Novel material capable of imitating multiple ornamental sculpture stone materials and manufacturing process of novel material

A new type of material, stone technology, applied in the field of architectural decoration, to achieve the effect of low demoulding time, high mold utilization rate and short setting time

Active Publication Date: 2015-04-01
广州新尚艺术股份有限公司
View PDF3 Cites 37 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This type of product can only be achieved by using cement, which is often used in construction, as the coagulating material, and then matched with natural stone-colored sand. However, various types of cement on the market can achieve white color, high strength, fast setting, simple manufacturing process, and durability. There is no requirement for excellent performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] In the embodiment of the present invention, a new type of material imitating a variety of decorative sculpture stones, the raw materials according to weight percentages include: 50% coagulation materials, 50% natural stone sand, and the raw materials of the coagulation materials include sulfoaluminate according to weight percentages. Salt cement clinker 48.8%, white gypsum 11%, calcium carbonate powder 9%, high-grade talc 26%, superplasticizer 3%, color powder 1.6%, coagulant 0.6%, the natural stone sand is in weight percentage The raw materials include: 43% pure white sand with a particle size of 1mm, 45% pure white sand with a particle size of 0.2mm, and 12% pure red sand with a particle size of 1mm.

[0033] The specific steps of the grinding method of the condensed material are as follows:

[0034] (1) Weigh the raw materials of the grinding condensed material according to the weight percentage;

[0035] (2) Open the closed ball mill, add sulphoaluminate cement clinker fo...

Embodiment 2

[0054] In the embodiment of the present invention, a new type of material imitating a variety of decorative sculpture stones, the raw materials in terms of weight percentages include: 55% of coagulation materials, 45% of natural stone sand, and the raw materials of the coagulation materials in terms of weight percentages include: sulfoaluminate 53% of salt cement clinker, 10% of white gypsum, 8% of calcium carbonate powder, 25% of high-grade talc, 2% of superplasticizer, 1.5% of color powder, 0.5% of setting agent, the natural stone sand is in weight percentage The raw materials include: 50% pure white sand with a particle size of 1.5mm, 40% pure white sand with a particle size of 0.4mm, 5% pure purple sand with a particle size of 1.4mm, and 5% pure red sand with a particle size of 1.6mm.

[0055] The specific steps of the grinding method of the condensed material are as follows:

[0056] (1) Weigh the raw materials of the grinding condensed material according to the weight percent...

Embodiment 3

[0076] In the embodiment of the present invention, a new type of material imitating a variety of decorative sculpture stones, the raw materials according to weight percentages include: 60% coagulation material, 40% natural stone sand, and the raw materials of the coagulation material include sulphoaluminate according to weight percentage. Salt cement clinker 57.2%, white gypsum 9%, calcium carbonate powder 7%, high-grade talc 24%, superplasticizer 1%, color powder 1.4%, setting agent 0.4%, the natural stone sand is in weight percentage The raw materials include: pure white sand with a particle size of 2mm, 57%, a particle size of 0.5mm, 35%, and a particle size of 1.8mm, 8%.

[0077] The specific steps of the grinding method of the condensed material are as follows:

[0078] (1) Weigh the raw materials of the grinding condensed material according to the weight percentage;

[0079] (2) Open the closed ball mill, add sulphoaluminate cement clinker and mill for 20 minutes;

[0080] (3) ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a novel material capable of imitating multiple ornamental sculpture stone materials. The novel material is prepared from a coagulation material and natural stone sand in percentage by weight, wherein the coagulation materials comprises the following raw materials in percentage by weight: sulfate aluminum cement clinker, white stone, calcium carbonate powder, high-class talcum powder, a super plasticizer, color powder and a thickening time control agent; the natural stone sand comprises the following raw materials in percentage by weight: pure white sand with the grain fineness of 1-2 mm, pure white sand with the grain fineness of 0.2-0.5 mm and colored sand with the grain fineness of 1-2 mm; the colored sand comprises one or two or more of pure red sand, pure pulp sand, pure blue sand and sand of other colors. The raw materials are finely grinded and compounded to obtain a coagulation material which is white in color, short in coagulation time and high in strength, various stone surface effects are achieved when various natural stone sands are compounded, the novel material can be produced in batch, and compared with a manner that sculptures are directly carved on stone materials, the novel material is much excellent in working efficiency, good in consistency of sculpture products, good in pattern abutting of finished products and low in production cost.

Description

Technical field [0001] The invention relates to the technical field of architectural decoration, in particular to a new type of material and manufacturing process for imitating various decorative sculpture stones. Background technique [0002] Among the many building decoration materials, stone has always been a commonly used decoration material with a rich choice of durable colors. With the progress of the times and changes in people's aesthetics, decorative stone is no longer satisfied with the original flat shape, and people begin to request Carving stone into various shapes and patterns for decoration, but the cost of stone carving is very high and expensive. In order to well solve the demand for such decorations, the idea of ​​developing imitation stone sculpture works of art came into being. [0003] First, the production cost of imitation stone sculpture artwork is lower than that of stone carving products, and the production efficiency is higher than that of stone carving....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/14B44C5/00B44C3/04B44F9/04B28B1/087B28B11/24
Inventor 舒浩
Owner 广州新尚艺术股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com