Color-coated sheet resisting VHP oxidation

A technology of oxidizing color and coating plate, applied in chemical instruments and methods, layered products, metal layered products, etc., to achieve the effect of good adhesion and fine and smooth coating

Active Publication Date: 2014-11-19
扬子江新型材料(苏州)有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] But at the same time, because vaporized hydrogen peroxide has a strong oxidation activity, it is quite corrosive to the workshop of the pharmaceutical workshop, and there are few wall materials specially designed and developed for it in the market, so this application aims at This market gap is used to develop a building material that can withstand the strong corrosion of vaporized hydrogen peroxide

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Color-coated sheet resisting VHP oxidation

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Anti-VHP oxidation color-coated plate, which is provided with anti-VHP oxidation fine coating 1, anti-VHP oxidation pre-coat 2, first passivation layer 3, galvanized sheet 4, second passivation layer 5 and Anti-VHP oxidation back coating6. Among them, the anti-VHP oxidation fine coating 1 is nanometer Mo 5 Si 3 B and Nano Ag 2 O blending modified polyester-polyamide resin, nano Mo 5 Si 3 B and Nano Ag 2 The particle size of O is 50nm, and nanometer Mo in polyester-polyamide resin 5 Si 3 The content of B is 1.5wt%, nano Ag 2 The content of O is 1.0wt%, and the thickness of the anti-VHP oxidation finish coating is preferably 15 μm.

[0026] Anti-VHP oxidation precoat 2 is nano ZrB 2 , nano-SiC and nano-ZrC blend modified epoxy resin, nano-ZrB 2 The particle size of nano-SiC and nano-ZrC is 100nm, and nano-ZrB in epoxy resin 2 The content of nano-SiC is 1.0wt%, the content of nano-SiC is 0.5wt%, the content of nano-ZrC is 0.5wt%, and the thickness of anti-VHP ox...

Embodiment 2

[0029] Anti-VHP oxidation color-coated plate, which is provided with anti-VHP oxidation fine coating 1, anti-VHP oxidation pre-coat 2, first passivation layer 3, galvanized sheet 4, second passivation layer 5 and Anti-VHP oxidation back coating6. Among them, the anti-VHP oxidation fine coating 1 is nanometer Mo 5 Si 3 B and Nano Ag 2 O blending modified polyester-polyamide resin, nano Mo 5 Si 3 B and Nano Ag 2 The particle size of O is 100nm, and nanometer Mo in polyester-polyamide resin 5 Si 3 The content of B is 2.5wt%, nano Ag 2 The content of O is 1.5wt%, and the thickness of the anti-VHP oxidation finish coating is preferably 20 μm.

[0030] Anti-VHP oxidation precoat 2 is nano ZrB 2 , nano-SiC and nano-ZrC blend modified epoxy resin, nano-ZrB 2 The particle size of nano-SiC and nano-ZrC is 200nm, and nano-ZrB in epoxy resin 2 The content of nano-SiC is 2.0wt%, the content of nano-SiC is 1.0wt%, the content of nano-ZrC is 1.0wt%, and the thickness of anti-VHP o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a color-coated sheet resisting VHP (Vaporized Hydrogen Peroxide) oxidation. The color-coated sheet sequentially comprises a VHP oxidation resisting fine coating, a VHP oxidation resisting pre-coating, a first passivation layer, a galvanized sheet, a second passivation layer and a VHP oxidation resisting back coating from top to bottom, wherein the VHP oxidation resisting fine coating is polyester-polyamide resin formed by blending modification of nano Mo5Si3B and nano Ag2O; the content of the nano Mo5Si3B in the polyester-polyamide resin is 1.5-2.5 weight percent; the content of the nano Ag2O is 1.0-1.5 weight percent; the thickness of the VHP oxidation resisting fine coating is 15-20 microns. According to the scheme, a trace of nano-scale oxidation-resisting materials are added into a surface paint film of the color-coated sheet, so that the own good bending performance of a steel sheet is not influenced; the color-coated sheet has the characteristics of acid-base resistance, solvent resistance and VHP oxidation resistance; even in a VHP environment for a long time, the coatings are kept fine and smooth, the adhesion force is good, and the phenomena of pulverization, cracking and bubbling are avoided.

Description

technical field [0001] The invention relates to the field of special materials, in particular to an anti-VHP oxidation color-coated plate used in a pharmaceutical workshop. Background technique [0002] Color-coated steel plate, also known as color-coated steel plate, is a composite material, mainly composed of substrate and coating, which has the advantages of both steel plate and organic material. Good decoration, corrosion resistance, beautiful appearance and other advantages of the material have achieved good effects such as replacing wood with steel, efficient construction, and energy saving, so it has become a new type of decoration in the construction industry, shipbuilding industry, furniture industry, vehicle manufacturing industry, and electrical industry. Material. At present, color-coated steel sheets are mainly made of cold-rolled steel sheets, electro-galvanized steel sheets or hot-dip steel sheets as substrates, after surface degreasing, phosphating, and comp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B27/08B32B27/18B32B9/04B32B15/00B32B33/00
Inventor 杨建仁秦昌和许曲锋周庆艳周丹张林元
Owner 扬子江新型材料(苏州)有限公司