Compound sludge curing agent and application thereof
A curing agent and sludge technology, which is applied in the direction of dehydration/drying/concentrated sludge treatment, etc., can solve the problems of poor water resistance, large drying shrinkage, and high water content of solidified sludge, so as to enhance road durability and increase sludge strength , the effect of increasing the moisture content
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0032] Example 1
[0033] Taking the production of 100kg of the product of the present invention as an example, the sludge composite curing agent of this embodiment is made by mixing 53.3Kg of ordinary Portland cement C325, 33.3Kg of medical stone with a particle size of 325 mesh, and 13.4Kg of pyrophyllite with a particle size of 120 mesh.
[0034] The weight ratio of the above raw materials is:
[0035] Cement 8 parts
[0036] 5 servings of medical stone
[0037] 2 parts of pyrophyllite
Example Embodiment
[0038] The implementation method of this sludge curing agent is as follows:
[0039] The preparation method of the pure inorganic sludge curing agent of this embodiment is as follows: according to the ratio determined by the principle of the sludge curing agent, respectively weigh cement and pyrophyllite, and mix them uniformly to obtain a pure inorganic sludge curing agent.
[0040] The application method of the pure inorganic sludge curing agent solidified sludge used in filling roads is as follows: firstly adopt precipitation treatment measures such as turning the sun to reduce the moisture content of the sludge used to below 25%, and then reduce the pure inorganic sludge curing agent of the present invention Mix it into the silt and stir evenly, and then pave the road filler. The mixing amount of the silt curing agent is 25% of the silt mass.
Example Embodiment
[0041] Example 2
[0042] Taking the production of 100 kg of the product of the present invention as an example, the sludge composite curing agent of this embodiment is made by mixing 57.1 kg of ordinary Portland cement C325, 28.6 kg of medical stone with a particle size of 325 mesh, and 14.3 kg of pyrophyllite with a particle size of 120 mesh.
[0043] The weight ratio of the above raw materials is:
[0044] Cement 20 parts
[0045] Maifan Stone 10 servings
[0046] 5 parts of pyrophyllite
[0047] The implementation method of the sludge composite curing agent of this embodiment is the same as that of Example 1, and the mixing amount of the sludge curing agent is 25% of the sludge mass.
PUM
Property | Measurement | Unit |
---|---|---|
Granularity | aaaaa | aaaaa |
Granularity | aaaaa | aaaaa |
Compressive strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap