Aerated concrete block with composition of mica powder and fly ash and preparation method

A technology of aerated concrete and fly ash, applied in the field of building materials, can solve the problems of single material source, large drying shrinkage value, poor thermal insulation, etc. Effect

Inactive Publication Date: 2013-10-02
梁莉
View PDF3 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] As a new type of wall material, air-entrained concrete is a low-energy, environmentally-friendly new building material, which belongs to the building materials promoted by the state. However, because ordinary air-entrained concrete is made of cement, fly ash, quicklime, gypsum, etc. Large shrinkage value, low strength, water seepage, non-corrosion resistance, poor heat insulation, single source of material, etc. Therefore, further research on aerated concrete block technology is urgently needed to further meet market requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] A composite aerated concrete block of mica powder and fly ash, which is characterized in that it is made of the following raw materials in parts by weight (kg): cement 12, quicklime 20, gypsum 12, fly ash 30, aluminum powder 0.2, mica powder 30. Talc powder 12. Iron nitrate 3. Lard oil 3. Sodium dodecylbenzene sulfonate 3. Iron ore tailings 1. Sodium persulfate 3. Oil foot 3. Polyisobutylene 3. Alum 8.

[0014] The preparation method of mica powder and fly ash composite aerated concrete block is characterized in that it comprises the following steps:

[0015] (1) Add appropriate amount of water to mica powder, talcum powder and alum, heat to 90-100°C, stir for 15-20 minutes, add oil feet and iron ore tailings, stir for 15-25 minutes, then add sodium persulfate, Polyisobutylene, after stirring for 20-35 minutes, stir into mud;

[0016] (2) Add cement and fly ash to 40-50°C hot water and mix for 20-35 minutes, then add the mud and aluminum powder, quicklime, gypsum, sodi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
Login to View More

Abstract

Provided is an aerated concrete block with composition of mica powder and fly ash and a preparation method. The aerated concrete block is characterized by being prepared from, by weight, 12-15 parts of cement, 15-20 parts of quicklime, 12-16 parts of gypsum, 30-35 parts of fly ash, 0.2-0.4 parts of aluminium powder, 30-35 parts of mica powder, 12-16 parts of talcum powder, 2-3 parts of ferric nitrate, 2-3 parts of lard, 2-3 parts of sodium dodecyl benzene sulfonate, 1-2 parts of iron mine tailings, 2-3 parts of sodium persulfate, 3-4 parts of oil foot, 3-4 parts of polyisobutylene and 8-10 parts of alum. The aerated concrete block employs composition of mica powder and fly ash, and is advantaged by high temperature resistance acid and alkali resistance, corrosion resistance and high block strength.

Description

technical field [0001] The invention belongs to a building material technology, in particular to a concrete block and a preparation method thereof. Background technique [0002] As a new type of wall material, air-entrained concrete is a low-energy, environmentally-friendly new building material, which belongs to the building materials promoted by the state. However, because ordinary air-entrained concrete is made of cement, fly ash, quicklime, gypsum, etc. Large shrinkage value, low strength, water seepage, no corrosion resistance, poor heat insulation, single source of material, etc. Therefore, further research on aerated concrete block technology is urgently needed to further meet market requirements. Contents of the invention [0003] The purpose of the present invention is to provide mica powder and fly ash composite aerated concrete block and its preparation method, so that the block has high temperature resistance, acid and alkali resistance, and corrosion resistanc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/14C04B38/02C04B14/20C04B24/08
Inventor 石玉伟
Owner 梁莉
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com