Water-based woodenware seal primer and preparing method thereof

A technology for sealing primer and woodware, applied in the direction of coating, etc., to achieve the effect of excellent sealing performance, excellent anti-swelling effect and strong permeability

Inactive Publication Date: 2015-01-07
漳州水之采环保科技有限公司
View PDF2 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These are common problems in the construction of water-based wood paints. It is difficult to solve the above problems with water-based wood sealer primers currently on the market.
In order to solve the problems of solid wood swelling and MDF swelling, fatty wood oil precipitation and tannic acid penetration, the present invention provides a high-performance water-based wood sealing primer, which can inhibit the penetration of water from the upper coating to the substrate, It can also prevent the tannic acid and oil in the wood from penetrating into the surface of the paint film to achieve the effect of anti-expansion oil sealing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Take the following mass percentages:

[0031] Acrylic emulsion: 80%

[0032] Silane coupling agent: 1%

[0033] Defoamer: 0.5%

[0034] Leveling agent: 0.5%

[0035] Thickener: 0.5%

[0036] PH regulator: 0.1%

[0037] Coalescing aid: 5%

[0038] Nano Enhancer: 3%

[0039] Deionized water: 9.4%

[0040] Wherein, the acrylic emulsion is Joncry 95; the silane coupling agent adopts vinyltriethoxysilane; the pH regulator adopts AMP-95 and ammonium dihydrogen phosphate; the film-forming aid The agent is TEXANOL, DPNB; the nano-enhancer is nano-silica; the defoamer is TEGO902W, the leveling agent is EFKA3580, and the thickener is PUR40.

[0041] Follow the steps below:

[0042] 1. Pour the acrylic emulsion into the first container, add the silane coupling agent dropwise at a stirring speed of 500-800 r / min and stir for 5-10 minutes;

[0043] 2. Add nano-silica, stir and disperse for 30 minutes at a speed of 500~1000 r / min;

[0044] 3. Pour TEXANOL a...

Embodiment 2

[0048] Take the following mass percentages:

[0049] Acrylic emulsion: 73%

[0050] Silane coupling agent: 2%

[0051] Defoamer: 0.4%

[0052] Leveling agent: 0.5%

[0053] Thickener: 0.8%

[0054] PH regulator: 0.2%

[0055] Coalescing aids: 6%

[0056] Nano Enhancer: 5%

[0057] Deionized water: 12.1%

[0058] Wherein, the acrylic emulsion is XK-12 or ECS4905; the silane coupling agent uses vinyltriethoxysilane and vinyltrimethoxysilane; the pH regulator uses AMP-95 and bicarbonate In sodium; the film-forming aids are TEXANOL and propylene glycol; the nano-enhancer is nano-silicon capsules; the defoamer is TEGO902W, the leveling agent is EFKA3580, and the thickener is PUR40.

[0059] Follow the steps below:

[0060] 1. Pour XK-12 or ECS4905 into the first container, add vinyltriethoxysilane and vinyltrimethoxysilane dropwise at a stirring speed of 500-800 r / min and stir for 5-10 minutes;

[0061] 2. Add nano silicon capsules, stir and disperse for 3...

Embodiment 3

[0066] Take the following mass percentages:

[0067] Acrylic emulsion: 85%

[0068] Silane coupling agent: 2%

[0069] Defoamer: 0.6%

[0070] Leveling agent: 0.4%

[0071] Thickener: 0.2%

[0072] PH regulator: 0.5%

[0073] Coalescing aid: 5%

[0074] Nano Enhancer: 1%

[0075] Deionized water: 5.3%

[0076] Wherein, the acrylic emulsion is AC2742; the silane coupling agent adopts r-(methacrylic acid oxygen)propyl trimethoxysilane, r-(methacrylic acid oxygen)propyl triisobutoxysilane; The pH regulator uses AMP-95 and sodium bicarbonate; the film-forming aids are DPNB, propylene glycol, and dipropylene glycol monomethyl ether; the nano-enhancer uses nano-silicon dioxide; the defoaming agent The agent is TEGO902W, the leveling agent is EFKA3580, and the thickener is PUR40.

[0077] Follow the steps below:

[0078] 1. Pour AC2742 into the first container, and add r-(methacrylic acid oxygen)propyltrimethoxysilane, r-(methacrylic acid oxygen)propyl Trii...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

Water-based woodenware seal primer and a preparing method thereof are disclosed. The seal primer comprises components in a certain ratio. The method includes adding an acrylic emulsion, a silane coupling agent, a nanometer enhancer, a coalescing agent, a defoaming agent, a leveling agent, a thickening agent and a pH conditioner in order, stirring, filtering and packaging. The seal primer is high in permeability and excellent in sealing performance, and is capable of penetrating into the inside of wood, blocking capillary pores on the surfaces of the wood, allowing the amount of open pores on the surfaces of the wood to be reduced, and making the sealed pores increased, thus inhibiting penetration of water in top paint into a base material so as to achieve excellent anti-expansion effects. A unique paint film enhancing technology is adopted, so that paint film is dried rapidly to achieve film formation. Compact honeycombed paint film is formed on the base material, and tannic acid and grease in the wood are prevented from penetrating to the surface of the paint film, thus achieving anti-expansion and grease-sealing effects.

Description

technical field [0001] The invention relates to a water-based primer, in particular to a water-based wood sealing primer and a preparation method thereof. Background technique [0002] Due to the unique looseness of wood, such as pine wood and medium density fiberboard absorb moisture, wood fibers are easy to swell, and tannins and oils in solid wood can easily penetrate into the surface of the paint film, making the paint film yellow or spit out oil. These are common problems in the construction of water-based wood lacquers, and it is difficult for the water-based wood sealing primers on the market to solve the above problems. In order to solve the problems of solid wood swelling and MDF swelling, fatty wood oil precipitation and tannic acid penetration, the present invention provides a high-performance water-based wood sealing primer, which can inhibit the penetration of water in the upper coating to the substrate, It can also prevent the tannic acid and oil in the wood f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D7/12
CPCC09D133/00C08K3/36C08K2201/011C09D7/40
Inventor 王志坚
Owner 漳州水之采环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com