Epoxy polyether polyol and production process thereof

An epoxy polyether alcohol and a production process technology, which is applied in the field of plastic toughening agents, can solve the problems of potential harm of polluted groundwater, weak adsorption capacity of surfactants, etc., and achieves inhibition of decomposition, good time-cold resistance, and improved toughness. Effect

Inactive Publication Date: 2015-05-27
FOSHAN XILUN CHEM
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, some surfactants have weak adsorption capacity in the soil and will migr

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0020] Example 1

[0021] The production formula of epoxy polyether alcohol is as follows in parts by weight:

[0022] Catalyst: 2 parts of potassium hydroxide, 100 parts of a mixture of glycerol and polyglycerol, 1076: 0.1 part of antioxidant, 168: 0.15 part of antioxidant.

[0023] The production process of epoxy polyether alcohol is as follows:

[0024] Put 2 grams of potassium oxyoxide, 100 grams of glycerol and polyglycerol mixture, 0.1 grams of antioxidant 1076 and 0.15 grams of antioxidant 168 into the reactor, vacuum to -0.99MPa, and then fill the reactor with nitrogen to 0.2 Kgf / cm 2 , The temperature of the material slowly rises to 245±2℃, and the pressure of the reactor is controlled at 1.0Kgf / cm 2 React for 12 hours; use cooling water to lower the temperature to 205±5°C, vacuum for 2 hours at -0.99MPa, and then lower the temperature to 90°C to discharge the product to obtain the epoxy polyether alcohol product.

[0025] Epoxy polyether alcohol products are used in productio...

Example Embodiment

[0033] Example 2

[0034] The production formula of epoxy polyether alcohol is as follows in parts by weight:

[0035] Catalyst: 2 parts of sodium hydroxide, 102 parts of a mixture of glycerol and polyglycerol, antioxidant DSTP: 0.2 part.

[0036] The production process of epoxy polyether alcohol is as follows:

[0037] Put 2 grams of sodium hydroxide, 102 grams of glycerol and polyglycerol mixture, 0.2 grams of antioxidant DSTP into the reactor, vacuum to -0.99MPa, and then fill the reactor with nitrogen to 0.25Kgf / cm 2 ,The temperature of the material slowly rises to 245±2℃, and the pressure of the reactor is controlled to 1.2Kgf / cm 2 React for 11.5 hours; use cooling water to lower the temperature to 205±5°C, vacuum for 1.8 hours at -0.99MPa, and then lower the temperature to 95°C to discharge the product, and then obtain the epoxy polyether alcohol product.

Example Embodiment

[0038] Example 3

[0039] The production formula of epoxy polyether alcohol is as follows in parts by weight:

[0040] Catalyst: 2.5 parts of sodium carbonate, 100 parts of a mixture of glycerol and polyglycerol, 1010: 0.3 parts of antioxidant.

[0041] The production process of epoxy polyether alcohol is as follows:

[0042] Put 2.5 grams of sodium carbonate, 100 grams of glycerol and polyglycerol mixture, 0.3 grams of antioxidant 1010 into the reactor, vacuum to -0.99MPa, and then fill the reactor with nitrogen to 0.28Kgf / cm 2 ,The temperature of the material slowly rises to 245±2℃, and the pressure of the reactor is controlled to 1.2Kgf / cm 2 React for 12 hours; use cooling water to lower the temperature to 205±5°C, vacuum for 2.2 hours at -0.99MPa, and then lower the temperature to 98°C to discharge, to obtain the epoxy polyether alcohol product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses epoxy polyether polyol and a production process thereof. The epoxy polyether polyol is characterized by comprising the following components in parts by weight: 1-3 parts of a catalyst, 95-105 parts of a mixture of glycerol and polyglycerol, and 0.15-0.4 part of an antioxidant. By adopting epoxy polyether polyol, the toughness of a product can be effectively improved, and decomposition of epoxy polyether polyol macromolecules can be effectively inhibited.

Description

technical field [0001] The invention relates to the technical field of plastic toughening agents, in particular to an epoxy polyether alcohol and a production process thereof. Background technique [0002] Glycerin is a colorless, odorless, sweet, clear thick liquid, chemically named "glycerol". Glycerol is mainly used as a stationary liquid for gas chromatography and organic synthesis, and can also be used as a solvent, shock absorber for gas meters and hydraulic machines, softener, nutrient for antibiotic fermentation, desiccant, etc. In recent years, my country's glycerin industry has developed very rapidly, and subsequently, many by-products discharged from the glycerin industry have caused pollution problems to the environment. The general technology of glycerin by-products is to react with fatty acids to produce surfactants after desalting and decolorization. Surfactants are a class of organic compounds that can reduce surface tension by adding a small amount, so the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08G65/34C08G65/48C07C43/13C07C41/09C07C69/30C07C67/08
Inventor 陆泳辉
Owner FOSHAN XILUN CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products