Coating film with large moisture permeability

Active Publication Date: 2014-09-10
PAN ASIAN MICROVENT TECH JIANGSU CORP
View PDF4 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to reduce the blurred phenomenon of water vapor scattering on the light, this theory uses a large number of vent plugs, which cannot solve the problem of condensation in the lower air temperature area of ​​the shell

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Coating film with large moisture permeability

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] The coating agent of the polyurethane emulsion copolymer coating 2 containing hemp stalk core superfine powder comprises the raw materials of following percentage by weight and evenly stirs to make:

[0034] Polyurethane 20%;

[0035] Dimethylformamide solvent 55%;

[0036] Hydrophilic group solvent 2%;

[0037] Hemp Stalk Core Superfine Powder 18%.

[0038] Wherein, the thickness of the polyurethane emulsion copolymer coating 2 containing the superfine powder of hemp stalk core is 0.012 mm.

[0039] The viscosity index of the coating agent is 33 Pa.s. The coating agent contained 35% non-volatile matter.

Embodiment 2

[0041] The coating agent of the polyurethane emulsion copolymer coating 2 containing hemp stalk core superfine powder comprises the raw materials of following percentage by weight and evenly stirs to make:

[0042] Polyurethane 23%;

[0043] Dimethylformamide solvent 57%;

[0044] Hydrophilic group solvent 4%;

[0045] Hemp Stalk Core Superfine Powder 21%.

[0046] Wherein, the thickness of the polyurethane emulsion copolymer coating 2 containing the hemp stalk core superfine powder is 0.0185mm.

[0047] The viscosity index of the coating agent is 33 Pa.s. The coating agent contains 40% non-volatile matter.

Embodiment 3

[0049] The coating agent of the polyurethane emulsion copolymer coating 2 containing hemp stalk core superfine powder comprises the raw materials of following percentage by weight and evenly stirs to make:

[0050] Polyurethane 25%;

[0051] Dimethylformamide solvent 60%;

[0052] Hydrophilic group solvent 5%;

[0053] Hemp Stalk Core Superfine Micron Powder 25%.

[0054] Wherein, the thickness of the polyurethane emulsion copolymer coating 2 containing the superfine powder of hemp stalk core is 0.025mm.

[0055] The viscosity index of the coating agent is 33 Pa.s. The coating agent contains 45% non-volatile matter.

[0056] In Examples 1-3, the manufacturing process of the hemp stalk core superfine powder includes: first processing the hemp stalk core into a coarse powder, and performing pretreatment, followed by refinement treatment and activation treatment, and drying after the treatment is completed. dry, then carry out modification treatment, then carry out microniza...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a coating film with the large moisture permeability. The coating film comprises a basic film layer and a coating layer, wherein the basic film layer is an expanded polytetrafluoroethylene film layer; the coating layer coating the expanded polytetrafluoroethylene film layer is a polyurethane emulsion copolymerization coating layer containing superfine micro-powder of hemp stalk cores; a coating agent of the polyurethane emulsion copolymerization coating layer containing the superfine micro-powder of the hemp stalk cores is prepared by uniformly stirring the following raw materials in percentage by weight: 20-25% of polyurethane; 55-60% of a dimethylfomamide solvent; 2-5% of a hydrophilic group solvent and 18-25% of the superfine micro-powder of the hemp stalk cores. Through the manner, the coating film has good moisture absorbing and guide performances; the content of moisture permeable factor fibrin in the superfine micro-powder of the hemp stalk cores is large; micro-grooves and micropores exist in the coasting film, so that the moisture absorption area and the diffusion area are increased; the coating film has excellent performances such as ultraviolet resistance, water proofing, dust proofing, oil proofing, moisture permeability and corrosion resistance on oxide solutions.

Description

technical field [0001] The invention relates to a coating film with high moisture permeability. Background technique [0002] In the prior art, the air vent hole of the European car lamp has the theory of fog and dew condensation removal, and there is a sponge dustproof inside, and the air in the lamp can be moved in and out with the change of the temperature in the lamp, so that the lamp can be realized quickly. Disperse the fog inside to remove condensation, and the ventilated car lights with bent tubes will accumulate dust in the housing and corrode the electrical components soon after use. [0003] The dew condensation theory of Gore Company in the United States: the lamp is through the air convection inside the lamp and the outside of the lamp to establish a kind of air pressure balance. The water vapor in the lamp will be discharged outside the lamp as the temperature inside the lamp rises. The larger air-permeable membrane patch method realizes mist removal and dew c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B32B27/08
CPCB32B27/40C09D175/04F21V31/00
Inventor 张云丁荣华
Owner PAN ASIAN MICROVENT TECH JIANGSU CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com