High-fluidity fiber reinforced PPS/ABS composite material and product thereof

A high fluidity, composite material technology, applied in the field of polymer materials, can solve the problems of poor toughness, impact resistance, low elongation at break, poor impact resistance, etc., and achieve low warpage, high mechanical strength, and high flow sexual effect

Inactive Publication Date: 2015-09-02
MITAC PRECISION TECH(KUNSHAN) CORP
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At the same time, because there are a large number of benzene rings in the main chain of PPS, and the degree of crystallinity is very high, its elongation at break is low, and its toughness and impact resistance are also poor, which limits its application to a certain extent.
[0004] In view of this, it is necessary to develop a PPS / ABS composite material and its products to solve the problems of poor fluidity, low elongation at break and poor impact resistance of the current PPS / ABS composite material.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-fluidity fiber reinforced PPS/ABS composite material and product thereof
  • High-fluidity fiber reinforced PPS/ABS composite material and product thereof
  • High-fluidity fiber reinforced PPS/ABS composite material and product thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029]

[0030] Dry the PPS polymer and ABS resin in an oven with dehumidification dryer respectively; weigh the dried PPS polymer and ABS resin and mix them; weigh the compatibilizer and other additives, and then add them to the high-speed mixer at high speed Premixing: adding the mixture in the above steps, the weighed flat cross-section glass fibers and hollow glass microspheres to a twin-screw extruder for melt extrusion and granulation.

Embodiment 2

[0032]

[0033] Dry the PPS polymer and ABS resin in an oven with dehumidification dryer respectively; weigh the dried PPS polymer and ABS resin and mix them; weigh the compatibilizer and other additives, and then add them to the high-speed mixer at high speed Premixing: adding the mixture in the above steps, the weighed flat cross-section glass fibers and hollow glass microspheres to a twin-screw extruder for melt extrusion and granulation.

[0034] Example 1:

[0035]

[0036] Dry the PPS polymer and ABS resin in an oven with dehumidification dryer respectively; weigh the dried PPS polymer and ABS resin and mix them; weigh the compatibilizer and other additives, and then add them to the high-speed mixer at high speed Premixing: adding the mixture in the above steps, the weighed flat cross-section glass fibers and hollow glass microspheres to a twin-screw extruder for melt extrusion and granulation.

Embodiment 3

[0038]

[0039] Dry the PPS polymer and ABS resin in an oven with dehumidification dryer respectively; weigh the dried PPS polymer and ABS resin and mix them; weigh the compatibilizer and other additives, and then add them to the high-speed mixer at high speed Premixing: adding the mixture in the above steps, the weighed flat cross-section glass fibers and hollow glass microspheres to a twin-screw extruder for melt extrusion and granulation.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-fluidity fiber reinforced PPS / ABS composite material and a product thereof. The composite material comprises: by weight, thermoplastic resin comprising 35-50 parts of PPS polymer and 0.1-10 parts of ABS resin; a reinforcing filling material comprising 40-60 parts of flat section glass fiber and 0.5-2 parts of a granular glass filling material; and 0.5-2 parts of a compatilizer. The PPS resin reinforced by the flat section glass fiber and the fibrous filling material except the flat section glass fiber is adopted as a substrate, the ABS resin and hollow glass beads are added, and the compatibilization effect of the added ABS resin with the compatilizer is used to increase the fluidity, the elongation at break and the impact strength, and a reinforced composite resin composition with high mechanical strength, high fluidity and low warp is formed.

Description

【Technical field】 [0001] The invention belongs to the technical field of polymer materials, and in particular relates to a high fluidity fiber reinforced PPS / ABS composite material and its products. 【Background technique】 [0002] Polyphenylene sulfide (PPS) is also known as polyphenylene sulfide and poly(sub)phenylene sulfide. PPS is a lightweight, high-performance material I1 developed by Philips Petroleum Company in 1967, industrialized production began in the 1970s, and put on the market under the trade name "Ryton"; it is following polyamide (PA), polyoxymethylene (POM ), polycarbonate (PC), modified polyphenylene oxide (MPPO), polybutylene methacrylate (PBT), and is recognized as the sixth largest engineering plastic. As the matrix of high-performance resin-based composite materials, PPS is receiving more and more attention in the application of electronics, automobiles, precision machinery, aerospace and military equipment. [0003] The chain link structural unit of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L81/02C08L55/02C08L83/04C08L33/08C08L31/04C08L51/00C08L51/06C08K7/14C08K9/00C08K7/20C08K7/28C08J5/04
CPCC08L81/02C08J5/043C08K2201/014
Inventor 陈冠华
Owner MITAC PRECISION TECH(KUNSHAN) CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com