Application and preparing method of macromolecular self-sealing hot melt adhesive

A self-sealing, polymer technology, applied in coatings, rosin coatings, etc., to prevent gas leakage in automobile tires, superior elasticity and ductility, and improve driving safety

Inactive Publication Date: 2014-05-28
LUOYANG JUNTENG ENERGY TECH
View PDF6 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to solve the above-mentioned problems, relevant manufacturers, research institutes and institutes have tried hard to find a solution, but no suitable polymer self-sealing hot melt adhesive has been found for a long time.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] The proportion and components of the polymer self-sealing hot melt adhesive (in weight% as the standard) 48% thermoplastic elastomer, 43% tackifier, 8% plasticizer, antioxidant and antioxidant total 1%; weigh the thermoplastic Elastomer SIS 660g, thermoplastic elastomer SBS 300g; tackifier: terpene resin 600g, C5 petroleum resin 260g; plasticizer: naphthenic oil 120g, dibutyl phthalate (DBP) 40g; antioxidant 101010g, Anti-aging agent RD 10g.

[0039] The preparation method is: use material crushing equipment to crush solid materials into <150 mesh particles; use continuous mixing equipment planetary mixer to uniformly mix the pulverized solid materials and liquid materials, and measure and bag them after mixing.

Embodiment 2

[0041] The proportion and components of the polymer self-sealing hot melt adhesive (based on weight %) 50% thermoplastic elastomer, 42% tackifier, 7% plasticizer, 1% antioxidant; weigh 800g of thermoplastic elastomer SIS , Thermoplastic elastomer SBS 100g, Thermoplastic elastomer SEBS 100g; Tackifier: terpene resin 500g, C5 / C9 petroleum resin 340g; Plasticizer: naphthenic oil 100g, diisobutyl phthalate (DIBP) 40g ; Antioxidant 107610g, antioxidant 300 10g.

[0042] The preparation method is: use material crushing equipment to crush solid materials into <150 mesh particles; use the continuous mixing equipment propeller stirrer to uniformly mix the crushed solid materials and liquid materials, and measure and bag them after mixing.

Embodiment 3

[0044] The proportion and components of the polymer self-sealing hot melt adhesive (in weight% as the standard) 49% thermoplastic elastomer, 45% tackifier, 5% plasticizer, antioxidant and antioxidant total 1%; weigh thermoplastic Elastomer SIS 580g, Thermoplastic Elastomer SEBS 400g; Tackifier: Coumarone resin 200g, Petroleum resin (C5 / C9) 500g, Rosin glyceride 200g; Plasticizer: Naphthenic oil 50g, Phthalate diisophthalate Butyl ester (DIBP) 50g; antioxidant 4010A 10g, antioxidant 30010g.

[0045] The preparation method is: use material crushing equipment to crush solid materials into <150 mesh particles; use continuous mixing equipment high-shear disperser to uniformly mix the crushed solid materials and liquid materials, and measure and bag them after mixing.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses application and preparing method of a macromolecular self-sealing hot melt adhesive which is used for an automobile tire. The macromolecular self-sealing hot melt adhesive is sprayed on the whole or the crown part of the inner wall surface of the automobile tire through a hot melt spray technology, and a uniform coating which is more than 3.5 mm in thickness is formed, wherein the macromolecular self-sealing hot melt adhesive consists of the following ingredients according to ratio by weight: 40-60% of thermoplastic elastomer, 34-51% of a tackifier, 5-8% of a plasticizer and 0.5-1.5% of an anti-ageing agent / antioxidant. The macromolecular self-sealing hot melt adhesive is sprayed on the inner wall of the tire, any destructive processing is not required to be carried out on the inner wall of the tire, and the removal washing of a mold release agent and drying processing are carried out on the inner wall of the tire only, the tire can be updated into a such tire capable of normally working in a range from the low temperature of -40 DEG C to the high temperature of 120 DEG C, and the tire has bullet-proof, leakage-proof and stab-proof performance.

Description

Technical field [0001] The invention relates to the use of a polymer self-sealing hot melt adhesive and a preparation method thereof, which are used for the safety upgrade of ordinary automobile tires. Background technique [0002] At present, there are two types of car wheels used in vehicles, one with tube wheels and the other with tubeless wheels. At present, almost all of the passenger vehicles use tubeless wheels, and the national requirements for heavy vehicles are gradually promoted. Use tubeless car wheels. Because tubeless car wheels have the advantages of good heat dissipation, softness, sealing, riding comfort, good performance and long time between inflation and use, but when tubeless car wheels are punctured by sharp objects, the sharp objects remain in the car. In the tire body, the high-pressure gas of the car wheel tire will leak or blow out at the puncture site; when the sharp object pierces the car tire and separates from the car tire, the high-pressure gas ins...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D153/02C09D145/00C09D157/02C09D193/04C09D145/02C09D7/12
Inventor 周仁福王自新刘宽亮史惠娟周强
Owner LUOYANG JUNTENG ENERGY TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com