A high-precision weldless iridium crucible manufacturing method

A manufacturing method and a technology without welds, applied in chemical instruments and methods, crystal growth, post-processing devices, etc., can solve problems such as difficult processing technology

Active Publication Date: 2017-02-22
BEIJING HUAXIA FURUN IND & TRADE
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the manufacturing method, the processing technology is very difficult, and there is no information about the processing method of the high-precision weldless iridium crucible at home and abroad.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0027] Hereinafter, the above-mentioned and other technical features and advantages of the present invention will be described in more detail.

[0028] The process of the high-precision weldless iridium crucible manufacturing method of the present invention comprises:

[0029] Preparation of mould; preparation of spinning tool; preparation of spinning wheel; preparation of top plate; preparation of driving knife; spinning forming process of iridium crucible.

[0030] Each process and principle of the above-mentioned manufacturing of high-precision weldless iridium crucibles is described in detail as follows:

[0031] Step a, the preparation of mold:

[0032] The initial rotation mold is made of YG hard alloy material, processed and ground to the size of the initial rotation mold, the bevel angle is 45°, and the final forming mold is ground to the size and shape of the inner shape of the crucible;

[0033] Step b, preparation of spinning tool:

[0034] (1) Spinning wheel: Th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-precision weldless iridium crucible and a manufacturing method of iridium products, wherein a processing method of sheet spinning formation is used for directly spinning an iridium sheet to form an integrated weldless iridium crucible; and the problem that high precision requirement of iridium crucible and iridium products cannot be reached for reason of casting process and welding process is solved. By the method disclosed by the invention, the high-precision iridium crucible and iridium products with diameter less than 100 mm can be produced; the boundary dimension deviation and thickness deviation can be 0.02 mm.

Description

technical field [0001] The invention relates to the field of iridium crucible manufacturing, in particular to a method for manufacturing a high-precision non-welded iridium crucible. Background technique [0002] Due to the high density of metal iridium (22.56g / cm 3 ), high melting point (2454°C), high temperature resistance, high hardness, high strength and acid and alkali corrosion resistance. Especially with the rapid development of the aerospace industry, the demand for high-precision iridium products is increasing. [0003] At present, the processing methods of iridium crucible mainly include casting method and plastic welding method. The casting method is to heat and melt iridium powder or iridium block through an intermediate frequency induction furnace, and then directly inject iridium solution into a magnesium oxide or graphite mold to cast an iridium crucible. The process is simple, but there are many defects, the most important ones are prone to defects such as ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23P15/00
CPCB23P15/00C30B35/002
Inventor 赵景谦崔长岭
Owner BEIJING HUAXIA FURUN IND & TRADE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com