Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A high-carbon bearing and steel smelting technology, applied in the field of metallurgy, can solve problems such as insufficient retention, increased cost, and brittle inclusions of large particles, and achieve the effects of lowering melting point, preventing increase, and low adsorption and inclusion capacity
Active Publication Date: 2014-10-08
ZENITH STEEL GROUP CORP +1
View PDF9 Cites 39 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
In order to reduce the oxygen content of bearing steel to a lower level, the refining slag generally requires a higher dissolved [Al] content in the steel during the production process, and even additional aluminum wires are added during the refining process, resulting in deoxidized products in the molten steel It is difficult to completely form clustered inclusions that are conducive to floating; in addition, because the Al in the slag 2 o 3 The content is low, the melting point of refining slag is relatively high, and the ability of refining slag to absorb spherical inclusions is limited
[0005] Although high-alkalinity refining slag is beneficial to the desulfurization and deoxidation of bearing steel, it is easy to form brittle inclusions in molten steel during the smelting process of bearing steel, which will greatly endanger the life of bearing steel. CaO or MgO in the furnace lining is reduced by [Al] or [C] in the steel and enters the molten steel
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0021] The furnace number is 014040530 and the smelting process of high carbon bearing steel GCr15 is as follows:
[0022] ①The tapping temperature of the electric furnace is 1627°C, the C content at the end point is 0.56%, the P content is 0.017%, the tapping amount is 86t, and there is no slag in tapping;
[0024] ③When the temperature of the refining station is 1478°C, it is heated by electricity, and at the same time, silicon carbide (total 170kg) is sprayed into the molten steel surface for diffusion deoxidation. Ensure the operation of white slag during the refining process, and at the same time add alloys to fine-tune the composition. The entire refining time is 66 minutes, and the temperature of the molten steel from the ladle out of the refining furnace is 1584°C;
[0025] ④ Take the slag in the late stage of refining, the main components in the test results ...
Embodiment 2
[0030]The furnace number is 014050175 high carbon bearing steel GCr15 smelting process is as follows:
[0031] ①The tapping temperature of the electric furnace is 1632°C, the C content at the end point is 0.56%, the P content is 0.013%, the tapping amount is 89t, and the tapping is not slag;
[0033] ③When the temperature of the refining station is 1499°C, it is heated by electricity, and at the same time, silicon carbide (total 160kg) is sprayed into the molten steel surface for diffusion deoxidation. Ensure the operation of white slag during the refining process, and at the same time add alloys to fine-tune the composition. The entire refining time is 69 minutes, and the molten steel temperature of the ladle out of the refining furnace is 1577°C;
[0034] ④ Take the slag in the later stage of refining, the main components in the test results are CaO: 53.86%, SiO 2 : ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a smelting process of high-carbon bearing steel. High-alkalinity refining slag with the alkalinity value of 6-9 is obtained through adding conditioned slag and a deoxidizing agent, so that relatively good desulfuration and deoxidization effects are achieved, the content of S can be reduced to about 0.002%, and the content of O can be reduced to be less than 7ppm. Meanwhile, in order to avoid brittle impurity generation caused by overhigh alkalinity of refining slag, the content Al of the molten steel is strictly controlled in a smelting process, enough aluminum blocks for deoxidizing are added at one step in a tapping process, and no aluminum is replenished in the subsequent process, so that a deoxidized product is prevented from being floated; the content of Al in the refining slag is controlled at about 0.010%, so that secondary oxidation caused in a pouring process is reduced. On the other hand, the value of CaO/Al2O3 in the refining slag is controlled at about 1.7, so that the melting point of slag is relatively low, the flowability of the slag is relatively good, the steel slag is easy to separate, and the slag rolling and reduction reaction of molten steel in a vacuumizing process are reduced. Therefore, D-type inclusions in the bearing steel are effectively prevented from being increased, and the rating standards of inclusions in the bearing steel are reached.
Description
technical field [0001] The invention belongs to the field of metallurgy and relates to a smelting process, in particular to a smelting process of high-carbon bearing steel. Background technique [0002] The non-metallic inclusions in bearing steel are the key factors affecting its service life, and a considerable part of the non-metallic inclusions in steel is caused by oxygen, so the rating of inclusions in steel and the oxygen content in steel are often used as a measure of bearing steel important indicator of quality. [0003] In order to effectively deoxidize and remove the inclusions in the steel to the greatest extent, so that the bearing steel can obtain higher cleanliness and quality, after determining the deoxidizer, select the appropriate slag material component to determine the physical and chemical properties of the refining slag. extremely important. For high-quality, high-cleanness bearing steel, the principles for determining the chemical composition of the ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.