Preparation method of waterborne polyurethane coating and adhesive modified by graphene and rare earth
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A water-based polyurethane and rare earth modification technology, used in polyurea/polyurethane coatings, adhesives, fire-retardant coatings, etc.
Inactive Publication Date: 2015-07-22
段宝荣
View PDF2 Cites 11 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
In the field of flame retardants, there is no precedent for the application of rare earth elements. How to combine rare earth elements and halogen-free flame retardants to meet the requirements of low toxicity, low smoke and harmlessness while taking into account the flame retardant effect is an update. research direction
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
specific Embodiment approach
[0021] detailed description Below in conjunction with example further illustrate the present invention.
example 1
[0023] (1) In a 500ml four-necked flask equipped with a stirring blade, a thermometer, and a condenser tube, add 92g of tetrakis hydroxymethylphosphorus sulfate and 44g of aqueous sodium hydroxide solution with a mass fraction of 20%, react at 80°C for 2h, and then Add 272 g of ytterbium chloride aqueous solution and 2 g of pentoxyverine with a mass fraction of 20%, adjust the pH value of the solution to 7-8 with a mass fraction of 20% sodium hydroxide solution, stir at 20° C. for 3 h, and after the reaction, Filtration, drying, and crushing to more than 3000 meshes, 96.2g of ytterbium phosphorus flame retardant can be obtained;
[0024] (2) Put 60g of the above-mentioned (1) ytterbium phosphorus flame retardant and 30g of hexamethylene diisocyanate into a 500ml four-neck flask equipped with a stirring blade, a thermometer, and a condenser tube. Under the conditions, react at 70°C for 2 hours, then add 0.1 g of sodium glucoheptonate, and react at 70°C for 30 minutes to obtain ...
example 2
[0029] (1) In a 500ml four-necked flask equipped with a stirring blade, a thermometer, and a condenser tube, add 92g of tetrakis hydroxymethyl phosphorus sulfate and 44g of aqueous sodium hydroxide solution with a mass fraction of 20%, react at 80°C for 2h, and then Add 272g of 20% ytterbium chloride aqueous solution and 2g of pentoxyverine, then use 20% sodium hydroxide to adjust the pH value of the solution to 7-8, stir at 30°C for 3h, and filter after the reaction , dried, crushed to more than 3000 mesh, 96.2g of ytterbium phosphorus flame retardant can be obtained;
[0030] (2) Put 60g of the above-mentioned (1) ytterbium phosphorus flame retardant and 15g of hexamethylene diisocyanate into a 500ml four-neck flask with a stirring blade, a thermometer, and a condenser tube, and put them in the presence of 0.53g of dibutyltin dilaurate Under the conditions, react at 90°C for 3 hours, then add 0.15 g of sodium glucoheptonate, and react at 90°C for 30 minutes to obtain 75.1 g ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a preparation method of waterborne polyurethane coating and adhesive which are modified by graphene and rare earth. The preparation method of the waterborne polyurethane coating and adhesive which are modified by graphene and rare earth comprises the following steps: in presence of a dibutyltin dilaurate catalyst, mixing a ytterbium phosphorus flame retardant with hexamethylene diisocyanate, carrying out reaction for 2-3 hours at the temperature of 70-90 DEG C, adding sodium glucoheptonate, and carrying out reaction for 30 minutes at the temperature of 70-90 DEG C, so that a polyurethane prepolymer is obtained; adding a hydrophilic chain extender and butanone into the polyurethane prepolymer, carrying out reaction for 1-3 hours at the temperature of 70-80 DEG C, adding triethylamine for carrying out reaction for 30-60 minutes, and adding water for emulsifying, so that hydrophilic polyurethane is formed; adding a graphene dispersion liquid and phospholipid into the hydrophilic polyurethane, and shearing and stirring for 60-90 minutes under the condition that pH value is 7, so that the waterborne polyurethane coating and adhesive which are modified by graphene and rare earth are obtained, and fire resistance and mechanical properties of the obtained polyurethane coating and adhesive are greatly improved.
Description
[0001] Technical field The present invention relates to a preparation method of water-based polyurethane coating and adhesive, in particular to a preparation method of graphene and rare earth modified water-based polyurethane coating and adhesive, the main purpose of which is to improve the flame retardancy of water-based polyurethane . Background technique [0002] Water-based polyurethane (also known as water-based polyurethane) is a polyurethane resin containing hydrophilic groups in the molecular chain of polyurethane, which has a strong affinity with water. It can be dispersed in water and formed by using a specific process. stable system. Water-based polyurethane is mainly used in leather finishing, textile printing and dyeing, papermaking, architectural coatings, adhesives, etc. Almost all of the materials involved are flammable materials. If these materials are not treated with flame retardant, they will inevitably become a fire hazard. . The flame retardancy of wate...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.