Anti-blocking low smoke zero halogen flame-retardant cable material for optical cable

A flame-retardant cable material, anti-adhesion technology, applied in the direction of insulated cables, cables, circuits, etc., can solve problems such as adhesion, and achieve the effect of increasing scratch resistance and wear resistance, improving physical and mechanical properties, and improving melt strength.

Active Publication Date: 2014-06-11
JIANGSU HENGTONG WIRE & CABLE TECH +1
View PDF6 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide an anti-adhesion low-smoke halogen-free flame-retardant cable material for optical cables, which solves the technical problem of adhesion with the core unit of the optical cable during processing, improves the processing performance of the product, and makes the outer diameter of the optical cable uniform. In this way, the shrinkage integrity of the optical cable core is guaranteed, and the signal will not be greatly attenuated during the transmission process; at the same time, the tensile strength of the cable is ≥13MPa, the elongation at break is ≥250%, and the oxygen index is ≥34%, which has excellent mechanical properties. performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-blocking low smoke zero halogen flame-retardant cable material for optical cable

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Embodiment 1: An anti-blocking low-smoke halogen-free flame-retardant cable material for optical cables, the anti-blocking low-smoke halogen-free flame-retardant cable material is composed of the following components by weight:

[0028] Ethylene-vinyl acetate copolymer (EVA) 69 parts,

[0029] High pressure metallocene polyethylene (EPPE) 21 parts,

[0030] 10 parts of modified polyethylene,

[0031] 105 parts of aluminum hydroxide,

[0032] 10 parts of magnesium hydroxide,

[0033] Silicone masterbatch 4.5 parts,

[0034] Polyethylene wax 1.8 parts,

[0035] Flow agent 20 parts,

[0036] Antioxidant 0.45 part,

[0037] 3 parts of black masterbatch;

[0038] The VA content of described ethylene-vinyl acetate copolymer is at 20~28%;

[0039] The high-pressure metallocene polyethylene has a melting index of ≤3g / 10min at 190°C and 2.16Kg, and a density of less than 0.92g / cm3.

[0040] The above flow agent is produced by Haimen Xinlongxiang Special Plastic Co., Ltd...

Embodiment 2

[0045] Embodiment 2: An anti-blocking low-smoke halogen-free flame-retardant cable material for optical cables, the anti-blocking low-smoke halogen-free flame-retardant cable material is composed of the following components by weight:

[0046] 69 parts of ethylene-vinyl acetate copolymer,

[0047] 21 parts of high-pressure metallocene polyethylene,

[0048] Modified polyethylene 15 parts,

[0049] 75 parts of aluminum hydroxide,

[0050] 30 parts of magnesium hydroxide,

[0051] Silicone masterbatch 4.5 parts,

[0052] Polyethylene wax 1.8 parts,

[0053] Flow agent 30 parts,

[0054] Antioxidant 0.45 part,

[0055] 4 parts of black masterbatch;

[0056] The VA content of the ethylene-vinyl acetate copolymer (EVA) is 20-28%;

[0057] The high-pressure metallocene polyethylene (EPPE) has a melting index of ≤3g / 10min at 190°C and 2.16Kg, and a density of less than 0.92g / cm3.

[0058] The above flow agent is produced by Haimen Xinlongxiang Special Plastic Co., Ltd.

[005...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
densityaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses an anti-blocking low smoke zero halogen flame-retardant cable material for an optical cable. The anti-blocking low smoke zero halogen flame-retardant cable material comprises the following components in parts by weight: 65-75 parts of ethylene-vinyl acetate copolymer, 20-30 parts of high pressure metallocene polyethylene, 10-20 parts of modified polyethylene, 70-110 parts of aluminum hydroxide, 20-30 parts of magnesium hydroxide, 2-5 parts of silicone master batch, 1-3 parts of polyethylene wax, 30-50 parts of flowable agent, 0.15-0.45 part of antioxidant, and 2-5 parts of black master batch, wherein the content of VA in the ethylene-vinyl acetate copolymer is 20-28%, the melt index of 2.16Kg of high pressure metallocene polyethylene at 190DEG C is less than or equal to 3g / 10min, the density is less than 0.92g / cm<3>. By adopting the anti-blocking low smoke zero halogen flame-retardant cable material, the outer diameter of the optical cable is uniform, so that the shrinkage integrity of the core of the optical cable is guaranteed, the signal transmitted in the optical cable is not attenuated sharply; and in addition, the tensile strength of the cable is greater than or equal to 13MPa, the elongation at break is greater than or equal to 250%, the oxygen index is greater than or equal to 34%, and the cable has excellent mechanical property.

Description

technical field [0001] The invention relates to a flame-retardant cable material, in particular to an anti-adhesion low-smoke halogen-free flame-retardant cable material for optical cables. Background technique [0002] With the enhancement of people's awareness of environmental protection and safety, the requirements for cable sheathing materials are getting higher and higher. Not only must they have excellent physical and mechanical properties, but they must also have high flame retardancy. According to relevant literature statistics, In the fire, the vast majority of people did not burn to death, but lost the chance of escape due to suffocation caused by a large amount of smoke and toxic gas, and finally lost their lives. Therefore, low-smoke halogen-free flame-retardant polyolefin cable compound is gradually replacing traditional PVC cable sheath compound as an environmentally friendly product. Since the "first year of China's FTTH" in 2008, China Telecom and other dome...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/08C08L23/06C08L83/04C08L51/06C08K3/22C08K3/04H01B3/44H01B7/295
CPCC08K2201/003C08K2201/014C08L23/0853C08L2201/02C08L2201/22C08L2203/202C08L2205/02C08L2205/025C08L2205/035C08L2207/066H01B3/44H01B3/441H01B7/18H01B7/295C08L51/06C08L23/06C08L83/04C08K13/02C08K2003/2227C08K2003/2224C08K3/04C08L23/26
Inventor 李凤彪张贤灵程晓松孙玉萍于德宝
Owner JIANGSU HENGTONG WIRE & CABLE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products