Ceramic tile adhesive

A tile adhesive and butyl cellosolve technology, applied in the field of tile adhesives, can solve the problems of environmental pollution, easy peeling, poor durability, etc., achieve good bonding performance, meet bonding requirements, acid, alkali and dirt resistance the effect of corrosion

Inactive Publication Date: 2015-03-11
QINGDAO ZHIGU INNOVATION TECH
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, most of the existing ceramic tile adhesives use cement mortar, which has weak cohesive force, poor durability, and is easy to peel off. Moreover, it adopts the method of stirring and thick layer construction, and the proportion is unstable, which affects the durability of tiles and wastes Raw materials are lost, which also affects the construction speed, pollutes the environment, its safety cannot be guaranteed, and safety accidents are prone to occur

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0008] A kind of ceramic tile adhesive, it is made from the raw material of following parts by weight:

[0009] 8-14 parts of crystalline sodium carbonate, 3-8 parts of borax, 5-9 parts of butyl cellosolve, 1-6 parts of sodium percarbonate, 5-9 parts of graphite powder, 3-5 parts of silicon dioxide, 1-4 parts of kaolin , 2-5 parts of manganese oxide, 9-16 parts of epoxy resin, 4-8 parts of vinyltriamine, 3-9 parts of disodium edetate, 4-6 parts of tricalcium phosphate, 2-8 parts of titanium dioxide , 1-3 parts of boric acid.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A ceramic tile adhesive is composed of the following raw materials in parts by weight: 8-14 parts of crystalline sodium carbonate, 3-8 parts of borax, 5-9 parts of butyl cellosolve, 1-6 parts of sodium percarbonate, 5-9 parts of graphite powder, 3-5 parts of silica, 1-4 parts of kaolin, 2-5 parts of manganese oxide, 9-16 parts of epoxy resin, 4-8 parts of ethylene triamine, 3-9 parts of disodium EDTA, 4-6 parts of tricalcium phosphate, 2-8 parts of titanium dioxide and 1-3 parts of boric acid. The beneficial effects are that: the ceramic tile adhesive is good in adhesive performance, can satisfy the people demand for bonding of ceramic tiles, and is acid, alkali and dirty corrosion resistant.

Description

technical field [0001] The present invention relates to a tile adhesive. Background technique [0002] With the improvement of people's living standards, people have higher and higher requirements for the aesthetic feeling of building houses. Ceramic tiles are people's first choice. However, when ceramic tiles are bonded, special adhesives are needed to meet the requirements of use. Ceramic tile adhesives are mainly used It is suitable for pasting ceramic tiles, face bricks, floor tiles and other decorative materials, and is widely used in the decoration of interior and exterior walls, floors, bathrooms, kitchens and other buildings. However, most of the existing ceramic tile adhesives use cement mortar, which has weak cohesive force, poor durability, and is easy to peel off. Moreover, it adopts the method of stirring and thick layer construction, and the proportion is unstable, which affects the durability of tiles and wastes Raw materials are lost, which also affects the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/14C04B14/10
Inventor 鞠纪恩
Owner QINGDAO ZHIGU INNOVATION TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products