Low-silver-content cadmium-free solder
A technology of silver content and brazing material, applied in welding/cutting medium/material, welding medium, metal processing equipment, etc., can solve the problem of cadmium harmful environmental pollution, disadvantage, etc. The effect of high wettability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0010] Example 1:
[0011] According to the components of the solder alloy, the weight percentage composition of the alloy components is: silver 24%, zinc 31.5%, manganese 0.8%, nickel 0.5%, and the balance is copper. The prepared brazing filler metal is processed into a wire with a diameter of 2.0mm, combined with FB102 brazing flux, and the copper alloy base metal is welded by conventional methods. The base metal has good wettability, good flowability, and tensile strength of 355MPa, melting The temperature is about 800℃, and the brazing temperature is about 905℃.
Example Embodiment
[0012] Example 2:
[0013] According to the alloy composition of the solder, the weight percentage composition of the alloy composition is: 25% silver, 33% zinc, 0.8% manganese, 0.5% nickel, and the balance is copper. The prepared brazing filler metal is processed into a wire with a diameter of 2.0mm, combined with FB102 brazing flux, and the copper alloy base metal is welded by conventional methods. The base metal has good wettability, good flowability, and tensile strength of 355MPa, melting The temperature is around 793℃, and the brazing temperature is around 899℃.
Example Embodiment
[0014] Example 3:
[0015] According to the components of the solder alloy, the weight percentage of the alloy components is composed of 26% silver, 35% zinc, 0.8% manganese, 0.5% nickel, and the balance is copper. The prepared brazing filler metal is processed into a wire with a diameter of 2.0mm, combined with FB102 brazing flux, and the copper alloy base metal is welded by conventional methods. The base metal has good wettability, good flowability, and tensile strength of 355MPa, melting The temperature is about 787℃, and the brazing temperature is about 891℃.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap