(meth)acrylic resin composition

A technology of methyl methacrylate and acrylic acid, applied in the direction of coating, can solve the problems of poor appearance, insufficient weather resistance, and inability to fully suppress thermal coloration of molded products, and achieve the effect of good appearance and excellent injection moldability.

Active Publication Date: 2017-09-22
KURARAY CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0015] However, the solutions proposed in the above-mentioned prior art documents are not sufficiently satisfactory due to problems such as a decrease in productivity, insufficient weather resistance, poor appearance of molded products, or inability to sufficiently suppress heat-induced coloring.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • (meth)acrylic resin composition

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0109] 92 parts by mass of purified methyl methacrylate and 8 parts by mass of methyl acrylate were added to an autoclave equipped with a stirrer and a sampling tube to prepare a monomer mixture. The yellowness index of the monomer mixture was 0.9. Add 0.007 parts by mass of a polymerization initiator (2,2'-azobis(2-methylpropionitrile (AIBN), dehydrogenation capacity: 1%, 1-hour half-life temperature: 83°C) to the monomer mixture and chain transfer Agent (n-octyl mercaptan) 0.45 mass parts, make it dissolve to obtain raw material liquid. Utilize nitrogen gas to get rid of the oxygen in the manufacturing device.

[0110] A certain amount of the raw material liquid was discharged from the autoclave, supplied at a constant flow rate to a continuous flow tank reactor controlled at a temperature of 140° C. so that the average residence time was 120 minutes, and bulk polymerization was performed. The reaction liquid was separated from the sampling tube of the reactor and measured ...

Embodiment 2

[0113] Except having changed the quantity of n-octyl mercaptan into 0.42 mass parts, the granular (meth)acrylic-type resin composition of this invention was obtained by the method similar to Example 1. Various physical properties of this granular (meth)acrylic resin composition were evaluated by the same method as Example 1. These results are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

A (meth)acrylic resin composition containing 99.5% by mass or more of a (meth)acrylic resin containing 80 to 100% by mass of methyl methacrylate-derived and 0 to 20% by mass of structural units derived from acrylate, the optical path length of the injection molded product obtained from the (meth)acrylic resin composition at a cylinder temperature of 280°C and a molding cycle of 4 minutes is 200mm The difference between the yellow index YI4 and the yellow index YI1 of the injection molded product with an optical path length of 200mm obtained at a barrel temperature of 280°C and a molding cycle of 1 minute is 3 or less, and the melt under the conditions of 230°C and 3.8kg load The flow rate is above 25 g / 10 minutes.

Description

technical field [0001] The present invention relates to a (meth)acrylic resin composition. More specifically, the present invention relates to a thin-walled and large-area molded article that can obtain a thin-walled and large-area molded product with little residual strain and almost no coloring at high productivity even when injection molding is performed at a low cylinder temperature and a high pressure. base) acrylic resin composition. Background technique [0002] The light guide plate which is a member of a liquid crystal display device is manufactured by injection-molding the resin composition containing transparent resin, such as a (meth)acrylic resin, for example (refer patent document 1). In recent years, there has been a high demand for light-weight and large-area liquid crystal display devices, and accordingly light guide plates have been required to be thinner and larger. [0003] In general, high injection pressure and high cylinder temperature are required f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L33/12B29C45/00C08F220/18C08J5/00B29K33/04
CPCB29C45/0001C08L33/12C08F2/02C08F220/14C08F220/18C08J5/00C08J2333/12C08L33/04
Inventor 新村卓郎小西启之小泽宙栗田日出美田村英孝
Owner KURARAY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap