P-10 nonionic/cationic composite asphalt emulsifier

An asphalt emulsifier and asphalt technology, which is applied in building components, building insulation materials, buildings, etc., can solve problems such as difficulty in adapting and meeting different use environments and road construction performance, achieve low adsorption loss, improve interfacial activity and oil. Compatibility, the effect of reducing interfacial tension

Inactive Publication Date: 2015-06-10
QINGDAO HUICHENG PETROCHEM TECH
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Asphalt emulsifier is a kind of surfactant. Its development has experienced the transformation from anionic to cationic and nonionic. It is difficult for a single type of asphalt emulsifier to adapt to different brands of asphalt and different types of mineral materials, and it is difficult to meet different requirements. Use environment and road construction performance needs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Example 1: Preparation of emulsifier aqueous solution: add 2.5g of emulsifier to 100g of hot water at 70-75°C, wait for emulsification

[0021] After the emulsifier is completely dissolved, adjust the pH of the solution to 4.5-5 with concentrated hydrochloric acid to obtain an aqueous emulsifier solution, and keep the solution temperature at 70-75°C.

[0022] Asphalt emulsion preparation: start the colloid mill, first add the emulsifier aqueous solution at 70-75°C to the colloid mill, then add 150g of road petroleum asphalt No. 100 heated to 130-140°C, and a certain amount of additives into the colloid mill, and circulate Grind for 1-2min to obtain asphalt emulsion.

[0023] Weigh 100g of stone, take a certain amount of water and additives, add it to the iron bowl, mix evenly, then weigh a certain amount of emulsified asphalt, pour it into the iron bowl, stir quickly and fully, and start timing, and the record can be mixed time and molding time.

[0024] Emulsificatio...

Embodiment 2

[0030] Example 2: Preparation of emulsifier aqueous solution: add 2.5g of emulsifier to 100g of hot water at 70-75°C, wait for emulsification

[0031] After the emulsifier is completely dissolved, adjust the pH of the solution to 4.5-5 with concentrated hydrochloric acid to obtain an aqueous emulsifier solution, and keep the solution temperature at 70-75°C.

[0032] Asphalt emulsion preparation: start the colloid mill, first add the emulsifier aqueous solution at 70-75°C to the colloid mill, then add 150g of 300AH-90 asphalt heated to 130-140°C, and a certain amount of additives into the colloid mill, and grind for 1 -2min, the asphalt emulsion is obtained.

[0033] Weigh 100g of stone, take a certain amount of water and additives, add it to the iron bowl, mix evenly, then weigh a certain amount of emulsified asphalt, pour it into the iron bowl, stir quickly and fully, and start timing, and the record can be mixed time and molding time.

[0034] Emulsification conditions: 30...

Embodiment 3

[0040] Example 3: Preparation of emulsifier aqueous solution: add 2.5g of emulsifier to 100g of hot water at 70-75°C, wait for emulsification

[0041] After the emulsifier is completely dissolved, adjust the pH of the solution to 4.5-5 with concentrated hydrochloric acid to obtain an aqueous emulsifier solution, and keep the solution temperature at 70-75°C.

[0042] Asphalt emulsion preparation: start the colloid mill, first add the emulsifier aqueous solution at 70-75°C to the colloid mill, then add 150g3 road petroleum asphalt No. 180 heated to 130-140°C, and a certain amount of additives into the colloid mill, and circulate Grind for 1-2min to obtain asphalt emulsion.

[0043] Weigh 100g of stone, take a certain amount of water and additives, add it to the iron bowl, mix evenly, then weigh a certain amount of emulsified asphalt, pour it into the iron bowl, stir quickly and fully, and start timing, and the record can be mixed time and molding time.

[0044] Emulsification co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
critical micelle concentration (mass)aaaaaaaaaa
surface tensionaaaaaaaaaa
Login to view more

Abstract

The invention discloses a nonionic / cationic composite asphalt emulsifier, OP-10 is reacted with epichlorohydrin to obtain a nonionic intermediate, the nonionic intermediate is reacted with alkylamine, and by chemical reaction, the nonionic surfactant is connected with the alkyl amine for synthesis and preparation of the nonionic / cationic composite asphalt emulsifier. The nonionic / cationic composite asphalt emulsifier is a slow cracking type asphalt emulsifier, and has good emulsifying properties and storage stability on different sources of asphalt and under different pH, and asphalt emulsion performance can reach technical requirements of emulsified asphalt used in roads in technical specification JTG F40-2004 for construction of highway asphalt pavements.

Description

technical field [0001] The invention relates to the synthesis of organic chemical products and their practical application in the field of asphalt road pouring, belonging to the fields of fine chemicals and building materials. Background technique [0002] Asphalt has the characteristics of water and moisture resistance, toughness, wear resistance, etc., and is widely used in the field of road construction. At room temperature, asphalt has poor fluidity and high viscosity, so it cannot be crushed to mix it evenly with aggregate. Traditional asphalt and aggregate mixing methods include solvent method and high-temperature melting method. The solvent method consumes a large amount of organic solvents, and the high-temperature melting method consumes a lot of energy. Both methods pollute the air. The emulsified asphalt technology solves this problem better. question. Environmental decontamination, improve construction conditions. When traditional hot asphalt is heated, a larg...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08J3/03C08L95/00C08G65/333C04B26/26
Inventor 洪龙峰
Owner QINGDAO HUICHENG PETROCHEM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap