Preparation method of high-density bismuth vanadate ceramic

A technology of density bismuth vanadate and bismuth vanadate, which is applied in the field of functional ceramic materials, can solve the problem that bismuth vanadate is difficult to sinter into ceramics, etc., achieve high density, ensure conversion rate and production efficiency, and inhibit volatilization.

Active Publication Date: 2014-10-22
CHEM & CHEM ENG GUANGDONG LAB
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention is to overcome the problem that bismuth vanadate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of high-density bismuth vanadate ceramic
  • Preparation method of high-density bismuth vanadate ceramic
  • Preparation method of high-density bismuth vanadate ceramic

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0021] The high-density bismuth vanadate ceramic of the present invention uses Bi 2 O 3 And V 2 O 5 The powder is the raw material and is made by firing twice, and can be specifically prepared by the following steps.

[0022] Step 1: Put Bi 2 O 3 And V 2 O 5 The powder is mixed according to the molar ratio of 1:1 and then mixed and loaded into the grinding equipment. It is manually grinded for 5 hours. When grinding, absolute ethanol is used as the solvent to keep the particles uniform and not produce powder dust. The added water is anhydrous The amount of ethanol is about 5% of the powder mass. Ensure that the volatilization is completed after grinding and will not remain in the powder. The ground powder is dried and pressed into tablets.

[0023] Step 2. Put the pressed tablet into a sealed quartz mold, put it in the muffle furnace and pre-fire at 890 ℃ for 12 hours, and then naturally anneal to cool down; in order to avoid the volatilization of the components, the quartz mold i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of high-density bismuth vanadate ceramic. The prepared bismuth vanadate ceramic has the density of more than 97%. The preparation method comprises the steps of with Bi2O3 powder and V2O5 powder as raw materials, mixing and tabletting, then, presintering at the temperature of 890 DEG C in a sealed quartz die, and then, grinding into powder; tabletting again, and calcining in the sealed quartz die; after the calcining is ended, cooling from 890 DEG C to 800 DEG C at the speed of 1.5 DEG C/min, cooling to 700 DEG C at the speed of 1.7 DEG C/min, then, cooling to 550 DEG C at the speed of 2.5 DEG C/min, and next, cooling to 350 DEG C at the speed of 3.3 DEG C/min; finally, naturally cooling to room temperature, and then, polishing to obtain the orange yellow bismuth vanadate ceramic.

Description

technical field [0001] The invention belongs to the field of functional ceramic materials, and in particular relates to a preparation method of high-density bismuth vanadate ceramics. Background technique [0002] Functional materials are the core of the field of new materials, and play an important role in promoting and supporting the development of high-tech. In the field of new materials in the world, functional materials account for about 85%. Functional ceramic materials are an important part of functional materials and have many excellent properties, which are highly valued by the scientific and technological circles and business circles. [0003] Bismuth vanadate (referred to as 184 yellow) is an important inorganic yellow pigment with the characteristics of non-toxicity, bright color and stable chemical properties. Bismuth vanadate is a semiconductor material with a narrow band gap ( E g = 2.4 eV), which has good oxygen production activity under visible light ir...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/495C04B35/64
Inventor 李国岭李海生王赵武曹京晓王丹丹马海祥刘书丽孙广宇郜元煜郑博含黄海明臧国忠李立本
Owner CHEM & CHEM ENG GUANGDONG LAB
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap