Copper strip rolling oil and preparation method thereof

A technology for rolling oil and copper strip, applied in the field of copper strip rolling oil, can solve problems such as low gloss and easy scratches, achieve high gloss, good lubricating performance, and be suitable for popularization and use

Inactive Publication Date: 2015-03-25
WUXI HEBANG METAL PROD
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Products rolled with existing copper strip rolling oil have low gloss and are prone to scratches

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] The formula of copper strip rolling oil of the present invention is as follows:

[0011] 5.5kg of palm oil, 0.3kg of sodium lauryl sulfonate, 1.1kg of sorbitol, 0.3kg of glycerin, 0.25kg of calcium silicate, 0.25kg of lauric acid diethanolamide, 0.15kg of sodium sulfate, 0.3kg of polyacrylamide, three Sodium polyphosphate 0.4kg, sodium borate 0.3kg, butyl stearate 0.2kg.

[0012] The preparation method of copper strip rolling oil of the present invention is as follows:

[0013] Palm oil 5.5kg, sodium dodecylsulfonate 0.3kg, sorbitol 1.1kg, calcium silicate 0.25kg, lauric acid diethanolamide 0.25kg, sodium sulfate 0.15kg, polyacrylamide 0.3kg, sodium tripolyphosphate Mix 0.4kg, heat to 70°C, and stir for 28 minutes; add 0.3kg of glycerin, 0.3kg of sodium borate, and 0.2kg of butyl stearate, stir at 22°C, and cool to room temperature.

Embodiment 2

[0015] The formula of copper strip rolling oil of the present invention is as follows:

[0016] Palm oil 5kg, sodium lauryl sulfonate 0.2kg, sorbitol 1.2kg, glycerin 0.4kg, calcium silicate 0.2kg, lauric acid diethanolamide 0.2kg, sodium sulfate 0.1kg, polyacrylamide 0.4kg, trimer Sodium phosphate 0.5kg, sodium borate 0.2kg, butyl stearate 0.1kg.

[0017] The preparation method of copper strip rolling oil of the present invention is as follows:

[0018] Palm oil 5kg, sodium dodecylsulfonate 0.2kg, sorbitol 1.2kg, calcium silicate 0.2kg, lauric acid diethanolamide 0.2kg, sodium sulfate 0.1kg, polyacrylamide 0.4kg, sodium tripolyphosphate 0.5 kg, heated to 65°C, and stirred for 30 minutes; added 0.4kg of glycerin, 0.2kg of sodium borate, and 0.1kg of butyl stearate, stirred at 20°C, and cooled to room temperature.

Embodiment 3

[0020] The formula of copper strip rolling oil of the present invention is as follows:

[0021] 6kg of palm oil, 0.4kg of sodium lauryl sulfonate, 0.8kg of sorbitol, 0.2kg of glycerin, 0.3kg of calcium silicate, 0.3kg of lauric acid diethanolamide, 0.2kg of sodium sulfate, 0.2kg of polyacrylamide, trimer Sodium phosphate 0.3kg, sodium borate 0.4kg, butyl stearate 0.3kg.

[0022] The preparation method of copper strip rolling oil of the present invention is as follows:

[0023] Palm oil 6kg, sodium dodecylsulfonate 0.4kg, sorbitol 0.8kg, calcium silicate 0.3kg, lauric acid diethanolamide 0.3kg, sodium sulfate 0.2kg, polyacrylamide 0.2kg, sodium tripolyphosphate 0.3 kg, heated to 75°C, and stirred for 25 minutes; added 0.2kg of glycerin, 0.4kg of sodium borate, and 0.3kg of butyl stearate, stirred at 25°C, and cooled to room temperature.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides copper strip rolling oil. The copper strip rolling oil is composed of the following components in parts by mass: 5-6 parts of palm oil, 0.2-0.4 part of sodium dodecyl sulfonate, 0.8-1.2 parts of sorbitol, 0.2-0.4 part of glycerin, 0.2-0.3 part of calcium silicate, 0.2-0.3 parts of lauric diethanolamide, 0.1-0.2 part of sodium sulfate, 0.2-0.4 part of polyacrylamide, 0.3-0.5 part of sodium tripolyphosphate, 0.2-0.4 part of sodium borate and 0.1-0.3 part of butyl stearate. The invention also provides a preparation method of the copper strip rolling oil. A copper strip rolled by using the copper strip rolling oil provided by the invention is high in glossiness, free of scratches and good in lubricating property. In addition, the preparation method of the copper strip rolling oil, provided by the invention, is simple and suitable for popularization and application.

Description

technical field [0001] The invention relates to a copper strip rolling oil. Background technique [0002] Rolling is a processing method in which metal passes through the gap between two relatively rotating rolls on a rolling mill, and is rolled and deformed into profiles (such as steel plates, round steel, angle steel, etc.). The main function of rolling oil is to reduce the friction between the roll and the copper strip and foil, provide a stable friction interface, realize stable rolling, and improve the surface quality. Products rolled with existing copper strip rolling oil have low gloss and are prone to scratches. Contents of the invention [0003] The invention provides a copper strip rolling oil. Copper strips rolled using the copper strip rolling oil of the invention have good gloss and no scratches; therefore, the invention also provides a preparation method thereof. [0004] The invention provides a copper strip rolling oil. The copper strip rolling oil is com...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C10M169/04C10N40/24
Inventor 邓义增
Owner WUXI HEBANG METAL PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap