Novel environment-friendly composite slurry and preparation method thereof

A kind of composite slurry and environment-friendly technology, applied in textiles, papermaking, fiber treatment, etc., can solve the problems of high surface tension, rigidity, poor elasticity, etc., and achieve good adhesion, low cost, and good desizing effect

Inactive Publication Date: 2015-05-13
张劲松
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Sodium alginate slurry is a pseudoplastic fluid with stable viscosity and is not affected by pH. It has the characteristics of low concentration and high viscosity, high surface tension, certain adhesion and film-forming ability, and good biodegradability. Poor elasticity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel environment-friendly composite slurry and preparation method thereof
  • Novel environment-friendly composite slurry and preparation method thereof
  • Novel environment-friendly composite slurry and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A novel environment-friendly composite slurry, in parts by weight, comprises the following components:

[0027] 5 parts of sodium alginate, 8 parts of PVA, 5 parts of polyacrylamide, 1 part of other additives, 20 parts of deionized water.

[0028] Its preparation method comprises the following steps:

[0029] (1) The pulp kettle is cleaned with deionized water, and dried for later use;

[0030] (2) Add 20 parts of deionized water and 5 parts of sodium alginate into the slurry kettle, start the mixer, slowly raise the temperature to 60°C, and stir for 30 minutes at a speed of 500 rpm;

[0031] (3) Add 1 part of other additives, continue to stir, and adjust its pH to 5, cool down to 40°C, slowly add 8 parts of PVA and 5 parts of polyacrylamide, stir while adding, and get a new type of environmentally friendly compound after stirring for 50 minutes. slurry.

Embodiment 2

[0033] A novel environment-friendly composite slurry, in parts by weight, comprises the following components:

[0034] 10 parts of sodium alginate, 15 parts of PVA, 12 parts of polyacrylamide, 5 parts of other additives, 30 parts of deionized water.

[0035] Its preparation method comprises the following steps:

[0036] (1) The pulp kettle is cleaned with deionized water, and dried for later use;

[0037] (2) Add 30 parts of deionized water and 10 parts of sodium alginate into the slurry kettle, start the mixer, slowly raise the temperature to 70°C, and stir for 60 minutes at a speed of 800 rpm;

[0038] (3) Add 5 parts of other additives, continue stirring, adjust the pH to 7, cool down to 50°C, slowly add 15 parts of PVA and 12 parts of polyacrylamide, stir while adding, and get a new type of environmentally friendly compound after stirring for 100 minutes. slurry.

Embodiment 3

[0040] A novel environment-friendly composite slurry, in parts by weight, comprises the following components:

[0041] 6 parts of sodium alginate, 9 parts of PVA, 6 parts of polyacrylamide, 2 parts of other additives, 22 parts of deionized water.

[0042] Its preparation method comprises the following steps:

[0043] (1) The pulp kettle is cleaned with deionized water, and dried for later use;

[0044] (2) Add 22 parts of deionized water and 6 parts of sodium alginate into the slurry kettle, start the mixer, slowly raise the temperature to 62°C, and stir for 35 minutes at a speed of 550 rpm;

[0045] (3) Add 2 parts of other additives, continue to stir, adjust the pH to 6, cool down to 42°C, slowly add 9 parts of PVA and 6 parts of polyacrylamide, stir while adding, and get a new type of environmentally friendly compound after stirring for 55 minutes. slurry.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
degree of polymerizationaaaaaaaaaa
alcoholysis degreeaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
Login to view more

Abstract

The invention discloses novel environment-friendly composite slurry. The novel environment-friendly composite slurry is prepared from the following components in parts by weight: 5-10 parts of sodium alginate, 8-15 parts of PVA, 5-12 parts of polyacrylamide, 1-5 parts of other additives and 20-30 parts of deionized water. The invention further discloses a preparation method of the composite slurry. The composite slurry disclosed by the invention has a good sizing effect, has good stickiness and film-forming property on most fibers, and is good in flexibility, elasticity and wearing resistance, high in mechanical strength, pollution-free, biodegradable, easy to desize, simple in preparation process and low in cost.

Description

Technical field: [0001] The invention relates to the field of textile sizing, in particular to a novel environment-friendly composite size. Background technique: [0002] In order to endow the warp yarn with the ability to resist external mechanical force, improve the weavability of warp yarn, and ensure the smooth progress of the weaving process, a certain amount of size is often adhered to the surface of the sizing yarn, and a size film is formed after drying. [0003] Sodium alginate slurry is a pseudoplastic fluid with stable viscosity and is not affected by pH. It has the characteristics of low concentration and high viscosity, high surface tension, certain adhesion and film-forming ability, and good biodegradability. Poor elasticity. [0004] Polyvinyl alcohol film has the characteristics of high strength, good elasticity, and good wear resistance, and it is biodegradable. Polyacrylamide has good adhesion and film-forming properties, and its mechanical strength is gre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/333D06M15/13D06M15/285
Inventor 沈旭源
Owner 张劲松
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap