Preparation method of special inorganic anti-veining additive for casting

An additive and veining technology, used in casting molding equipment, metal processing equipment, casting molds, etc., can solve the problems of large weakening effect of sand mold strength, poor anti-veining effect, and small inhibition effect, so as to prevent casting veining. Grain defects, good anti-veining effect, anti-cracking effect

Active Publication Date: 2016-05-11
共享新材料(山东)有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Although the veining defect can be improved by replacing silica sand with pearl sand and the like to inhibit its phase transformation expansion, pearl sand is much more expensive than silica sand, and the casting cost is too high; and the addition of traditional inorganic anti-veining additives is high. The weakening effect of the sand mold strength is large, and the plasticity is small, and the inhibition effect on the phase change expansion cracking of the silica sand mold is small, and the anti-veining effect is not good.
[0005] There is currently no way to overcome the above drawbacks

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Embodiment one: a kind of preparation method of special inorganic anti-veining additive for casting, the method comprises the following steps:

[0020] a. Sieve iron oxide red and iron oxide black with a 70-mesh sieve respectively, discard the sieve, and keep the sieve residue for subsequent use;

[0021] b. Sieve the spodumene, kyanite, and hollow microspheres with a 30-mesh sieve respectively, discard the sieve, and keep the sieve residue for subsequent use;

[0022] c. Weigh 340kg of red iron oxide, 260kg of black iron oxide, 150kg of spodumene, 90kg of kyanite, and 80kg of hollow microspheres after sieving, weigh 50kg of lithium carbonate, and 30kg of potassium carbonate, and add special stirring and mixing equipment in turn, Then turn on the stirring for mixing, after the mixing is completed, the material is discharged.

Embodiment 2

[0023] Embodiment two: a kind of preparation method of special inorganic anti-veining additive for casting, the method comprises the following steps:

[0024] a. Sieve iron oxide red and iron oxide black with a 70-mesh sieve respectively, discard the sieve, and keep the sieve residue for subsequent use;

[0025] b. Sieve the spodumene, kyanite, and hollow microspheres with a 30-mesh sieve respectively, discard the sieve, and keep the sieve residue for subsequent use;

[0026] c. Weigh 300kg of red iron oxide, 280kg of black iron oxide, 180kg of spodumene, 80kg of kyanite, and 100kg of hollow microspheres after sieving, weigh 40kg of lithium carbonate, and 20kg of potassium carbonate, and then add special stirring and mixing equipment in turn. Then turn on the stirring for mixing, after the mixing is completed, the material is discharged.

Embodiment 3

[0027] Embodiment three: a kind of preparation method of casting special inorganic anti-veining additive, this method comprises the following steps:

[0028] a. Sieve iron oxide red and iron oxide black with a 70-mesh sieve respectively, discard the sieve, and keep the sieve residue for subsequent use;

[0029] b. Sieve the spodumene, kyanite, and hollow microspheres with a 30-mesh sieve respectively, discard the sieve, and keep the sieve residue for subsequent use;

[0030] c. Weigh 400kg of red iron oxide, 250kg of black iron oxide, 120kg of spodumene, 100kg of kyanite, 60kg of hollow microspheres after sieving, weigh 30kg of lithium carbonate, and 40kg of potassium carbonate, and add special stirring and mixing equipment in turn, Then turn on the stirring for mixing, after the mixing is completed, the material is discharged.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a preparation method of an additive, and in particular relates to a preparation method of a special inorganic anti-veining additive for casting. The method comprises the following steps: respectively sieving iron oxide red and black iron oxide through a sieve of 70mesh; removing oversize materials and remaining the residues on the sieve for later use; respectively sieving spodumene, kyanite and hollow microspheres through a sieve of 30mesh; removing oversize materials and remaining the residues on the sieve for later use; sequentially feeding the sieved raw materials, potassium carbonate and lithium carbonate into a special agitating device according to a technical formula; then starting to agitate for mixing; discharging after mixing. The special inorganic anti-veining additive has the advantages that the addition quantity is small, the influence on the strength of moulding sand is low, the anti-veining effect is good, and the production cost can be effectively decreased.

Description

technical field [0001] The invention relates to a preparation method of an additive, in particular to a preparation method of a special inorganic anti-veining additive for casting. Background technique [0002] When producing automobile cylinder blocks and cylinder heads, thin burrs or veining defects often appear in the intake and exhaust passages, the inner cavity of the water jacket, and the inner corners of the heat joints. Because the burrs are located in the inner cavity, it is difficult to clean, and the veins in the water jacket cavity Defects will hinder the normal flow of cooling water, and in severe cases, the engine will burn; the veins in the intake and exhaust passages will affect the vortex characteristics of the air passage, and seriously affect the performance of the engine. is crucial. [0003] The root cause of the veining defects on the casting surface is the cracking of the sand mold caused by the expansion of silica sand at 573°C. At a temperature of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B22C1/02
CPCB22C1/02
Inventor 陈学更王娟娟韩文
Owner 共享新材料(山东)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products