Sisal hemp fiber and polypropylene fiber mixture interior ornament material of vehicle

A polypropylene fiber, sisal fiber technology, applied in textiles, papermaking, non-woven fabrics and other directions, can solve the problems of unsatisfactory tensile and impact strength, environmental pollution of interior materials, poor heat resistance, etc. The tensile strength and sound absorption and heat insulation effect are good, the cost is favorable for environmental protection, and the cost is low.

Inactive Publication Date: 2015-10-21
湖北南泽汽车复合材料有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This type of interior material has many defects such as poor heat resistance, unsatisfactory tensile and impact strength during use.
Moreover, synthetic polymer materials such as polystyrene and polyvinyl chloride are difficult to degrade in nature, and discarded interior materials are bound to bring environmental pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Step 1, sisal hemp is cut into the hemp fiber of 5cm;

[0024] Step 2, put the cut hemp fiber into a stainless steel container, mix it with sodium hydroxide solution, soak and stir for 1 hour to make the hemp fiber full, the sodium hydroxide solution is formed by mixing clear water with 99% pure sodium hydroxide, The mixing ratio is 8kg of sodium hydroxide per 100Kg of water;

[0025] Step 3, taking out the hemp fiber after the above-mentioned agitation treatment, washing it with clear water, removing the sodium hydroxide, and then putting it into hot water at 30° C. to remove the residual sodium hydroxide through a constant temperature bath;

[0026] Step 4, the hemp fiber obtained in step 3 is processed by oven drying;

[0027] Step 5, the hemp fiber after the drying of step 4 adopts every 100Kg clear water to be blended into 0.5% methyl methacrylate and 0.05% enammonium nitrate mixed solution to carry out soaking reaction;

[0028] Step 6, drying the hemp fiber aft...

Embodiment 2

[0039] Step 1, sisal hemp is cut into the hemp fiber of 6cm;

[0040] Step 2, put the cut hemp fiber into a stainless steel container, mix it with sodium hydroxide solution, soak and stir for 1 hour to make the hemp fiber full, the sodium hydroxide solution is formed by mixing clear water with 99% pure sodium hydroxide, The mixing ratio is 9kg of sodium hydroxide per 100Kg of water;

[0041] Step 3, taking out the hemp fiber after the above-mentioned agitation treatment, washing it with clear water, removing the sodium hydroxide, and then putting it into hot water at 45° C. to remove the residual sodium hydroxide through a constant temperature bath;

[0042] Step 4, the hemp fiber obtained in step 3 is processed by oven drying;

[0043] Step 5, the hemp fiber after step 4 drying adopts every 100Kg clear water to be blended into 0.7% methyl methacrylate and 0.07% enammonium nitrate mixed solution to carry out soaking reaction;

[0044] Step 6, drying the hemp fiber after the ...

Embodiment 3

[0055] Step 1, sisal hemp is cut into the hemp fiber of 7cm;

[0056] Step 2, put the cut hemp fiber into a stainless steel container, mix it with sodium hydroxide solution, soak and stir for 1 hour to make the hemp fiber full, the sodium hydroxide solution is formed by mixing clear water with 99% pure sodium hydroxide, The mixing ratio is 10kg of sodium hydroxide per 100Kg of water;

[0057] Step 3, taking out the hemp fiber after the above-mentioned agitation treatment, washing it with clear water, removing the sodium hydroxide, and then putting it into hot water at 60 ° C to remove the residual sodium hydroxide through a constant temperature bath;

[0058] Step 4, the hemp fiber obtained in step 3 is processed by oven drying;

[0059] Step 5, the hemp fiber after step 4 drying adopts every 100Kg clear water to be blended into 1% methyl methacrylate and 0.1% enammonium nitrate mixed solution to carry out soaking reaction;

[0060] Step 6, drying the hemp fiber after the ab...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a sisal hemp fiber and polypropylene fiber mixture interior ornament material of a vehicle. First, Sisal hemp is cut into sisal hemp fiber with 5 to 7 cm; second, the sisal hemp fiber is put into a stainless steel container and is mixed with sodium hydroxide solution to soak and stir for 1 hour; third, the sisal hemp fiber is cleaned with clear water for removing sodium hydroxide and then the sisal hemp fiber is put into hot water with 30 to 60 temperature so as to removing residual sodium hydroxide with constant temperature bath; fourth, the sisal hemp fiber is dried by a dryer; fifth, mixed liquid of methyl methacrylate of 0.5 to 1 percent blended with clear water every 100kg and nitric acid ene ammonium of 0.5 to 0.1 percent is used to soak for reaction; sixth, the sisal hemp fiber is dried after being cleaned with clear water; seventh, the sisal hemp fiber and polypropylene fiber are put on a wool comber for opening mixture; the sisal hemp fiber is within the range of 60 to 70 percent and the polypropylene fiber is within the range of 30 to 40 percent; eighth, the sisal hemp fiber and the polypropylene fiber mixture is carded to be a net by a carding machine; ninth, the sisal hemp fiber and the polypropylene fiber mixture is spread to be mixture material with 1500 g per square meter by a parallel net-spread machine; and tenth, the mixture material is molded into an interior ornament type part by a mould-pressing molding machine.

Description

technical field [0001] The invention relates to an automobile interior material, in particular to an automobile interior material mixed with sisal fiber and polypropylene fiber. Background technique [0002] Automotive interior moldings are usually made of polystyrene, polyvinyl chloride and other materials. This type of interior material has many defects such as poor heat resistance, unsatisfactory tensile and impact strength during use. Moreover, synthetic polymer materials such as polystyrene and polyvinyl chloride are difficult to degrade in nature, and discarded interior materials are bound to bring environmental pollution. Contents of the invention [0003] The object of the present invention is to provide an automobile interior material mixed with sisal fiber and polypropylene fiber, which has the characteristics of good stability, strong impact resistance, and environmental friendliness. [0004] The present invention comprises that the mixed material is mold...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D04H1/541D04H1/544
Inventor 周兴平解孝林朱谦朱邦国
Owner 湖北南泽汽车复合材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com