056] The rest is Fe and other unavoidable impurities.

[0057] A method for manufacturing a boron-containing seamless line pipe for offshore oil and gas development, the steps of the method are as follows:

[0058] a) Steel scrap, pig iron and ingredients are smelted and cast to obtain the tube blank, and in this process, ensure that the chemical elements of the boron-containing seamless line pipe for offshore oil and gas development meet the above-mentioned mass percentage requirements: scrap steel, pig iron The ingredients and ingredients are first smelted in the electric furnace, foll...

Embodiment 3

[0064] A boron-containing seamless line pipe for offshore oil and gas development, its chemical elements and their mass percentages are as follows:

[0065] C: 0.15%;

[0066] Si: 0.3%;

[0067] Mn: 1%;

[0068] Mo: 0.4%;

[0069] Ni: 0.2%;

[0070] B: 0.002%;

[0071] Cr: 0.15%;

[0072] Nb: 0.02%;

[0073] P:0.01%;

[0074] S:0.006%;

[0075] Cu:0.4%;

[0076] Al: 0.04%;

[0077] The rest is Fe and other unavoidable impurities.

[0078] A method for manufacturing a boron-containing seamless line pipe for offshore oil and gas development, the steps of the method are as follows:

[0079] a) Steel scrap, pig iron and ingredients are smelted and cast to obtain the tube blank, and in this process, ensure that the chemical elements of the boron-containing seamless line pipe for offshore oil and gas development meet the above-mentioned mass percentage requirements: scrap steel, pig iron The ingredients and ingredients are first smelted in the electric furnace, followed ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a boron-containing seamless pipe line pipe for ocean oil and gas exploitation. The boron-containing seamless pipe line pipe is characterized by comprising the following chemical elements by weight percent: 0.09 to 0.19 percent of C, 0.23 to 0.38 percent of Si, 0.9 to 1.7 percent of Mn, 0.0015 to 0.0025 percent of B, 0.01 to 0.07 percent of Nb, less than or equal to 0.012 percent of P, less than or equal to 0.007 percent of S and the balance of Fe and unavoidable impurities. The boron-containing seamless pipe line pipe is high in tensile strength, good in welding property, excellent in salt water and acid environmental corrosion resistance and good in low-temperature impact resistance, the low-temperature impact resistance can reach 100J under the condition of minus 70 DEG C, and the boron-containing seamless pipe line pipe has the characteristic of high flexibility; by adopting the way for combining hot rolling and tempering heat treatment, the strength can reach the grade of more than 80ksi.

Description

technical field [0001] The invention relates to a boron-containing seamless line pipe for offshore oil and gas development, belonging to the technical field of seamless line pipes. Background technique [0002] At present, with the recovery of the world economy and the continuous expansion of the economic development scale of developing countries, especially the rapid development of China's economy, the world's energy and transportation have entered an extremely tense situation. Conduct new feasibility study report and new pipeline laying plan. It is estimated that in the next 10 to 15 years, the total global energy consumption will increase by about 60% compared with the present, and the consumption of natural gas will double. [0003] CO emissions from natural gas 2 Less, so the current trend of energy use is a steady transition from oil to natural gas. Different from oil transportation, high-pressure operation is used in the gas transportation process, which can improve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/12C22C38/58C22C38/54C22C38/38C22C38/32C22C38/16C22C38/14
Inventor 许才斌郑臻高建昌於宝祥汪勇李珺张劲松王燕萍
Owner JIANGSU CHANGBAO STEELTUBE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap