Paper for packaging carrier tape and preparation method thereof

A technology for carrying tape and packaging paper and pulp, applied in pulp beating/refining method, wrapping paper, wrapping paper, etc., can solve the problems of jamming electronic components, troubles of lower-end manufacturers, etc., and achieve high-level bonding strength. Effect

Active Publication Date: 2014-10-08
JIANGXI JIEMEI ELECTRONICS INFORMATION MATERIAL CO LTD
View PDF6 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because the burr (fur) sometimes remains in the loading hole punched out by the general carrier tape packaging paper, when the residual burr (fur) > 0.1mm, it is easy to cause jamming (that is, the electronic component is stuck by the burr on the suction nozzle) can not be sucked out), causing great trouble to the lower-end manufacturers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Paper for packaging carrier tape and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The specific production process is as follows:

[0033] (1) Send the bleached softwood pulp into the high-consistency pulper for 25-30 minutes, and the pulp concentration is 10-12%. After pulping, put it into the pulp tank to adjust the pulp concentration to 3.5%-4.0 %stand-by;

[0034] (2) The pulp treated in step (1) is sent to the double-disc refiner for refining, and the refiners are arranged in the order of cutting first and then splitting, and the pulp fibers are decomposed, cut and split, until The beating degree is 35-48°SR, the wet weight is 2.5g-5.0g, and the treated pulp is put into the pulp tank for use;

[0035] (3) Send the bleached hardwood pulp into the high-consistency pulper for 25-30 minutes, and the pulp concentration is 10-12%. After pulping, it is put into the pulp tank to adjust the pulp concentration to 3.5%-4.0 % Standby;

[0036] (4) The pulp treated in step (3) is sent to the double-disc refiner for refining. 35-48°SR, wet weight 2.5g-5.0g...

Embodiment 2

[0045] The specific production process is as follows:

[0046] (1) Send the bleached softwood pulp into the high-consistency pulper for 25-30 minutes, and the pulp concentration is 10-12%. After pulping, put it into the pulp tank to adjust the pulp concentration to 3.5%-4.0 %stand-by;

[0047] (2) The pulp treated in step (1) is sent to the double-disc refiner for refining, and the refiners are arranged in the order of cutting first and then splitting, and the pulp fibers are decomposed, cut and split, until The beating degree is 35-48°SR, the wet weight is 2.5g-5.0g, and the treated pulp is put into the pulp tank for use;

[0048] (3) Send the bleached hardwood pulp into the high-consistency pulper for 25-30 minutes, and the pulp concentration is 10-12%. After pulping, it is put into the pulp tank to adjust the pulp concentration to 3.5%-4.0 % Standby;

[0049] (4) The pulp treated in step (3) is sent to the double-disc refiner for refining. 35-48°SR, wet weight 2.5g-5.0g...

Embodiment 3

[0058] The specific production process is as follows:

[0059] (1) Send the bleached softwood pulp into the high-consistency pulper for 25-30 minutes, and the pulp concentration is 10-12%. After pulping, put it into the pulp tank to adjust the pulp concentration to 3.5%-4.0 %stand-by;

[0060] (2) The pulp treated in step (1) is sent to the double-disc refiner for refining, and the refiners are arranged in the order of cutting first and then splitting, and the pulp fibers are decomposed, cut and split, until The beating degree is 35-48°SR, the wet weight is 2.5g-5.0g, and the treated pulp is put into the pulp tank for use;

[0061] (3) Send the bleached hardwood pulp into the high-consistency pulper for 25-30 minutes, and the pulp concentration is 10-12%. After pulping, it is put into the pulp tank to adjust the pulp concentration to 3.5%-4.0 % Standby;

[0062](4) The pulp treated in step (3) is sent to the double-disc refiner for refining. 35-48°SR, wet weight 2.5g-5.0g,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Tightnessaaaaaaaaaa
Thicknessaaaaaaaaaa
Stiffnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses paper for packaging a carrier tape and a preparation method thereof. The paper and the preparation method are characterized in that the thickness of the paper for packaging the carrier tape is 0.25mm-1.00mm, the thickness deviation is plus or minus 0.02mm, the compactness is 0.80-0.95g / cm<3>, the moisture content is 6.0%-9.0%, the deflection is greater than or equal to 30mN.m, the peel strength between all the layers is greater than or equal to 80ftlb / 1,000in2, the critical wax rod strength of a surface layer is greater than or equal to 18A, and the residual rate of burrs (soft flocks) greater than 0.1mm in a carrying hole punched by using a punching mould is less than 5 / 1000. According to the paper for packaging the carrier tape and the preparation method thereof, by utilizing short fiber paper pulp subjected to pulp grinding treatment, and adding and spraying a high-molecular polymer resin adhesive, dry-strength resin, wet-strength resin, a stiffening agent, a sizing agent and the like into the paper pulp and between made wet paper sheet layers, a three-dimensional network structure is formed by bonding paper pulp fibers with various polymer resin macromolecules, so that paper boards have relatively high interlayer bonding strength, surface strength and stiffness, and the fibers are easier to cut off during punching to reduce the production of the soft flocks, so as to meet the quality requirements for the packaging the carrier tape.

Description

technical field [0001] The invention belongs to the technical field of electronic information materials, and in particular relates to a tape carrier packaging paper used for packaging chip electronic components in the field of microelectronics and a preparation method thereof. Background technique [0002] With the development of miniaturization of electrical appliances, the requirements for the miniaturization of electronic components are getting higher and higher. Chip electronic components are the mainstream form of discrete electronic components, and their size is getting smaller and smaller. From 3216 to 1608, its application The mainstream size is transitioning from 1608 to 1005. At present, the smallest has developed to 0603 or even 0402. At such a small scale, the packaging, transportation and access of components must have corresponding carriers. Plastic carrier tape is used as a packaging carrier, but it is acceptable to use plastic carrier tape when the size is la...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D21H27/10D21F11/08D21H21/16D21H21/18D21H21/14D21H11/14D21H11/02D21D1/20
Inventor 姜兆宏
Owner JIANGXI JIEMEI ELECTRONICS INFORMATION MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com