PFA fluorine color masterbatch and production process thereof

A production process and color masterbatch technology, applied in the field of fluoroplastic color masterbatch, can solve the problems of poor electrical insulation performance, short service life, poor corrosion resistance, etc., and achieve high insulation resistance, long service life and excellent electrical insulation performance Effect

Inactive Publication Date: 2015-04-29
WANLI SHENZHEN IND
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the formulation technology and processing technology of fluoroplastic color masterbatches, especially PFA fluoroplastic color masterbatches, have been monopolized by f

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PFA fluorine color masterbatch and production process thereof
  • PFA fluorine color masterbatch and production process thereof

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach

[0029] figure 1 It shows the production process of the PFA fluorochrome masterbatch disclosed in the present invention, which can be directly used in the standardized production of the fluorochrome masterbatch of the PFA formula disclosed in the present invention, and can finally produce the PFA shown in the table at the end of this section Performance parameters of fluorochrome masterbatch.

[0030] The PFA fluorine masterbatch of the present invention can be made from the raw materials of the following weight ratio:

[0031] 65%~85% PFA;

[0032] 8%~25% high temperature pigment;

[0033] 3% to 6% dispersant;

[0034] 0.1% to 2% processing aids.

[0035] Such as figure 1 As shown, the present invention also discloses a production process for preparing the above-mentioned a kind of PFA fluorine masterbatch, comprising the following steps:

[0036] (1) Ingredients: 65% to 85% of PFA, 8% to 25% of high temperature pigment, 3% to 6% of dispersant and 0.1% to 2% of processin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a PFA fluorine color masterbatch and a production process thereof. The PFA fluorine color masterbatch produced by virtue of a formula and the production process has excellent corrosion resistance and electrical insulation performance and is relatively long in service life and low in cost. The PFA fluorine color masterbatch is produced from the following raw materials in percentage by weight: 65%-85% of PFA, 8%-25% of a high-temperature pigment, 3%-6% of a dispersing agent and 0.1%-2% of a machining aid. The invention also discloses the production process of the PFA fluorine color masterbatch, comprising the following steps: (1) burdening; (2) molding by extrusion; (3) cooling; (4) granulating; (5) dehydrating; (6) sorting; (7) drying; and (8) packaging and warehousing.

Description

technical field [0001] The invention relates to the field of fluoroplastic color masterbatch, in particular to PFA fluorine color masterbatch and its production process. Background technique [0002] Fluoroplastic color masterbatches are mainly used in internal wires and lead wires of aviation, ships, electronic equipment, wires and cables in public places such as computer networks, subways, vehicles, high-rise buildings, internal wires of traditional communication equipment and other fluoroplastic products; [0003] The application of PFA (soluble polytetrafluoroethylene) fluorine masterbatch in fluoroplastic masterbatch is very extensive. PFA is mainly a copolymer of a small amount of perfluoropropyl perfluorovinyl ether and polytetrafluoroethylene. Enhanced melt adhesion, decreased melt viscosity, and no change in performance compared with PTFE; excellent chemical resistance, corrosion resistance to all chemicals, lowest coefficient of friction among plastics, and good E...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L27/18C08J3/22B29C47/92B29C48/92
CPCC08L27/18B29B9/06B29C48/92B29C2948/92704C08J3/226C08J2423/18C08L2201/02C08L2201/08C08L2310/00
Inventor 周志坚
Owner WANLI SHENZHEN IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap