Ceramic cup containing tourmaline and six-ring rock and preparation method thereof

A technology of hexacyclic stone and tourmaline, applied in the field of daily-use ceramics, can solve the problems of poor plasticity and achieve the effects of good comprehensive performance, promotion of human health, and low production cost

Inactive Publication Date: 2015-04-22
FOSHAN MINGQIAN TECH
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Ceramic materials generally have higher hardness, but poor plasticity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A ceramic cup containing tourmaline and hexagonite is made of the following components in parts by weight:

[0022] 4.5 parts of tourmaline, 5 parts of hexacyclite, 13 parts of potassium feldspar, 13 parts of albite, 2 parts of raw talc, and 3 parts of magnesium oxide.

[0023] Its preparation method comprises the following steps:

[0024] Weigh the above-mentioned substances according to the stated ratio, ball mill for 30 minutes, add the powder obtained by ball milling to 1 times its weight in deionized water to make ceramic mud, and make a ceramic green body; then fire at 1100°C for 7 hours, and cool to After grinding and planing at room temperature, the product is obtained.

Embodiment 2

[0026] A ceramic cup containing tourmaline and hexagonite is made of the following components in parts by weight:

[0027] 3.5 parts of tourmaline, 3 parts of hexacyclite, 10 parts of potassium feldspar, 10 parts of albite, 1 part of raw talc, 2 parts of magnesium oxide.

[0028] Its preparation method comprises the following steps:

[0029] Weigh the above-mentioned substances according to the stated ratio, ball mill for 35 minutes, add the powder obtained by ball milling to 1.5 times its weight in deionized water to make ceramic mud, and make a ceramic green body; then fire at 1150°C for 7.5 hours, and cool to After grinding and planing at room temperature, the product is obtained.

Embodiment 3

[0031] A ceramic cup containing tourmaline and hexagonite is made of the following components in parts by weight:

[0032] 3 parts of tourmaline, 3 parts of hexacyclic stone, 10 parts of potassium feldspar, 13 parts of albite feldspar, 2 parts of raw talc, 3 parts of magnesium oxide;

[0033] Its preparation method comprises the following steps:

[0034] Weigh the above-mentioned substances according to the stated ratio, ball mill for 33 minutes, add the powder obtained by ball milling to 1.3 times its weight in deionized water to make ceramic mud, and make a ceramic green body; then fire at 1125°C for 7.3 hours, and cool to After grinding and planing at room temperature, the product is obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a ceramic cup containing tourmaline and six-ring rock and a preparation method thereof, belonging to the technical field of domestic ceramics. The ceramic cup comprises the following raw material components in parts by weight: 1-5 parts of tourmaline, 1-5 parts of six-ring rock, 10-15 parts of potassium feldspar, 10-15 parts of albite, 1-3 parts of raw talc and 2-4 parts of magnesium oxide. The preparation method comprises the following steps: proportionally weighing the substances, performing ball milling for 30-35 minutes, adding deionized water which is 1-1.5 times the powder obtained by the ball milling in weight to obtain ceramic pug, and preparing a ceramic body from the ceramic pug; and firing for 7-7.5 hours at 1,100-1,150 DEG C, cooling to room temperature and polishing to obtain the product. The ceramic cup has good comprehensive properties and realizes a certain effect on promoting health of a human body after long-time use; and the process is simple and easy to implement, and the production cost is relatively low.

Description

technical field [0001] The invention relates to a ceramic cup, in particular to a ceramic cup containing tourmaline and hexagonite and a preparation method thereof, belonging to the technical field of daily-use ceramics. Background technique [0002] Ceramics is the general term for pottery and porcelain. Humans invented pottery as early as the Neolithic Age, about 8000 BC. Ceramic materials are mostly oxides, nitrides, borides and carbides. Common ceramic materials are clay, alumina, kaolin and so on. Ceramic materials generally have higher hardness, but poor plasticity. In addition to the use of tableware and decoration, it also plays an important role in the development of science and technology. The raw material of ceramics is obtained by quenching the earth's original large resource clay. The nature of clay is tough, it can be molded when it meets water at room temperature, it can be carved when it is slightly dry, and it can be ground when it is completely dry; it...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B35/16
Inventor 黄朝阳
Owner FOSHAN MINGQIAN TECH
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com