Diatomite coating with formaldehyde adsorbing and decomposing effects

A technology of diatom coating and formaldehyde, applied in the direction of coating, etc., can solve the problems of inconvenient processing, high use cost, complicated construction technology, etc., and achieve the effect of good catalytic decomposition, strong light oxidation and reduction ability

Active Publication Date: 2015-02-04
中健生命科技(深圳)有限公司
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The house decoration is often limited by the water source, which causes some inconvenience to the processing. In addition, there are strict regulations on the amount of water added, and the construction process is complicated, which has high technical requirements for the construction personnel.
In addition, it is costly to use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Diatomite coating with formaldehyde adsorbing and decomposing effects

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Add 50.4 parts of water to the stirring tank, then add 2 parts of 5040 type dispersant, 0.1 part of 405 type wetting agent, 0.3 part of AGITAN-208 type defoamer, 0.3 part of 400 type polyethylene glycol and 0.3 part of 2-amino- 2-methyl-1-propanol, and stir well. Then add 2 parts of Cu / Al to the stirred tank 2 o 3 Type catalyst, 2 parts of nano-tungsten trioxide and 2 parts of anatase nano-titanium dioxide, and slowly drop 0.5 parts of Kh-570 type silane coupling agent, and stir at high speed to make it evenly dispersed. Finally, add 45 parts of diatomaceous earth to the stirring tank to continue the dispersion, and slowly add 0.1 part of TT-935 thickener, and stir evenly at a medium speed to obtain a diatomite dispersion loaded with decomposable formaldehyde materials for future use.

[0037]Add 26.4 parts of water, 0.5 parts of 5040 dispersant, 0.5 parts of 2,2,4-trimethyl 1,3-pentanediol monoisobutyrate, 0.1 parts of Kh-550 silane coupling agent, 0.5 parts of ethy...

Embodiment 2

[0039] Add 58.5 parts of water to the stirring tank, then add 1.2 parts of 5040 type dispersant, 0.3 parts of 405 type wetting agent, 0.2 parts of AGITAN-208 type defoamer, 0.5 parts of 400 type polyethylene glycol and 0.2 parts of 2-amino- 2-methyl-1-propanol, and stir well. Then add 3 parts of Cu / Al to the stirred tank 2 o 3 Type catalyst, 1.2 parts of nano-tungsten trioxide and 1.2 parts of anatase nano-titanium dioxide, and slowly drop 0.4 parts of Kh-570 type silane coupling agent, and stir at high speed to make it evenly dispersed. Finally, add 33 parts of diatomite to the stirring tank to continue the dispersion, and slowly add 0.3 parts of TT-935 thickener, and stir evenly at a medium speed to obtain a diatomite dispersion loaded with decomposable formaldehyde materials, which is ready for use.

[0040] Add 22.2 parts of water, 1.2 parts of 5040 dispersant, 1.2 parts of 2,2,4-trimethyl 1,3-pentanediol monoisobutyrate, 0.2 parts of Kh-550 silane coupling agent, 1.2 p...

Embodiment 3

[0042] Add 67.3 parts of water to the stirred tank, then add 0.5 parts of 5040 type dispersant, 0.5 part of 405 type wetting agent, 0.1 part of AGITAN-208 type defoamer, 0.8 part of 400 type polyethylene glycol and 0.1 part of 2-amino- 2-methyl-1-propanol, and stir well. Then add 4 parts of Cu / Al to the stirred tank 2 o 3 Type catalyst, 0.5 parts of nano-tungsten trioxide and 0.5 parts of anatase nano-titanium dioxide, and slowly drop 0.2 parts of Kh-570 type silane coupling agent, and stir at high speed to make it evenly dispersed. Finally, add 25 parts of diatomite to the stirring tank to continue the dispersion, and slowly add 0.5 parts of TT-935 thickener, and stir evenly at a medium speed to obtain a diatomite dispersion loaded with decomposable formaldehyde materials for future use.

[0043] In another stirred tank, add 20.6 parts of water, 2 parts of 5040 dispersant, 2 parts of 2,2,4-trimethyl 1,3-pentanediol monoisobutyrate, 0.3 parts of Kh-550 type silane coupling ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention provides a diatomite coating with formaldehyde adsorbing and decomposing effects. The diatomite coating is formed by compounding raw materials comprising a diatomite dispersion liquid loaded with a material capable of decomposing formaldehyde, a 5040 dispersant, 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate, a Kh-550 type silane coupling agent, a polyacrylate thickener, 2-amino-2-methyl-1-propanol, kaolin, mica powder, titanium dioxide powder, octyl phenol polyoxyethylene ether, ethylene glycol, a 705 EVA emulsion, an AGITAN-208 defoaming agent, isothiazolinone, water and the like, wherein the diatomite dispersion liquid loaded with the material capable of decomposing formaldehyde is formed by compounding a Cu / Al2O3 catalyst, anatase-type nanometer titanium dioxide, nanometer tungsten trioxide, diatomite, a 5040-type dispersant, a 405 wetting agent, an AGITAN-208 type defoaming agent, a 400 polyethylene glycol, 2-amino-2-methyl-1-propanol, a Kh-570 type silane coupling agent, a TT-935 thickener and water. The prepared product has formaldehyde adsorbing and decomposing effects.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a diatom coating capable of absorbing and decomposing formaldehyde. Background technique [0002] The sources of formaldehyde in the indoor environment are mainly furniture and fabrics, wood product fillers, construction sources, detergents, cosmetics, and personal products, among which artificial boards are the main sources. Formaldehyde has an irritating effect on the skin and mucous membranes. Inhalation of formaldehyde can cause symptoms such as dizziness, headache, fatigue, and nausea. In severe cases, it can also cause infertility, fetal malformation, and carcinogenicity. According to GB / T18883-2002 "Indoor Air Quality Standard", the formaldehyde content in the air should be ≤0.10mg / m 3 , and many formaldehyde levels in indoor air exceed the national standard, which poses a threat to people's health. [0003] At present, many manufacturers have developed interior decora...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D123/08C09D7/12
CPCC08K2003/2241C09D123/0853C08K2201/011C08K2201/014C08L2205/03C09D7/61C09D7/62C09D7/63C08L33/08C08L71/02C08K13/06C08K9/06C08K3/34C08K5/053C08K3/22
Inventor 吴少勇
Owner 中健生命科技(深圳)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap