Beta/ZSM-12 composite molecular sieve and its synthesis method

A technology of ZSM-12 and composite molecular sieve, which is applied in the direction of ZSM-12 crystalline aluminum silicate zeolite, molecular sieve and alkali exchange compound, molecular sieve catalyst, etc., can solve the first component damage, affect the adsorption and catalytic performance, composite structure Difficult to control and other issues, to achieve the effect of maintaining integrity, avoiding the decrease of crystallinity, improving physical and chemical properties and catalytic activity

Active Publication Date: 2015-05-06
CHINA PETROLEUM & CHEM CORP +1
View PDF8 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] However, there are still many defects and deficiencies in the synthesis technology of composite molecular sieves, which cause some deficiencies in the physical and chemical properties of composite molecular sieves.
For example, the composite structure of composite molecular sieves is not easy to control, and the acid properties are also difficult to adjust.
Moreover, many composite molecular sieves are synthesized by a two-step method, which easily causes damage to the first component during the compounding process, which reduces the physical and chemical properties of the composite molecular sieve, thereby affecting the adsorption and catalytic performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Beta/ZSM-12 composite molecular sieve and its synthesis method
  • Beta/ZSM-12 composite molecular sieve and its synthesis method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] (1) Dissolve 40 g of glucose in 100 mL of distilled water, add 8 g of ZSM-12 molecular sieves into the glucose solution under stirring conditions, stir for 30 min, place the mixture in an ultrasonic cleaner for 2 h, and then The mixture was filtered, and the obtained product was dried at 120 °C for 12 h, and then calcined at 500 °C for 2 h in a nitrogen atmosphere to obtain a pretreated ZSM-12 molecular sieve.

[0036] (2) Dissolve 0.25 g of sodium hydroxide in 30 mL of 25% TEAOH and stir for 30 min. Then add 0.5 g of sodium aluminate and stir for 30 min. Add 7 g of white carbon black slowly and stir for 30 min. Then put it into a closed reactor and crystallize in an oven at 140 °C for 4 h.

[0037] (3) Mix 5 g of ZSM-12 prepared in step (1) with the pre-crystallized colloid prepared in step (2), and stir for 30 min; then put it into a closed reactor and crystallize in an oven at 140 °C for 10 h. Then the obtained product was washed 4 times with distilled water to ne...

Embodiment 2

[0039] (1) Dissolve 40 g of glucose in 100 mL of distilled water, add 8 g of ZSM-12 molecular sieves into the glucose solution under stirring conditions, stir for 30 min, place the mixture in an ultrasonic cleaner for 2 h, and then The mixture was filtered, and the obtained product was dried at 120 °C for 12 h, and then calcined at 500 °C for 2 h in a nitrogen atmosphere to obtain a pretreated ZSM-12 molecular sieve.

[0040] (2) Dissolve 0.25 g of sodium hydroxide in 30 mL of 25% TEAOH and stir for 30 min. Then add 0.5 g of sodium aluminate and stir for 30 min. Add 6 g of white carbon black slowly and stir for 30 min. Then put it into a closed reactor and crystallize in an oven at 150 °C for 3 h.

[0041] (3) Mix 6 g of ZSM-12 prepared in step (1) with the pre-crystallized colloid prepared in step (2), and stir for 30 min; then close the reactor and crystallize in an oven at 150 °C for 12 h. Then the obtained product was washed 4 times with distilled water to neutrality, t...

Embodiment 3

[0043] (1) Dissolve 35 g of glucose in 100 mL of distilled water, add 7 g of ZSM-12 molecular sieves into the glucose solution under stirring conditions, stir for 30 min, place the mixture in an ultrasonic cleaner for 2 h, and then place the mixture After filtering, the obtained product was dried at 120° C. for 12 h, and then calcined at 550° C. for 1.5 h in a nitrogen atmosphere to obtain a pretreated ZSM-12 molecular sieve.

[0044] (2) Dissolve 0.2 g of sodium hydroxide in 25 mL of 25% TEAOH and 10 mL of distilled water, and stir for 30 min. Then add 0.5 g of aluminum nitrate and stir for 30 min. Add 7 g of white carbon black slowly and stir for 30 min. Then put it into a closed reactor and crystallize in an oven at 150 °C for 2 h.

[0045] (3) Mix 8 g of ZSM-12 prepared in step (1) with the pre-crystallized colloid prepared in step (2), and stir for 30 min; then put it into a closed reaction kettle, and crystallize in an oven at 150 °C for 52 h. Then the obtained produc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a Beta / ZSM-12 composite molecular sieve. The Beta / ZSM-12 composite molecular sieve has the following two crystal forms at the same time: a ZSM-12 molecular sieve and a Beta molecular sieve. The synthesis method for the Beta / ZSM-12 composite molecular sieve provided by the invention comprises the following steps: adding the ZSM-12 molecular sieve into a glucose solution for pretreatment so as to obtain a treated ZSM-12 molecular sieve; then mixing water, an alkali source, a template agent, an aluminum source and a silicon source and carrying out high-temperature crystallization so as to prepare pre-crystallized colloid; then mixing the pre-crystallized colloid with the treated ZSM-12 molecular sieve and carrying out crystallization at a temperature of 100 to 180 DEG C for 5 to 25 h so as to obtain the Beta / ZSM-12 composite molecular sieve. According to the invention, glucose is introduced into the pores of the ZSM-12 molecular sieve and becomes carbon after roasting; the carbon occupies the pore channels of the ZSM-12 molecular sieve to prevent alkali from entering the interior of ZSM-12 molecular sieve crystals, so the ZSM-12 molecular sieve is not destroyed in the process of crystallization and the integrity of crystal structure is maintained, which are beneficial for improving the physical and chemical properties and the catalytic activity of the Beta / ZSM-12 composite molecular sieve.

Description

technical field [0001] The invention belongs to the field of synthesis of molecular sieve catalytic materials, in particular to a Beta / ZSM-12 composite molecular sieve and a synthesis method thereof. Background technique [0002] Composite molecular sieve is a composite molecular sieve with a special structure, which is a co-crystal formed by two or more molecular sieves, or a composite crystal with the structural characteristics of two or more molecular sieves. Due to the particularity of the composite molecular sieve structure, this molecular sieve has a more reasonable distribution of acidity and good hydrothermal stability, overcomes the limitations of its components, better meets the needs of industrial applications, and has a wide range of applications. Application prospects. [0003] At present, there are many technologies about composite molecular sieves. For example, CN1583562A discloses a double microporous zeolite molecular sieve and its preparation method. The ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C01B39/42B01J20/18B01J29/80
CPCC01B39/023B01J29/80C01P2002/72C01P2006/12B01J2229/14B01J35/66
Inventor 范峰凌凤香王少军张会成陈晓刚杨春雁
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com