Novel black metal antirust agent and preparation method thereof

A technology of ferrous metal and antirust agent, which is applied in the field of new ferrous metal antirust agent and its preparation, which can solve the problems of large oil consumption, oily waste liquid discharge, manpower and material resources, etc., to improve utilization rate and antirust performance Strong, saving production and processing costs

Inactive Publication Date: 2015-11-11
江门市三清环境技术工程有限公司
2 Cites 4 Cited by

AI-Extracted Technical Summary

Problems solved by technology

However, the use of anti-rust oil not only consumes a large amount of oil raw materials, but also requires removal of anti-rust oil during subsequent metal processing (such as electroplating, painting, welding, a...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Method used

As can be seen from Table 1-3, iron and steel workpiece is soaked in antirust agent, observes antirust effect after depositing 10 days, 30 days, and antirust effect is excellent, and large piece of rust and pitting do not app...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Abstract

The invention relates to a novel black metal antirust agent and a preparation method thereof. The metal antirust agent comprises, by weight, 2%-10% of sodium nitrite, 5%-15% of sodium silicate, 1%-5% of sodium tripolyphosphate, 5%-10% of benzotriazole, 8%-15% of triethanolamine oleate, 1%-8% of cyclohexylamine carbonate, 5%-15% of urotropine and 30%-70% of deionized water. The black metal antirust agent is excellent in performance, high in anti-rust property, low in cost, convenient to operate, capable of not damaging the original color and luster of the surface of a machine part, and high in rust preventing and membrane forming speed, thereby being an effect optimum product for medium-short-term rust prevention.

Technology Topic

Image

  • Novel black metal antirust agent and preparation method thereof
  • Novel black metal antirust agent and preparation method thereof
  • Novel black metal antirust agent and preparation method thereof

Examples

  • Experimental program(4)
  • Effect test(1)

Example Embodiment

[0025] Example 1
[0026] A new type of ferrous metal rust inhibitor, including the following components by weight ratio:
[0027]
[0028] The preparation method of the novel ferrous metal antirust agent includes the following steps:
[0029] (1) Add deionized water into a stainless steel reaction tank and heat it to 45°C;
[0030] (2) Add sodium nitrite, sodium silicate, and triethanolamine oleate into a stainless steel reaction tank, and stir for 15 minutes to dissolve;
[0031] (3) Add sodium tripolyphosphate, benzotriazole, cyclohexylamine carbonate and urotropine into the reaction tank in sequence;
[0032] (4) After fully stirring for 1 hour, the tank can be discharged.

Example Embodiment

[0033] Example 2
[0034] A new type of ferrous metal rust inhibitor, which is characterized in that it comprises the following components in weight ratio:
[0035]
[0036] The preparation method of ferrous metal antirust agent is characterized in that it comprises the following steps:
[0037] (1) Add deionized water into a stainless steel reaction tank and heat it to 40°C;
[0038] (2) Add sodium nitrite, sodium silicate, and triethanolamine oleate into a stainless steel reaction tank, and stir for 15 minutes to dissolve;
[0039] (3) Add sodium tripolyphosphate, benzotriazole, cyclohexylamine carbonate and urotropine into the reaction tank in sequence;
[0040] (4) After fully stirring for 1 hour, the tank can be discharged.

Example Embodiment

[0041] Example 3
[0042] A new type of ferrous metal rust inhibitor, which is characterized in that it comprises the following components in weight ratio:
[0043]
[0044] The preparation method of ferrous metal antirust agent is characterized in that it comprises the following steps:
[0045] (1) Add deionized water into a stainless steel reaction tank and heat it to 50°C;
[0046] (2) Add sodium nitrite, sodium silicate, and triethanolamine oleate into a stainless steel reaction tank, and stir for 15 minutes to dissolve;
[0047] (3) Add sodium tripolyphosphate, benzotriazole, cyclohexylamine carbonate and urotropine into the reaction tank in sequence;
[0048] (4) After fully stirring for 1 hour, the tank can be discharged.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

no PUM

Description & Claims & Application Information

We can also present the details of the Description, Claims and Application information to help users get a comprehensive understanding of the technical details of the patent, such as background art, summary of invention, brief description of drawings, description of embodiments, and other original content. On the other hand, users can also determine the specific scope of protection of the technology through the list of claims; as well as understand the changes in the life cycle of the technology with the presentation of the patent timeline. Login to view more.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Similar technology patents

Film-removing paint for building template and its preparing method and use

InactiveCN1667104AStrong rust resistanceImprove adhesionAdditivesForm treatmentSolventSteel quality
Owner:北京信邦通达科技有限公司

Countersunk head cross-shaped self-drilling screw and preparation technology thereof

InactiveCN108561396AStrong rust resistanceStrong enoughBoltsScrewsCorrosion resistantWork performance
Owner:江苏固德建筑机械有限公司

Classification and recommendation of technical efficacy words

  • Strong rust resistance
  • Good anti-rust effect

Film-removing paint for building template and its preparing method and use

InactiveCN1667104AStrong rust resistanceImprove adhesionAdditivesForm treatmentSolventSteel quality
Owner:北京信邦通达科技有限公司

Countersunk head cross-shaped self-drilling screw and preparation technology thereof

InactiveCN108561396AStrong rust resistanceStrong enoughBoltsScrewsCorrosion resistantWork performance
Owner:江苏固德建筑机械有限公司

Antirust oil and preparation method thereof

InactiveCN107653045AFast workGood anti-rust effectLubricant compositionCo solventAntioxidant
Owner:上海有道新能源技术有限公司 +1

Aqueous antirust agent

InactiveCN103556157AGood anti-rust effectLong anti-rust periodOXALIC ACID DIHYDRATETriazole
Owner:珠海市金宜科环保材料有限公司

Rust-proof water-based cutting fluid

InactiveCN105567407AGood cooling and lubricating propertiesGood anti-rust effectLubricant compositionChemistryDodecylsulfonic acid
Owner:QINGDAO WENSHENG AUTOMOBILE COMPONENTS & PARTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products