Stable abrasion-resistant rubber gasket

A wear-resistant rubber and stable technology, applied in the field of wear-resistant rubber pads, can solve problems such as loss of performance and appearance of objects, and achieve the effect of good wear resistance

Inactive Publication Date: 2015-01-21
QINGDAO GAOYUAN PHOTOELECTRIC MEASUREMENT & CONTROL TECH
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In daily life and work places, due to the constant friction between objects and workpieces, as the friction time increases, the appearance of the object will be damaged or even lose its original performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0008] A stable wear-resistant rubber pad is made of the following raw materials in parts by weight:

[0009] 3-5 parts of corn stalks, 7-11 parts of polypropylene ester, 2-9 parts of stearic acid, 10-20 parts of raw methyl vinyl silicone rubber, 4-9 parts of dimethyl trimethylsilyl phosphonate , 5-7 parts of glycerol triglyceride, 1-4 parts of methyl triethoxysilane, 3-5 parts of stearic acid, 2-4 parts of metal manganese powder, 1-4 parts of carbon black N330, clay 2 -6 parts, 4-6 parts of naphthenic oil, 3-8 parts of aluminum hydroxide.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a stable abrasion-resistant rubber gasket which is prepared from the following raw materials in parts by weight: 3-5 parts of corn straw, 7-11 parts of polypropenyl ester, 2-9 parts of stearic acid, 10-20 parts of unvulcanized methylvinyl silicone rubber, 4-9 parts of trimethylsilyl dimethyl methyl phosphonate, 5-7 parts of glycerol triglyceride, 1-4 parts of methyltriethoxysilane, 3-5 parts of stearic acid, 2-4 parts of manganese metal powder, 1-4 parts of carbon black N330, 2-6 parts of argil, 4-6 parts of naphthenic hydrocarbon oil and 3-8 parts of aluminum hydroxide. The stable abrasion-resistant rubber gasket has the advantages of favorable abrasion resistance, stable chemical properties and low deformation tendency.

Description

technical field [0001] The invention relates to a stable wear-resistant rubber pad. Background technique [0002] In daily life and work places, due to the constant friction between objects and workpieces, as the friction time increases, the appearance of the object will be damaged or even lose its original performance. For example, the sole of the shoe needs to have a certain wear resistance, so as to ensure that people will not be easily worn out after daily walking or running sports, so that the service life of the shoe is longer; there are also rubber gaskets, which must prevent wear and tear, so as to ensure Good sealing effect. Therefore, it is of practical significance to increase the wear resistance of the rubber pad. Contents of the invention [0003] Aiming at the deficiencies of the prior art, the problem to be solved by the present invention is to provide a stable wear-resistant rubber pad, which has good wear resistance, and at the same time has stable chemi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)