Method for forming isotropic neodymium-iron-boron magnet

An isotropic, NdFeB technology, applied in the field of forming isotropic NdFeB magnets, can solve problems such as oxidation, high organic content, and imperfect binder system

Active Publication Date: 2014-06-18
BEIJING ZHONG KE SAN HUAN HI TECH
View PDF9 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, there are still some problems in the preparation of sintered NdFeB magnets by gel injection molding technology.
For example, since the base phase and the Nd-rich phase inside the sintered NdFeB have a strong affinity with oxygen, even if the temperature is n

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for forming isotropic neodymium-iron-boron magnet
  • Method for forming isotropic neodymium-iron-boron magnet
  • Method for forming isotropic neodymium-iron-boron magnet

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0031] A specific embodiment of the present invention will be described in more detail below by means of an example.

[0032] The pre-alloyed ingot was prepared by arc vacuum melting process, and the melting formula was: industrial grade pure iron, niobium, and neodymium were 62g, 2.8g, and 32g respectively, and the boron content was 4.9g of ferroboron with a boron content of 20.21wt%, and the atomic composition was Nd. 14 Fe 78 Nb 2 B 6 pre-alloyed ingots. The pre-alloyed ingot was subjected to vacuum remelting and quick quenching treatment to obtain quick quenching strip fragments. The selected equipment was a single copper roller rapid condensation furnace, and the surface speed of the copper roller was 37m / s. Mix the obtained quick-quenching belt fragments with an appropriate amount of alcohol, put them into an ordinary ball mill for ball milling for 4 hours, the speed of the ball mill is 65r / min, and the weight ratio of grinding steel balls to quick-quenching belt frag...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Concentrationaaaaaaaaaa
Login to view more

Abstract

The invention provides a method for forming an isotropic neodymium-iron-boron magnet. The method comprises the step of smelting an alloy raw material into a prealloyed cast ingot, the step of performing non-crystallizing treatment on the prealloyed cast ingot to obtain a fast-quenched alloy, the step of performing ball milling on the fast-quenched alloy to obtain a powder, the step of mixing the powder with a binder to obtain a slurry, and the step of forming the slurry into the magnet. The binder is a water-based binder, preferably a methylcellulose aqueous solution, and the solid content in the slurry ranges from 30vol% to 60vol%. The method is capable of realizing the formation of the isotropic neodymium-iron-boron magnet large in dimension and complex in shape, and therefore, the purpose of reducing the oxygen content is achieved, and simultaneously, the carbon residue in a degreasing process can be greatly reduced.

Description

technical field [0001] The invention relates to a forming method of an isotropic NdFeB magnet. Background technique [0002] Metal injection molding (Metal injection molding, MIM) is a new type of near-net forming technology introduced from the plastics industry to powder metallurgy. It is a combination of traditional powder metallurgy and modern injection molding. This process can produce small precision parts with complex shapes and uniform structure. Metal injection molding technology has long been used in the preparation of bonded NdFeB permanent magnets. The shape of the magnets can be relatively complex and the performance is excellent, which makes up for the shortcomings of the traditional powder metallurgy dry forming technology, and many products have achieved industrial production. [0003] However, there are few studies on the injection molding technology of sintered NdFeB permanent magnets. The main process difficulties are: 1) The magnetic powder and thermoplas...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22F3/22
Inventor 陈治安饶晓雷胡伯平
Owner BEIJING ZHONG KE SAN HUAN HI TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap