A kind of insulating environment-friendly PVC modified material and preparation method thereof

Abstract

The invention relates to the technical field of PVC modified materials and particularly relates to an insulating and environment-friendly PVC modified material and a preparation method thereof. The insulating and environment-friendly PVC modified material contains the following raw materials: 80-120 parts of PVC resin, 40-60 parts of bulking agent, 40-60 parts of plasticizer, 10-15 parts of insulation modifier, 3-7 parts of heat stabilizer and 0.5-1.5 parts of lubricant, wherein the plasticizer is a mixture prepared from dioctyl terephthalate and tri-n-butyl citrate which are in the weight ratio of (5-7): 1; the insulation modifier is a mixture prepared from kaolin, titanium white and glass micro-beads which are in the weight ratio of (2-4): (1.5-2.5): 1, and the particle size of the glass micro-beads is smaller than 20 microns. According to the modified material prepared by the preparation method, all properties exceed the national standards, the insulating property is good, the resistivity reaches up to 5.1*10<14> omega, and the modified material is environment-friendly; the preparation method disclosed by the invention is simple in process, convenient in operation and control, stable in quality and high in production efficiency and can be applied to large-scale industrial production.

Description

technical field [0001] The invention relates to the technical field of PVC modified materials, in particular to an insulating and environment-friendly PVC modified material and a preparation method thereof. Background technique [0002] Polyvinyl chloride (PVC) is one of the earliest industrialized and widely used general-purpose thermoplastics. It has the advantages of light weight, high strength, insulation, flame retardancy, corrosion resistance, excellent comprehensive performance, low price and wide source of raw materials; but also There are the following disadvantages: 1. The toughness is poor, and it is easy to be brittle when impacted, so it cannot be used as a structural material. In addition, the brittleness of polyvinyl chloride is greatly affected by temperature. The lower limit of general PVC products is -15°C. The lower limit of use of PVC is -30°C; 2. Poor thermal stability, it begins to decompose HCl at 100°C, and decomposes more rapidly when it is higher th...

AI Technical Summary

Problems solved by technology

[0002] Polyvinyl chloride (PVC) is one of the earliest industrialized and widely used general-purpose thermoplastics. It has light weight, high strength, insulation, flame retardancy, corrosion resistance, It has the advantages of excellent comprehensive performance, low price and wide source of raw materials; but it also has the following disadvantages: 1. Poor toughness, easy to be brittle when impacted, so it cannot be used as a structural material. In addition, the brittleness of polyvinyl chloride is greatly affected by temperature. Large, the lower limit of general PVC products is -15°C, and the lower limit of soft PVC is -30°C; 2. Poor thermal stability, it begins to decompose HCl at 100°C, and decomposes more rapidly when it is higher than 150°C. The melting temperature of PVC is about 210°C; 3. The viscosity of PVC is extremely high and its fluidity is extremely poor, which limits its use to a certain extent.

[0006] The performance indicators of most of the existing PVC materials are only meeting the basic requirements of national standards, and the insulation of the current PVC materials is not good, so the insulation of PVC materials needs to be further optimized and improved; in addition, the existing PVC Sheathed cables, PVC plugs, PVC films and PVC pipes all have quite serious pollution, which will cause certain harm to human health. It is also particularly important to develop an environmentally friendly PVC modified material