Antibacterial antistatic slippery polyethylene masterbatch and preparation method thereof

A polyethylene and antistatic technology, which is applied in the field of polyethylene antibacterial antistatic smooth masterbatch and its preparation, can solve the problems of poor antibacterial performance durability, poor polyethylene smoothness, and poor antistatic effect, and achieve antistatic Excellent performance, improved production efficiency, good anti-blocking and smooth effect

Inactive Publication Date: 2014-06-11
QINGDAO SANLI ZHONGDEMEI WATER EQUIP
View PDF0 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Polyethylene (PE) has good chemical stability, puncture resistance, impact and environmental friendliness, etc. It is often used in film or blown film packaging in food, beverage, cosmetics, electronics, toys, printing and other industries, but polyethylene The smoothness is relatively poor, and the antistatic effect is not good
At the same time, with the improvement of people's living standards, the demand for antibacterial polyethylene products is also increasing. Adding an appropriate amount of antibacterial agent can endow polyethylene products with a certain antibacterial and bactericidal ability, but the disadvantage is that the antibacterial performance is poor in durability, and it may also lead to During the production process, due to the heat reaction, the product turns yellow and discolored, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A polyethylene antibacterial and antistatic slippery masterbatch, its components are proportioned by mass percentage: polyethylene 45%, oleic acid amide 20%, anti-blocking agent 10%, fatty acid monoglyceride 15%, silver ion antibacterial calcium phosphate 6%, polyethylene wax 2%, silane coupling agent 1.5%, other additives 0.5%, wherein, the described opening agent is light synthetic silica with a particle size between 1 and 4 μm, and the other additives It is a stabilizer and colorant.

[0020] Preparation method: (1) Weigh each component according to the weight ratio for use; (2) Add the anti-blocking agent and silane coupling agent into a high-speed mixer with a rotation speed of 500-1500 rpm, and mix for 3-5 minutes , then add polyethylene, oleic acid amide, fatty acid monoglyceride, silver ion antibacterial calcium phosphate, polyethylene wax and other additives into the high-speed mixer, and mix at a temperature of 85 ° C to 100 ° C for 5 to 15 minutes; (3) Then ...

Embodiment 2

[0022] A polyethylene antibacterial and antistatic slippery masterbatch, its components are proportioned by mass percentage: polyethylene 63%, oleic acid amide 10%, anti-blocking agent 5%, fatty acid diglyceride 10%, sulfadiazine silver 10% , 1% of oxidized polyethylene wax (EVA wax), 0.5% of silane coupling agent, and 0.5% of other additives, wherein the opening agent is light synthetic silica with a particle size between 1 and 4 μm, and the The other additives are stabilizers and colorants.

[0023] Preparation method: (1) Weigh each component according to the weight ratio for use; (2) Add the anti-blocking agent and silane coupling agent into a high-speed mixer with a rotation speed of 500-1500 rpm, and mix for 3-5 minutes , then add polyethylene, oleic acid amide, fatty acid diglyceride, silver sulfadiazine, oxidized polyethylene wax (EVA wax) and other additives into the high-speed mixer, and mix at a temperature of 85 ° C to 100 ° C for 5 to 15 minutes; (3) Add the abov...

Embodiment 3

[0025] A polyethylene antibacterial and antistatic slippery masterbatch, its components are proportioned by mass percentage: polyethylene 30%, erucamide 30%, antiblocking agent 15%, fatty acid polyethylene glycol ester 10%, sulfadiazine silver 10%, ethylene bis stearic acid amide (EBS) 3%, silane coupling agent 2%, wherein, the opening agent is light synthetic silicon dioxide with a particle diameter of 1-4 μm.

[0026] Preparation method: (1) Weigh each component according to the weight ratio for use; (2) Add the anti-blocking agent and silane coupling agent into a high-speed mixer with a rotation speed of 500-1500 rpm, and mix for 3-5 minutes , and then add polyethylene, erucamide, fatty acid polyethylene glycol ester, silver sulfadiazine and ethylene bisstearic acid amide (EBS) into a high-speed mixer, and mix at a temperature of 85°C to 100°C for 5 to 15 minutes (3) Add the above-mentioned mixed materials into the twin-screw extruder to fully melt and blend, the melting te...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses an antibacterial antistatic slippery polyethylene masterbatch and a preparation method thereof. The antibacterial antistatic slippery polyethylene masterbatch disclosed by the invention comprises the components in percentage by mass: 30-70% of carriers, 10-30% of a slipping agent, 5-15% of an antiblocking agent, 10-20% of an antistatic agent, 5-10% of an antibacterial agent, 1-3% of a dispersing agent, 0.5-2% of a coupling agent and 0-1% of other additives. Compared with the prior art, the antibacterial antistatic slippery polyethylene masterbatch is applied to a polyethylene film or film blowing products and has the characteristics of good antiblocking and slippery effects, lasting and stable antibacterial effect, excellent antistatic performance, favorable impact toughness, machinability and the like; in addition, the preparation method is convenient to use, simple in operation, convenient to increase the production efficiency and improve the production environment and relatively good in application prospect.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a polyethylene antibacterial and antistatic smooth masterbatch and a preparation method thereof. Background technique [0002] Polyethylene (PE) has good chemical stability, puncture resistance, impact and environmental friendliness, etc. It is often used in film or blown film packaging in food, beverage, cosmetics, electronics, toys, printing and other industries, but polyethylene The smoothness is relatively poor, and the antistatic effect is not good. At the same time, with the improvement of people's living standards, the demand for antibacterial polyethylene products is also increasing. Adding an appropriate amount of antibacterial agent can endow polyethylene products with a certain antibacterial and bactericidal ability, but the disadvantage is that the antibacterial performance is poor in durability, and it may also lead to During the production process, the pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/06C08K13/06C08K5/20C08K3/36C08K5/103C08K3/32C08K5/435C08J3/22
CPCC08L23/06B29B9/06B29C48/92B29C2948/9258B29C2948/92704C08K3/36C08K5/103C08K5/20C08K5/435C08K13/06C08L2201/04C08L2203/16C08L2205/025C08K2003/325C08L23/30
Inventor 夏伟光
Owner QINGDAO SANLI ZHONGDEMEI WATER EQUIP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com