Wire drawing lubricant

A technology of wire drawing oil and palm oil, which is applied in the field of wire drawing oil, can solve the problems of poor lubrication and cooling performance of wire drawing oil, and achieve the effect of excellent lubrication performance, good lubrication and cooling performance, and good thermal conductivity

Inactive Publication Date: 2015-03-25
WUXI HEBANG METAL PROD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing wire drawing oil has poor lubricating and cooling performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] The formula of drawing oil of the present invention is as follows:

[0011] Palm oil 18kg, epoxy soybean oil 4kg, polyethylene glycol 0.6kg, sodium stearate 1.4kg, triethanolamine borate 2kg, sodium sorbitol 0.25kg, benzotriazole 0.8kg, urea 2.2kg, water 1000kg.

[0012] The preparation method of drawing oil of the present invention is as follows:

[0013] Mix 2kg of triethanolamine borate, 0.25kg of sodium sorbitol, 4kg of epoxidized soybean oil, 0.8kg of benzotriazole, and 1000kg of water, heat to 72°C, and stir for 28 minutes; add 18kg of palm oil, 0.6 kg, 1.4kg of sodium stearate and 2.2kg of urea, stirred for 18min, and cooled to room temperature.

Embodiment 2

[0015] The formula of drawing oil of the present invention is as follows:

[0016] Palm oil 15kg, epoxy soybean oil 3kg, polyethylene glycol 0.5kg, sodium stearate 1.2kg, triethanolamine borate 1.5kg, sodium sorbitol 0.2kg, benzotriazole 0.9kg, urea 2.5kg, 1000kg of water.

[0017] The preparation method of drawing oil of the present invention is as follows:

[0018] Mix 1.5kg of triethanolamine borate, 0.2kg of sodium sorbitol, 3kg of epoxidized soybean oil, 0.9kg of benzotriazole, and 1000kg of water, heat to 70°C, and stir for 30 minutes; add 15kg of palm oil, polyethylene glycol 0.5kg, sodium stearate 1.2kg and urea 2.5kg, stirred for 20min, cooled to room temperature.

Embodiment 3

[0020] The formula of drawing oil of the present invention is as follows:

[0021] Palm oil 20kg, epoxy soybean oil 5kg, polyethylene glycol 0.8kg, sodium stearate 1.5kg, triethanolamine borate 2.5kg, sodium sorbitol 0.3kg, benzotriazole 0.6kg, urea 2kg, water 1000kg.

[0022] The preparation method of drawing oil of the present invention is as follows:

[0023] Mix 2.5kg of triethanolamine borate, 0.3kg of sodium sorbitol, 5kg of epoxidized soybean oil, 0.6kg of benzotriazole, and 1000kg of water, heat to 75°C, and stir for 25 minutes; add 20kg of palm oil, polyethylene glycol 0.8kg, 1.5kg of sodium stearate and 2kg of urea, stirred for 15 minutes, and cooled to room temperature.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a wire drawing lubricant. The wire drawing lubricant is prepared from the following components in parts by mass: 15-20 parts of palm oil, 3-5 parts of epoxidized soybean oil, 0.5-0.8 part of polyethylene glycol, 1.2-1.5 parts of sodium stearate, 1.5-2.5 parts of triethanolamine borate, 0.2-0.3 part of sodium sorbitol, 0.6-0.9 part of benzotriazole, 2-2.5 parts of urea and 1000 parts of water. The wire drawing lubricant provided by the invention is favorable in lubricating performance, and the surface brightness of a machined part is high. The wire drawing lubricant is a water-based wire drawing lubricant so as to be good in heat conducting property. Due to the adoption of the urea, the surface of metal can be brighter; and meanwhile, the urea can play a certain antirust effect on cutters and machine tools.

Description

Technical field [0001] The invention relates to a drawing oil. Background technique [0002] Drawing oil is mainly used in the following aspects: 1. The drawing process of various wire materials and wires; 2. The drawing process of copper-clad steel wire, bronze-plated bead steel wire, and copper-plated steel wire for the lead wires of electronic components; 3. , Drawing of smooth steel wire. Existing drawing oil has poor lubrication and cooling properties. Contents of the invention [0003] The invention provides a wire drawing oil with good lubrication and cooling properties. [0004] The invention provides a drawing oil, which is prepared from the following components by mass: 15-20 parts of palm oil, 3-5 parts of epoxidized soybean oil, 0.5-0.8 parts of polyethylene glycol, 1.2-1.5 parts of sodium stearate, 1.5-2.5 parts of triethanolamine borate, 0.2-0.3 parts of sodium sorbitol, 0.6-0.9 parts of benzotriazole, 2-2.5 parts of urea, and 1000 parts of water. [0005...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C10M173/00B21C9/02C10N40/24
Inventor 邓义增
Owner WUXI HEBANG METAL PROD
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More