One-section type composite material vehicle transmission shaft preparation method

A technology of composite materials and composite material tubes, which is applied in the field of preparation of one-piece composite material automobile transmission shafts, can solve the problems of impossible batch production, poor bending stiffness, poor bending and torsional fatigue resistance, and complicated preparation methods , to achieve the effects of good fatigue, high static torsional strength and high natural frequency

Active Publication Date: 2015-10-21
SHANGHAI HUAYU NEW MATERIAL TECH CO LTD
View PDF6 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It has been reported that composite pipes with slub structure reinforcement are prepared by using plaster molds, and the bending stiffness, bending resist

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • One-section type composite material vehicle transmission shaft preparation method
  • One-section type composite material vehicle transmission shaft preparation method
  • One-section type composite material vehicle transmission shaft preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] The preparation method of a one-stage composite material automobile drive shaft of the present invention comprises an aluminum alloy cross joint 1 and an aluminum alloy spherical cage type universal joint 3 respectively connected to both ends of a composite material pipe having internal threads, the aluminum alloy The cross universal joint is connected with the automobile power system, and the aluminum alloy ball cage type universal joint is connected with the rear axle system in the form of a flange, and the preparation method includes the following steps:

[0039] 1) Preparation of composite material pipe 2 with internal thread:

[0040] a. First impregnate the glass fiber with epoxy resin to form a glass fiber prepreg. The thickness of the prepreg is 0.02mm, and then wind the glass fiber prepreg onto the external thread mold, such as image 3 As shown, the externally threaded mold is a stud with a helical groove, and the depth of the groove is 1mm. First, the glass f...

Embodiment 2

[0048] The preparation method of a one-stage composite material automobile drive shaft of the present invention comprises a magnesium alloy cross joint 1 and a magnesium alloy cage type universal joint 3 respectively connected to both ends of a composite material pipe having an internal thread, the magnesium alloy The cross universal joint is connected with the automobile power system, and the magnesium alloy ball cage type universal joint is connected with the rear axle system in the form of a flange. The preparation method includes the following steps:

[0049] 1) Preparation of composite material pipe 2 with internal thread:

[0050] a. First, soak the aramid fiber in bismaleimide resin to form an aramid fiber prepreg. The thickness of the aramid fiber prepreg is 1mm, and then wrap the aramid fiber prepreg on the external thread mold, such as image 3 As shown, the external thread mold is a stud with a helical screw groove, the depth of the screw groove is 2mm. First, the a...

Embodiment 3

[0058] The preparation method of a one-stage composite material automobile drive shaft of the present invention comprises a titanium alloy cross joint 1 and a titanium alloy cage type universal joint 3 respectively connected to both ends of a composite material pipe having an internal thread, and the titanium alloy The cross universal joint is connected with the automobile power system, and the titanium alloy ball cage type universal joint is connected with the rear axle system in the form of a flange, and the preparation method includes the following steps:

[0059] 1) Preparation of composite material pipe 2 with internal thread:

[0060] a. First, soak the carbon fiber in bismaleimide resin to form a carbon fiber prepreg. The thickness of the carbon fiber prepreg is 0.1mm, and then wind the carbon fiber prepreg onto the external thread mold, such as image 3 As shown, the externally threaded mold is a stud with a helical screw groove, and the depth of the screw groove is 1m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thread widthaaaaaaaaaa
Thread widthaaaaaaaaaa
Thread widthaaaaaaaaaa
Login to view more

Abstract

The present invention discloses a one-section type composite material vehicle transmission shaft preparation method, wherein the vehicle transmission shaft comprises a cross type universal joint and a cage type universal joint, the cross type universal joint and the cage type universal joint are respectively connected with both ends of a composite material pipe having inner threads, the cross type universal joint is connected with a vehicle power system, the cage type universal joint is connected with a rear bridge system by using a flange form, the composite material pipe is prepared through an outer thread mold provided with a spiral groove, and the cross type universal joint and the cage type universal joint are connected on both ends of the composite material pipe to prepare the vehicle transmission shaft. According to the present invention, the advantage that the natural frequency of the composite material-made transmission shaft is higher than the natural frequency of the steel-made transmission shaft is completely provided, and the composite material transmission shaft has characteristics of extremely high fatigue resistance, extremely high static torsional strength and the like, can meet the requirements of the vehicles on the transmission shaft length and angle changing during the movement process, and can be applied in passenger vehicles, trucks, commercial vehicles, sport utility vehicles, and other fore-laying rear-drive vehicles.

Description

technical field [0001] The invention belongs to the field of composite materials, and relates to a method for preparing a one-piece composite material automobile transmission shaft. Background technique [0002] Composite pipe fittings are commonly used structural parts in engineering. The pipe-shaped products are characterized by being hollow, continuously closed in the circumferential direction, having a certain length in the axial direction, and having high mechanical properties in the axial and circumferential directions. Tension and compression, bending and torsion have high structural efficiency and are one of the common forms of structural parts in various structures. Common tubular products include transmission shafts in aircraft, vehicles, machinery, tail cones on aircraft / helicopters, missile barrels / head cones / tail nozzles, special-shaped cross-section tubes and tubes for propellers / rotors / fan blade skins Type pressure vessels, tubular stress members commonly use...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B29C70/34B29C70/54B29B15/14
Inventor 余许多林江滨许群
Owner SHANGHAI HUAYU NEW MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap