A technology of stone paper and heavy calcium carbonate, which is applied in the field of preparation of new paper materials, can solve the problems of three wastes polluting the environment, and achieve the effects of improving economic benefits, reducing costs, and small differences in tear strength

Inactive Publication Date: 2014-06-04
GUANGXI SUYUAN INVESTMENT
View PDF16 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, the traditional papermaking process using plant fibers as raw materials produces three wastes that seriously pollute the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] 1. According to the following raw materials and proportions: 90 parts of heavy calcium carbonate, 2 parts of high-density polyethylene, 2 parts of metallocene polyethylene, 2 parts of aluminate, 1.0 parts of polyethylene wax, 1.0 parts of stearic acid, 1.0 parts of antioxidant, 1.0 parts of EBS. Prepare various raw materials in place.

[0048] 2. Production is carried out according to the following process: firstly, the above-mentioned water content is 0.3%, the specification is 800 mesh heavy calcium carbonate and surface treatment agent polyethylene wax, stearic acid, antioxidant, EBS and coupling agent The aluminate is sent into the high-speed mixer in sequence and stirred evenly at high speed, the purpose is to use the surface treatment agent and coupling agent to activate and modify the calcium carbonate; then add the density of 0.95 g / cm 3 , high-density polyethylene with a hardness of 65 and a density of 0.935 g / cm 3 , The melting point is 130°C metallocene pol...

Embodiment 2

[0050] 1. According to the following raw materials and proportions: 80 parts of heavy calcium carbonate, 10 parts of high-density polyethylene, 5 parts of metallocene polyethylene, 1.8 parts of aluminate, 0.7 parts of polyethylene wax, 0.8 parts of stearic acid, Antioxidant 0.7 part, EBS 1.0 part. Prepare various raw materials in place.

[0051] 2. Production is carried out according to the following process flow: first, the above-mentioned water content is 0.25%, the specification is 1250 mesh heavy calcium carbonate and the surface treatment agent polyethylene wax, stearic acid, antioxidant, EBS and coupling agent The aluminate is sent into the high-speed mixer in sequence and stirred evenly at high speed, the purpose is to use the surface treatment agent and coupling agent to activate and modify the calcium carbonate; then add the density of 0.95 g / cm 3 , high-density polyethylene with a hardness of 65 and a density of 0.935 g / cm 3 , Melting point is 130 ℃ metallocene pol...

Embodiment 3

[0053] 1. According to the following raw materials and proportions: 75 parts of heavy calcium carbonate, 14 parts of high-density polyethylene, 8 parts of metallocene polyethylene, 1.0 part of aluminate, 0.5 parts of polyethylene wax, 0.5 parts of stearic acid, Antioxidant 0.5 part, EBS 0.5 part. Prepare various raw materials in place.

[0054] 2. Production is carried out according to the following technological process: first, the above-mentioned water content is 0.2%, the specification is 1000 mesh heavy calcium carbonate and the surface treatment agent polyethylene wax, stearic acid, antioxidant, EBS and coupling agent The aluminate is sent into the high-speed mixer in sequence and stirred evenly at high speed, the purpose is to use the surface treatment agent and coupling agent to activate and modify the calcium carbonate; then add the density of 0.95 g / cm 3 , high-density polyethylene with a hardness of 65 and a density of 0.935 g / c m 3 , Melting point is 130 ℃ metallo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
melting pointaaaaaaaaaa
hardnessaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of preparation of novel paper, and specifically to stone paper and a preparation method thereof. The stone paper specifically includes the raw materials of coarse whiting, high density polyethylene, metallocene polyethylene, aluminic ester, polyethylene wax, stearic acid, an antioxidant, and EBS. A process flow is as below: first, evenly stirring coarse whiting and surface treatment agents ethylene wax, stearic acid and EBS, and a coupling agent aluminic ester together in a high-speed mixer through high speed stirring, and modifying the coarse whiting by using the surface treatment agents and coupling agent; then adding the high density polyethylene and metallocene polyethylene, and mixing by stirring; after combination of the above raw materials, conducting extrusion granulation, extrusion casting, three-roll press polish, biaxial tension and corona treatment on the polymer to obtain the stone paper. Biaxial tension process realizes the small difference of tear strength at vertical and horizontal directions of the paper material, and realizes the reduction of original paper density to expand the paper material area, thereby reducing the cost and increasing economic benefit.

Description

technical field [0001] The invention relates to the technical field of preparation of a novel paper material, in particular to a stone paper and a preparation method thereof. technical background [0002] Traditional paper materials are mostly made of plant fibers such as wood as raw materials. With the increasing scarcity of deep forest resources, the raw materials for papermaking are limited to a large extent, and the production cost is also rising steadily. In addition, the traditional papermaking process using plant fibers as raw materials produces three wastes that seriously pollute the environment. [0003] With the rapid development of science and technology, papermaking technology is also changing with each passing day. Calcium carbonate, the most abundant mineral resource in the earth's crust, is used as the main raw material, and polymer materials and various inorganic substances are used as auxiliary materials. Using the principle of polymer interface chemistry ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/04
Inventor 曹修苗
Owner GUANGXI SUYUAN INVESTMENT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap