Waterborne acrylic modified saturated polyester resin

A water-based acrylic and polyester resin technology, used in polyester coatings, coatings, etc., can solve the problems of high VOC content, easy hydrolysis, low construction solid content, etc., to improve hydrolysis resistance, excellent water resistance, flexibility Good results

Inactive Publication Date: 2015-07-08
BEIJING JINHWEILI APPLIED CHEM PROD +1
View PDF4 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current water-based saturated polyester resin products have the defects of low solid content in construction, easy hydrolysis, and high VOC content.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waterborne acrylic modified saturated polyester resin
  • Waterborne acrylic modified saturated polyester resin
  • Waterborne acrylic modified saturated polyester resin

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0032] The present invention will be further described below in conjunction with the accompanying drawings and specific embodiments. The principles and features of the present invention are described below, and the examples given are only used to explain the present invention, and are not intended to limit the scope of the present invention.

[0033] The specific implementation steps are as follows:

[0034] 1) Put polybasic acid, E10P, and polyalcohol into a 1L reaction flask equipped with a stirring device, a reflux condensing device, a dropping device and a temperature control device, feed in nitrogen, slowly heat to 190°C, keep it warm for 1 hour, and slowly raise the temperature to 250°C, keep warm for 6 hours, add 3% xylene in this step and reflux until the acid value is less than 20mgKOH / g, and control the temperature of the distillation head during the reaction to be less than 100°C;

[0035] 2) Cool down to 110°C and add co-solvent;

[0036] 3) Add a mixture of acry...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention relates to an aqueous acrylic acid modified saturated polyester resin, comprising the following materials of parts by weight: 5-25 parts of a polyacid, 15-40 parts of a polyol, 1-3 parts of a solubilizing agent, 5-20 parts of an acrylic acid monomer I, 0.5-10 parts of acrylic acid monomer II, 0.01-8 parts of an initiator, 0.5-10 parts of a neutralizer, 2-20 parts of glycidyl ester tertcarbonate, and 40-50 parts of deionized water. The aqueous acrylic acid modified saturated polyester resin prepared in the present invention has excellent stability, high solid-ness, low viscosity, and low VOC content, and can be mainly used for amino baked-on coating for aqueous coatings.

Description

technical field [0001] The invention relates to a water-based acrylic modified saturated polyester resin, which belongs to the field of water-based coatings. Background technique [0002] Water-based coatings are more and more widely used as low-VOC content coatings. However, because of the low solid content of water-based coatings, it is difficult to achieve the high decorative effect of the soluble type. As the film-forming substance of water-based paint, water-based resin, the solid content, viscosity and VOC content of its aqueous dispersion play a decisive role in the performance of the paint film and the impact on the environment. Saturated polyester has high gloss, high fullness, and excellent weather resistance, and is used in medium and high-grade amino baking varnishes and polyurethane topcoats. However, the current water-based saturated polyester resin products have the defects of low solid content in construction, easy hydrolysis, and high VOC content. Conten...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08F283/01C08F283/02C08F220/14C08F220/18C08F220/28C08F220/06C08G63/64C09D151/08
CPCC09D151/08C09D167/06C08F220/28C08F283/02C08F220/20C08F220/1804C08F220/1808C08F220/1811
Inventor 陈明秦文王英
Owner BEIJING JINHWEILI APPLIED CHEM PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap