Zircon aluminum silicate glass and preparation method thereof

A zirconium aluminosilicate and glass technology, applied in glass manufacturing equipment, glass tempering, manufacturing tools, etc., can solve the problems of application limitation, reduce the life of furnace refractory materials, and high energy consumption, and achieve less bubble defects, The best clarifying effect and the effect of low melting temperature

Active Publication Date: 2015-10-21
QINGYUAN CSG NEW ENERGY SAVING MATERIALS CO LTD
View PDF2 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These substances are restricted by the Directive on the Restriction of the Use of Certain Hazardous Components in Electrical and Electronic Equipment (ROHS) and the Registration, Evaluation, Authorization and Restriction of Chemicals (Reach), which makes them widely used in the

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Zircon aluminum silicate glass and preparation method thereof
  • Zircon aluminum silicate glass and preparation method thereof
  • Zircon aluminum silicate glass and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0048] The above-mentioned zirconium aluminosilicate glass is prepared by a float process. see figure 1 , the preparation method of the above-mentioned zirconium aluminosilicate glass comprises the following steps:

[0049] Step S110: Quartz sand, Na 2 CO3 , CaCO 3 、KNO 3 、K 2 CO 3 、NaNO 3 , MgO, Al 2 o 3 , CeO 2 , SnO 2 , zircon sand, TiO 2 Mix with glass clarifier to obtain a mixture, keep the mixture at 1400℃~1520℃ for 1 hour to melt the mixture, wherein the glass clarifier includes NH 4 NO 3 、Na 2 SO 4 , CeO 2 and SnO 2 .

[0050] The ratio of the above raw materials makes the final zirconium aluminosilicate glass include the following components in terms of mass percentage: SiO 2 55.0~68.0%; Al 2 o 3 5.0~20.0%; CaO 0~5.0%; MgO 0~10.0%; K 2 O1.0~8.0%; Na 2 O 10.0~17.0%; CeO 2 0.01~2.0%;TiO 2 0.001~2.0%; ZrO 2 0.3~3.0%; SnO 2 0.01~1.5% and Fe 2 o 3 0.010-0.012%. Among them, K 2 O and Na 2 The total mass percentage of O is 12.0-20.0%, and K 2 ...

Embodiment 1

[0069] 1. Quartz sand, Na 2 CO 3 、KNO 3 、K 2 CO 3 、NaNO 3 , MgO, Al 2 o 3 , CeO 2 , SnO 2 , zircon sand, TiO 2 Mix with a glass clarifier to obtain a mixture, place the mixture in an electric furnace, and keep it warm at 1500°C for 1 hour to melt the mixture, wherein the glass clarifier includes NH 4 NO 3 、Na 2 SO 4 , CeO 2 and SnO 2 ;

[0070] 2. Heat up the melted mixture to 1605°C for clarification for 2 hours to obtain molten glass;

[0071] 3. The molten glass is formed by the float method to obtain zirconium aluminosilicate glass. The components of the zirconium aluminosilicate glass are shown in Table 1;

[0072] 4. Heat the zirconium aluminosilicate glass at 300°C for 30 minutes, then place it in a potassium nitrate melt at 420°C for 6 hours, and finally cool it down to 100°C at a rate of 5°C / min, and Heat preservation at 100° C. for 30 minutes to obtain tempered zirconium aluminosilicate glass.

Embodiment 2

[0074] 1. Quartz sand, Na 2 CO 3 、KNO 3 、K 2 CO 3 、NaNO 3 , MgO, Al 2 o 3 , CeO 2 , SnO 2 , zircon sand, TiO 2 Mix with a glass clarifier to obtain a mixture, place the mixture in an electric furnace, and keep it warm at 1510°C for 1 hour to melt the mixture, wherein the glass clarifier includes NH 4 NO 3 、Na 2 SO 4 , CeO 2 and SnO 2 ;

[0075] 2. Heat the melted mixture to 1615°C for clarification for 2 hours to obtain molten glass;

[0076] 3. The molten glass is formed by the float method to obtain zirconium aluminosilicate glass. The components of the zirconium aluminosilicate glass are shown in Table 1;

[0077] 4. Heat the zirconium aluminosilicate glass at 300°C for 30 minutes, then place it in a potassium nitrate melt at 420°C for 6 hours, and finally cool it down to 100°C at a rate of 5°C / min, and Heat preservation at 100° C. for 30 minutes to obtain tempered zirconium aluminosilicate glass.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to zircon aluminum silicate glass and a preparation method thereof. The zircon aluminum silicate glass comprises, by mass percentage, 55.0-68.0% of SiO2, 5.0-20.0% of Al2O3, 0-5.0% of CaO, 0-10.0% of MgO, 1.0-8.0% of K2O, 10.0-17.0% of Na2O, 0.01-2.0% of CeO, 0.001-2.0% of TiO2, 0.3-3% of ZrO, 0.01-1.5% of SnO2 and 0.010-0.012% of Fe2O3, wherein the total mass percentage of the K2O and the Na2O is 12.0-20.0%, and the weight ratio of the K2O to the Na2O meets 0.03< K2O/ Na2O<0.75; the total mass percentage of the CaO and the MgO is less than or equal to 12.0%. The zircon aluminum silicate glass has the advantages that no toxic and harmful substance exists, the fusion and the clarification temperatures are low, and bubble defects are less.

Description

technical field [0001] The invention relates to the technical field of glass, in particular to a zirconium aluminosilicate glass and a preparation method thereof. Background technique [0002] Zirconium aluminosilicate glass is widely used as protective glass in touch screens, cash machines, self-service printing terminal equipment and 3D TVs. It can also be used in safety glass for windshields of vehicles such as aviation equipment and high-speed rail locomotives. It has high mechanical strength. , wear resistance, impact resistance, good chemical stability and other characteristics, can effectively prevent the impact and scratch damage of the product surface, prolong the service life of the product and enhance the use effect. [0003] The preparation of current zirconium aluminosilicate glasses mostly involves the use of As 2 o 3 , Sb 2 o 3 , Cl 2 or F 2 As a clarifying agent for glass to remove air bubbles in the glass as much as possible. But this clarifying agent...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C3/095C03C1/00C03B18/00C03B27/03
Inventor 王明忠陶武刚陈自发陈志鸿王杏娟
Owner QINGYUAN CSG NEW ENERGY SAVING MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap