A technology of rolling copper foil and production process, which is applied in the field of production process of rolling copper foil for lithium batteries, can solve problems such as low elongation, lower yield, and difficulty in achieving balance, and achieve increased elongation, increased yield, and balanced sex good effect

Active Publication Date: 2015-11-18
江苏富威科技股份有限公司
View PDF6 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As the cathode current collector of lithium-ion batteries, copper foil has high performance requirements, and the balance is difficult to achieve. The performance of the existing electrolytic copper foil is unstable and cannot meet the performance requirements of copper foil for lithium-ion battery production.
In addition, in the existing technology, the copper content of general-purpose electrolytic copper foil is ≥99.98%, showing a hard Y state, the tensile strength is ≥350MPa, and the elongation is ≥8%. Pressing, although it is a slight change, but the low elongation often causes the copper foil to break and reduce the yield

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The rolled copper foil for lithium batteries of this embodiment is obtained by the following steps in sequence:

[0025] (1) Selection of raw materials. The qualified oxygen-free copper casting slab of TU2 obtained by horizontal continuous casting process is selected as the raw material. In this embodiment, the thickness of the oxygen-free copper casting slab used as raw material is 16.3mm;

[0026] (2) Rough rolling, the oxygen-free copper casting slab is subjected to multi-pass rough rolling to obtain a copper strip slab. Here, a four-roll reversible rolling mill is used for rough rolling, and the rough rolling speed is controlled between 2.3m / s and 3.6m / s. The thickness of the 16.3mm oxygen-free copper billet is successively changed to 10.5mm through multiple passes of rough rolling. —6.5mm—3.5mm—2.0mm—0.8mm—0.53mm, that is, the thickness of the copper strip blank after rough rolling is 0.53mm;

[0027] (3) Intermediate annealing, the copper strip blank obtained by ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a production technology for rolled copper foil for a lithium battery. Rough rolling, intermediate annealing, intermediate rolling, semi-finished product annealing, finished product rolling, anti-sticking agent spraying, finished product annealing, finished product cleaning and splitting processing are conducted on a selected TU2 anaerobic copper casting blank, then the rolled copper foil for the lithium battery is obtained, and the content of copper of the copper foil product is larger than 99.97%, the copper foil is in a soft state M, the tensile strength of the copper foil is larger than or equal to 140 MPa, ductility is larger than or equal to 10%, and electrical conductivity is larger than or equal to 100% of the IACS. The performance movement and balance of the copper foil are good, most obviously, ductility is improved, so that in the production technology of the lithium ion battery production technology, the copper foil is not prone to being broken when being pressed, and the finished product rate is increased.

Description

technical field [0001] The invention relates to a production process of rolled copper foil for lithium batteries. Background technique [0002] In recent years, with the rapid development of global mobile terminal equipment, the country has vigorously supported new energy electric vehicles, and the demand for lithium batteries has also expanded rapidly. Copper foil is one of the key materials for the production of lithium-ion batteries, and its quality directly affects the manufacturing process and overall performance of lithium-ion batteries. As the cathode current collector of lithium-ion batteries, copper foil has high performance requirements, and it is difficult to achieve a balance. The performance of the existing electrolytic copper foil is unstable and cannot meet the performance requirements of copper foil for lithium-ion battery production. In addition, in the existing technology, the copper content of general-purpose electrolytic copper foil is ≥99.98%, showing...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B21B1/40C21D1/26
Inventor 苏平殷明亮胡龙龙
Owner 江苏富威科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap