Self-leveling mortar doped with phosphorus slag powder
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of self-leveling mortar and phosphorus slag powder, applied in the field of building materials, can solve the problems of uneven surface, restrictions on the production and promotion of self-leveling mortar, and high production costs
Inactive Publication Date: 2014-08-20
TONGJI UNIV
View PDF2 Cites 14 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, at present, the production cost of self-leveling mortar is relatively high, and the problem of shrinkage cracking in the later stage cannot be completely overcome, and the phenomenon that the surface is not very smooth and easy to powder after hardening of the surface layer often occurs, which restricts the production and popularization of self-leveling mortar in my country. pace
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0053] Example 1, a self-leveling mortar mixed with phosphorus slag powder, according to ordinary Portland cement 100, high alumina cement 20, phosphorus slag powder 10, S105 slag powder 10, fly ash 5, river sand 150, composite excitation Agent 1.00, water reducing agent 0.05, stabilizer 0.04, defoamer 0.02, water 25 weight ratio prepared. The performance test results are shown in Table 1.
Embodiment 2
[0054] Example 2, a self-leveling mortar mixed with phosphorus slag powder, according to ordinary Portland cement 100, high alumina cement 30, phosphorus slag powder 20, S105 slag powder 20, fly ash 10, river sand 250, composite excitation Agent 2.00, water reducing agent 1.50, stabilizer 0.08, defoamer 0.04, water 45 weight ratio prepared. The performance test results are shown in Table 1.
Embodiment 3
[0055] Example 3, a self-leveling mortar mixed with phosphorus slag powder, according to ordinary Portland cement 100, high alumina cement 40, phosphorus slag powder 30, S105 slag powder 30, fly ash 20, river sand 350, composite excitation Agent 3.00, water reducing agent 2.50, stabilizer 0.12, defoamer 0.08, water 65 weight ratio prepared. The performance test results are shown in Table 1.
[0056] Table 1 Example performance test results
[0057]
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
particle diameter
aaaaa
aaaaa
specific surface area
aaaaa
aaaaa
particle diameter
aaaaa
aaaaa
Login to view more
Abstract
The invention belongs to the technical field of building materials, and particularly relates to a self-leveling mortar doped with phosphorus slag powder. The self-leveling mortar doped with phosphorus slag powder comprises ordinary Portland cement, high-aluminum cement, phosphorus slag powder, S105 slag powder, coal ash, river sand, a composite activator, a water reducer, a stabilizer, a defoaming agent and water. By adopting the self-leveling mortar doped with phosphorus slag powder, the problems of high cost, rough hardened surface and shrinkage crack of ordinary self-leveling mortar are solved, and the recycling use ratio of the industrial byproduct phosphorus slag is also improved. The self-leveling mortar doped with phosphorus slag powder has the advantages of good fluidity, fast speed in curing and hardening, low heat of hydration, high early strength, fast speed in improvement of long-term strength, small shrinkage distortion, smooth and level hardened surface, no crack and so on, can be used for not only construction of new ground and but also repairing of worn, dusting or damaged ground, and can be used for self leveling of various floor base levels.
Description
technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a self-leveling mortar mixed with phosphorus slag powder. Background technique [0002] Phosphorus slag is the industrial waste slag discharged during the process of refining yellow phosphorus in high-temperature electric furnaces. For every 1 ton of yellow phosphorus produced, about (8-10) tons of phosphorus slag is produced, and the discharge is huge. The chemical composition and phase structure of phosphorus slag are similar to those of water-quenched blast furnace slag, and it has potential chemical activity. At present, a large amount of phosphorus slag is mainly disposed of by stacking, which not only occupies a large amount of land, but also pollutes nearby soil and water bodies. In the construction process of the traditional cement mortar floor, after the mortar is mixed, manual paving, scraping, plastering and other processes are used. The conseq...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more