Bamboo strip softener and preparation process thereof

A softener and bamboo strip technology, which can be used in the manufacture of tools, wood processing utensils, reed/straw treatment, etc., can solve the problems of too simple softening method, easy roasting and breaking of bamboo, affecting the toughness and strength of bamboo, etc. Use, softening effect, better effect

Inactive Publication Date: 2015-04-22
界首市祥雨竹编专业合作社
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The existing bamboo sticks are generally softened in the traditional way of roasting. After the bamboo is roasted, it can be bent and woven into various products. This softening method is too simple, and it is easy to break the bamboo, which affects the toughness and strength of the bamboo.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Embodiment 1: bamboo strip softening agent, it is characterized in that: comprise 28 parts of strength improvers, 41 parts of shape retaining agents, 66 parts of softening agents, 16 parts of initiators, 10 parts of accelerators, 130 parts of water;

[0015] Strength improver: stearyl alcohol 60%, stearic acid 40%;

[0016] Form retaining agent: 15% stearic acid, 65% ethyl carbamate, 20% paraffin;

[0017] Softener: glycerol 20%, alcohol ether glycoside 20%, polyoxyethylene ether 30%, surfactant 30%;

[0018] Initiator: potassium persulfate 15%, formaldehyde 25%, ammonium persulfate 60%;

[0019] Accelerator: 40% cobalt naphthenate, 30% dimethylaniline, 30% calcium carbonate.

[0020] Preparation method of bamboo stick softener: it is characterized in that: take glycerin, alcohol ether glycoside, polyoxyethylene ether, and surfactant, put them into a stirring tank, stir for 30 minutes, and the stirring temperature is 80°C, and then add potassium persulfate , formalde...

Embodiment 2

[0023] Embodiment 2: bamboo strip softening agent, it is characterized in that: comprise 34 parts of strength improvers, 48 ​​parts of shape retaining agents, 71 parts of softening agents, 19 parts of initiators, 16 parts of accelerators, 140 parts of water;

[0024] Strength improver: stearyl alcohol 70%, stearic acid 30%;

[0025] Form retaining agent: 25% stearic acid, 65% ethyl carbamate, 15% paraffin;

[0026] Softener: glycerol 30%, alcohol ether glycoside 30%, polyoxyethylene ether 20%, surfactant 20%;

[0027] Initiator: potassium persulfate 25%, formaldehyde 20%, ammonium persulfate 55%;

[0028] Accelerator: 40% cobalt naphthenate, 30% dimethylaniline, 30% calcium carbonate.

[0029] Preparation method of bamboo stick softener: it is characterized in that: take glycerin, alcohol ether glycoside, polyoxyethylene ether, and surfactant, put them into a stirring tank, stir for 30 minutes, and the stirring temperature is 80°C, and then add potassium persulfate , formal...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a bamboo strip softener and a preparation process thereof. The bamboo strip softener is prepared by the following steps: weighing glycerol, alkylethoxyglucoside, polyoxyethylene ether and a surfactant, putting into a stirring tank, stirring for 30 minutes with the stirring temperature to be 80 DEG C, then adding potassium persulfate, formaldehyde and ammonium persulfate, simultaneously adding cobalt naphthenate, dimethylaniline and calcium carbonate, rapidly stirring for 3 minutes with the stirring temperature to be 130 DEG C, finally adding stearyl alcohol, stearic acid, stearic acid, urethane and paraffin, stirring for 1h, and cooling at room temperature. The bamboo strip softener has the beneficial effects that the prepared softener is good in softening effect without corrosion and good in effect, is capable of strengthening the strength and the toughness of the softening part and is convenient in popularization and using.

Description

Technical field: [0001] The invention relates to the technical field of bamboo softening, in particular to a bamboo strip softener and a preparation process thereof. Background technique: [0002] The existing bamboo sticks are generally softened in the traditional way of roasting. After the bamboo is roasted, it can be bent and woven into various products. This softening method is too simple, and it is easy to break the bamboo, which affects the toughness and strength of the bamboo. . Invention content: [0003] The technical problem to be solved by the present invention is to overcome the defects of the prior art and provide a softener for bamboo sticks and a preparation process thereof. [0004] The technical problem to be solved by the present invention is realized by the following technical solutions. [0005] The softening agent for bamboo strips is characterized in that: it includes 28-34 parts of strength improving agent, 41-48 parts of shape maintaining agent, 6...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B27K3/52B27K5/06
CPCB27K3/52B27K5/06B27K9/002
Inventor 王银
Owner 界首市祥雨竹编专业合作社
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com