Rubber powder modified emulsified asphalt waterproof coating

A technology for emulsified asphalt and waterproof coatings, applied in asphalt coatings, unspecified rubber coatings, coatings, etc., can solve the problems of high price, pollution of the environment, complex production process, etc., and achieve good high temperature stability, resource recycling, The effect of simple process

Pending Publication Date: 2014-07-02
李志国
View PDF3 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The object of the present invention is to provide a rubber powder modified emulsified asphalt waterproof coating and its preparation method. This waterproof coating maintains the excellent performance of rubber modified asphalt and solves the problem that rubber modified asphalt cannot be preserved and used at normal temperature. , overcome the shortcomings of rubber modified asphalt such as high energy consumption, inconvenient construction, and environmental pollution, and overcome the problems of traditional SBS and SBR modified emulsified asphalt, which are expensive and complex in production process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Get 60 parts of 90# asphalt in Dagang Oilfield (parts by weight, the same below), 2 parts of cationic emulsifier quaternary ammonium salt, 1 part of stabilizer polyvinyl alcohol, and 37 parts of water; prepare by mixing quaternary ammonium salt, polyvinyl alcohol and water To form a mixed solution, heat the mixed solution to 60-80°C; heat the asphalt to 120-160°C; mix the mixed solution with the asphalt, and perform high-speed shear emulsification treatment on it with a colloid mill, when the asphalt particles are dispersed and suspended In the aqueous medium of the mixed liquor, it is emulsified asphalt.

[0019] Take the 30-mesh tire rubber powder crushed by the normal temperature method, and soak it in 120# (rubber) solvent oil for 60 minutes until the rubber particles expand 5-10 times; during the operation, use a recovery device to recover solvent oil and solvent oil volatile matter.

[0020] Take 36 parts of swollen rubber powder, 2 parts of cationic emulsifier qu...

Embodiment 2

[0024] Take 55.5 parts of 100# asphalt in Dagang Oilfield, 1.5 parts of cationic emulsifier alkylammonium salt, 1 part of stabilizer cellulose, and 42 parts of water; prepare a mixed solution by mixing alkylammonium salt, cellulose and water, and use the Heat the mixture to 60-80°C; heat the asphalt to 120-160°C; mix the mixture with the asphalt, and use a colloid mill to perform high-speed shear emulsification, when the asphalt particles are dispersed and suspended in the water medium of the mixture Among them, it is emulsified asphalt.

[0025] Take the 60-mesh tire rubber powder crushed by the normal temperature method, and soak it in 120# (rubber) solvent oil for 60 minutes until the rubber particles expand 5-10 times; the operation process uses a recovery device to recover solvent oil and solvent oil volatile matter.

[0026] Take 45 parts of swollen rubber powder, 1.5 parts of cationic emulsifier alkylammonium salt, 1 part of stabilizer cellulose, 1 part of titanate coup...

Embodiment 3

[0029] Take 51 parts of 100# asphalt in Dagang Oilfield, 2 parts of cationic emulsifier alkylammonium salt, 1 part of stabilizer polyvinyl alcohol, and 46 parts of water; prepare a mixed solution by mixing alkylammonium salt, polyvinyl alcohol and water. The mixture is heated to 60-80°C; the asphalt is heated to 120-160°C; the mixture is mixed with the asphalt, and the colloid mill is used for high-speed shear emulsification, when the asphalt particles are dispersed and suspended in the water of the mixture In the medium, it is emulsified asphalt.

[0030] Take the 80-mesh tire rubber powder crushed by the normal temperature method, and soak it in 120# (rubber) solvent oil for 60 minutes until the rubber particles expand 5-10 times; the operation process uses a recovery device to recover solvent oil and solvent oil volatile matter.

[0031] Take 54 parts of swollen rubber powder, 2 parts of cationic emulsifier quaternary ammonium salt amine, 1 part of stabilizer polyvinyl alco...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a rubber powder modified emulsified asphalt waterproof coating. The rubber powder modified emulsified asphalt waterproof coating comprises emulsified asphalt and a rubber powder emulsion. Asphalt is prepared into the emulsified asphalt, swelling treatment is performed on rubber powder, the swollen rubber powder is prepared into the rubber powder emulsion, the emulsified asphalt and the rubber powder emulsion are metered, mixed and uniformly stirred, and high-speed shear modification treatment is performed by a colloidal mill to obtain the rubber powder modified emulsified asphalt waterproof coating disclosed by the invention. The waterproof coating keeps the excellent performances of rubber modified asphalt, solves the problem that the rubber modified asphalt can not be saved and used at normal temperature, overcomes the shortcomings of high energy consumption, inconvenience in construction, environmental pollution and the like of the rubber modified asphalt, and overcomes the problems of expensive price, complex manufacturing process and the like of traditional SBS (styrene-butadiene-styrene) and SBR (styrene butadiene rubber) modified emulsified asphalt. The rubber powder modified emulsified asphalt waterproof coating disclosed by the invention takes waste tire rubber powder as a modifying material so as to be in line with the national industrial policy of circular economy and low-carbon economy.

Description

technical field [0001] The invention relates to a waterproof material, in particular to a rubber powder modified emulsified asphalt waterproof coating and a preparation method thereof Background technique [0002] Rubber modified asphalt is widely used in the construction field due to its good waterproof performance and weather resistance. The modification of rubber powder to asphalt is based on their full mixing. Under high temperature conditions, the asphalt softens and the rubber powder particles absorb the asphalt. After the light part, swelling occurs. Through high-speed shearing, the swollen rubber particles interact with the rest of the asphalt to form a new structural system. The inherent characteristics of rubber can improve the performance of asphalt accordingly. However, during the production and use of rubber asphalt, it needs to be carried out under high temperature conditions, which will cause problems such as high energy consumption, inconvenient construction,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D195/00C09D121/00C09D7/12C08J3/03C08L95/00C08L21/00
Inventor 李志国赵丰泽
Owner 李志国
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com