Growth method of compound sodium cadmium borate crystal

A technology of sodium borate and crystal, which is applied in the growth field of compound sodium cadmium borate crystal to achieve the effects of low viscosity, fast growth speed and low cost

Active Publication Date: 2016-07-06
XINJIANG TECHN INST OF PHYSICS & CHEM CHINESE ACAD OF SCI
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] CrystEngComm magazine (2013, Vol15, 3412-3416) reported that Na 2 CD 7 B 8 o 20 Crystal, its molecular weight is 1239.26, this crystal belongs to the orthorhombic crystal system, the space group is Fdd2, and the unit cell parameter is Z=108, but didn't grow up 2 CD 7 B 8 o 20 crystals, and for most functional crystal applications, it is necessary to grow single crystals with high optical quality up to several millimeters or even centimeters

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Growth method of compound sodium cadmium borate crystal
  • Growth method of compound sodium cadmium borate crystal

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] According to the reaction formula Na 2 CO 3 +CdO+H 3 BO 3 →Na 2 Cd 7 B 8 o 20 +H 2 O↑+CO 2 ↑ Preparation of compound Na 2 Cd 7 B 8 o 20 ;

[0035] The compound sodium cadmium borate (Na 2 Cd 7 B 8 o 20 )Synthesis:

[0036] Na 2 CO 3 :CdO:H 3 BO 3 Weigh it into a mortar with a molar ratio of 1:7:8, mix and grind carefully, put it into a corundum crucible, put it into a muffle furnace, slowly raise the temperature to 200°C, keep the temperature constant for 3 hours, cool to room temperature and grind evenly, slowly Raise the temperature to 500°C, exhaust the gas as much as possible, take out the crucible after cooling, grind the sample evenly, and then put it in the crucible, raise the temperature of the muffle furnace to 670°C, keep the temperature for 48-90 hours, take out the sample, put it in the research The single-phase polycrystalline powder of sodium borate cadmium compound can be obtained by crushing and grinding in a bowl, and then the poly...

Embodiment 2

[0043] According to the reaction formula Na 2 CO 3 +CdO+B 2 o 3 →Na 2 Cd 7 B 8 o 20 +H 2 O↑+CO 2 ↑ Preparation of compound Na 2 Cd 7 B 8 o 20 ;

[0044] The compound sodium cadmium borate (Na 2 Cd 7 B 8 o 20 ) is synthesized according to Example 1;

[0045] The synthesized compound sodium cadmium borate and flux B 2 o 3 -Mix NaF=1:2, then use a Φ80mm×80mm open platinum crucible as a container, put the crucible into the single crystal growth furnace, seal the opening on the top of the furnace with insulation material, and the top of the furnace corresponds to the center of the crucible Leave a small hole for the seed rod to come out, heat up to 800°C at a heating rate of 5°C / hour, keep the temperature for 10 hours, and quickly cool down to 750°C to obtain a mixed melt of sodium cadmium borate and co-solvent ;

[0046]At a temperature of 750°C, quickly lower the seed rod into the melt, wait for it to produce drift crystals, keep the temperature for 0.5h with...

Embodiment 3

[0050] According to the reaction formula NaNO 3 +CdO+H 3 BO 3 →Na 2 Cd 7 B 8 o 20 +NO 2 ↑+H 2 O ↑ Preparation of compound Na 2 Cd 7 B 8 o 20 ;

[0051] The compound sodium cadmium borate (Na 2 Cd 7 B 8 o 20 ) is synthesized according to Example 1;

[0052] Preparation of co-solvent Na 2 B 4 o 7 : Use analytically pure NaNO 3 and H 3 BO 3 molar ratio NaNO 3 :H 3 BO 3 =1:4 for mixing, after mixing and grinding, sintering at a temperature of 420°C for 24 hours to make a cosolvent Na 2 B 4 o 7 ;

[0053] The synthesized Na 2 Cd 7 B 8 o 20 With the prepared co-solvent Na 2 B 4 o 7 Massive Na 2 Cd 7 B 8 o 20 :Na 2 B 4 o 7 = After mixing evenly at 1:1, put it into an open platinum crucible of Φ80mm×80mm, put the crucible into the single crystal growth furnace, seal the opening on the top of the furnace with insulating material, and place it at the position corresponding to the center of the crucible on the top of the furnace Leave a small ho...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to a kind of growth method of compound sodium cadmium borate crystal, the method combines sodium cadmium borate compound and auxiliary solvent B 2 o 3 -R system or Na 2 B 4 o 7 Mixing, heating, constant temperature, and cooling to obtain a mixed melt containing sodium cadmium borate and a cosolvent, putting the seed crystal mounted on the seed crystal rod into the prepared mixed melt, rotating the seed crystal rod at the same time, cooling, and then Slowly lower the temperature to obtain the desired crystal, lift the crystal from the liquid surface, and lower it to room temperature to obtain the compound sodium cadmium borate crystal. This method has fast growth speed and low cost, and can grow 20mm×20mm×10mm Na with high optical quality. 2 Cd 7 B 8 o 20 The crystal obtained by the method of the present invention has good mechanical properties, is not easily broken, does not deliquesce, and is easy to process.

Description

technical field [0001] The present invention relates to a kind of compound sodium cadmium borate (Na 2 Cd 7 B 8 o 20 ) crystal growth method. Background technique [0002] In recent decades, a large number of borates have been widely studied, and a large number of nonlinear compound crystal materials with excellent frequency doubling effects have emerged, such as BBO, LBO, KBBF, KDP, etc. Alkali metal cadmium borates have been rarely reported so far, and most of the reported compounds are compounds with a central structure. [0003] CrystEngComm magazine (2013, Vol15, 3412-3416) reported that Na 2 Cd 7 B 8 o 20 Crystal, its molecular weight is 1239.26, this crystal belongs to the orthorhombic crystal system, the space group is Fdd2, and the unit cell parameter is Z=108, but didn't grow up 2 Cd 7 B 8 o 20 Crystals, and for most applications of functional crystals, it is necessary to grow single crystals with high optical quality up to several millimeters or ev...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C30B29/22C30B11/06
Inventor 潘世烈周琳
Owner XINJIANG TECHN INST OF PHYSICS & CHEM CHINESE ACAD OF SCI