Medical tooth root post composite material

A composite material and root post technology, used in dentistry, medical science, dental preparations, etc., can solve the problem of high price and achieve the effects of simple operation, strong market competitiveness and wide application range

Inactive Publication Date: 2015-06-10
TIANJIN ZHONGXING TECH
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Moreover, the fiber post can achieve a high bonding strength between the resin adhesive and the root canal dentin, which can prolong the service life of the restoration and reduce the occurrence of root fractures,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Medical tooth root post composite material
  • Medical tooth root post composite material
  • Medical tooth root post composite material

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0020] Example 1

[0021] The composite material of the medical tooth root post has the following composition and mass ratio:

[0022] Component A:

[0023]

[0024] Component B:

[0025] 1 part thermochromic powder;

[0026] 12 parts of 191 unsaturated polyester resin.

[0027] Mix component A:component B according to the mass ratio of 10:3; then put it into the extruder, and extrude it in a stick shape at a temperature of 80-120°C. Cut the package according to the size of the root post.

Example Embodiment

[0028] Example 2:

[0029] The composite material of medical tooth root post of the present invention, its component and mass fraction ratio are as follows:

[0030] Component A:

[0031]

[0032] Component B:

[0033] 2 parts of thermochromic powder;

[0034] 10 parts of unsaturated polyester resin.

[0035] Mix component A:component B according to the mass ratio of 10:3; then put it into the extruder, and extrude it in a stick shape at a temperature of 80-120°C. Cut the package according to the size of the root post.

[0036] Mix component A:component B according to the mass ratio of 10:3; then put it into the extruder, and extrude it in a stick shape at a temperature of 80-120°C. Cut the package according to the size of the root post.

Example Embodiment

[0037] Example 3

[0038] The composite material of medical tooth root post of the present invention, its component and mass fraction ratio are as follows:

[0039] Component A:

[0040]

[0041] Component B:

[0042] 1 part thermochromic powder;

[0043] 8 parts of 196 unsaturated polyester resin.

[0044] Mix component A:component B according to the mass ratio of 10:3; then put it into the extruder, and extrude it in a stick shape at a temperature of 80-120°C. Cut the package according to the size of the root post.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a medical tooth root post composite material. The medical tooth root post composite material comprises unsaturated polyester resin, curing agents, accelerant, quartz fibers and heat discoloration powder. The components are mixed in proportion, placed into an extruder and extruded in a stick-like mode at the temperature ranging from 80 DEG C to 120 DEG C. Cutting and packaging are conducted according to the size of required tooth root posts. The tooth root post composite material fills the blank in China and reaches the international advanced level, and the bending strength of a formed fiber post reaches 600 mpa. The composite material is good in elasticity modulus, light, high in strength, good in color and luster, superior in tooth repair, wide in application range, quick and easy to operate and suitable for repairing a dental crown with large-area missing, the fixing position of a fixed partial denture, detorted teeth, malposed teeth or rotated teeth and the like, has strong market competitiveness and wide market prospects, and the frequency of return visits of a patient is reduced.

Description

technical field [0001] The invention relates to a medical polymer material, in particular to a medical tooth root post composite material. Background technique [0002] We wear braces on the teeth that have been treated. Generally, a post needs to be placed in the root of the tooth, so that it can be stronger after wearing porcelain or other materials. We all know that the post and core are like the foundation of porcelain teeth, and the foundation is very important. Therefore, only by choosing a suitable post and core can a good restoration effect and use effect be achieved. There are many types of post cores, and the materials of the root posts currently used are metal posts and fiber post; the main component of ordinary metal posts is nickel-chromium alloy or cobalt-chromium alloy, which is relatively hard, and the post core itself is very strong, but it is very easy to cause Root splitting, easy to corrode, poor biocompatibility, choose carefully. Silver-palladium allo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A61K6/087A61K6/027A61K6/891
Inventor 阎辉
Owner TIANJIN ZHONGXING TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap