Metal hydroxide coated carbon and sulfur lithium-sulfur battery positive electrode material, and preparation method and application thereof

A hydroxide and lithium-sulfur battery technology, applied in battery electrodes, nanotechnology for materials and surface science, secondary batteries, etc., can solve the problems of cumbersome preparation process, high price, and difficulty in industrialization, and achieve Simple process, low price, and good electrochemical performance

Active Publication Date: 2015-12-02
杭州亿昇达新能源科技有限公司
View PDF10 Cites 33 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, whether it is graphene, graded porous carbon or polymer polymers, the preparation process of these materials is relatively cumbersome, requires strict control of temperature, pH value, atmosphere, etc., and is expensive, and it is still difficult to achieve industrialization.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Metal hydroxide coated carbon and sulfur lithium-sulfur battery positive electrode material, and preparation method and application thereof
  • Metal hydroxide coated carbon and sulfur lithium-sulfur battery positive electrode material, and preparation method and application thereof
  • Metal hydroxide coated carbon and sulfur lithium-sulfur battery positive electrode material, and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] 1) Uniformly grind sublimated sulfur and conductive carbon black in a mortar with a mass ratio of 3:2, heat-treat and melt mix at 155°C for 12 hours in an argon protective atmosphere, and grind to obtain sulfur-carbon black composite powder after cooling;

[0038] 2) Co(NO 3 ) 2 ·6H 2 O, hexamethylenetetramine is dissolved in water, then add polyvinylpyrrolidone and the sulfur carbon black composite powder in step 1), vigorously stir and ultrasonically form a black mixed solution, the concentration of cobalt salt in the black mixed solution is 0.05mol / L, the concentration of hexamethylenetetramine is 0.025mol / L, the concentration of polyvinylpyrrolidone is 0.1g / L, the concentration of sulfur carbon black composite powder is 10g / L, this black mixed solution is poured in the reactor, Hydrothermal reaction at 90°C for 2 hours, after cooling, centrifuge with deionized water, and dry in air at 60°C for 24 hours to obtain a lithium-sulfur battery cathode material coated wi...

Embodiment 2

[0044] 1) Uniformly grind sublimated sulfur and conductive carbon black in a mortar with a mass ratio of 3:2, heat-treat and melt mix at 155°C for 12 hours in an argon protective atmosphere, and grind to obtain sulfur-carbon black composite powder after cooling;

[0045] 2) Ni(NO 3 ) 2 ·6H 2 O, hexamethylenetetramine is dissolved in water, then add polyvinylpyrrolidone and the sulfur carbon black composite powder in step 1), vigorously stir and ultrasonic, form black mixed solution, the concentration of nickel salt in the black mixed solution is 0.05mol / L, the concentration of hexamethylenetetramine is 0.025mol / L, the concentration of polyvinylpyrrolidone is 0.1g / L, the concentration of sulfur carbon black composite powder is 10g / L, this black mixed solution is poured in the reactor, Hydrothermal reaction at 100°C for 2 hours, after cooling, centrifuge with deionized water, and dry in air at 60°C for 24 hours to obtain a lithium-sulfur battery positive electrode material co...

Embodiment 3

[0051] 1) Uniformly grind sublimated sulfur and conductive carbon black in a mortar with a mass ratio of 7:3, heat-treat and melt mix at 155°C for 12 hours in an argon protective atmosphere, and grind to obtain sulfur-carbon black composite powder after cooling;

[0052] 2) Co(NO 3 ) 2 ·6H 2 O, hexamethylenetetramine is dissolved in water, then add polyvinylpyrrolidone and the sulfur carbon black composite powder in step 1), vigorously stir and ultrasonically form a black mixed solution, the concentration of cobalt salt in the black mixed solution is 0.05mol / L, the concentration of hexamethylenetetramine is 0.025mol / L, the concentration of polyvinylpyrrolidone is 0.1g / L, the concentration of sulfur carbon black composite powder is 10g / L, this black mixed solution is poured in the reactor, Hydrothermal reaction at 90°C for 2 hours, after cooling, centrifuge with deionized water, and dry in air at 60°C for 24 hours to obtain a lithium-sulfur battery cathode material coated wi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
pore sizeaaaaaaaaaa
sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a metal hydroxide coated carbon and sulfur lithium-sulfur battery positive electrode material, and a preparation method and an application thereof. The preparation method comprises the following steps: uniformly grinding sublimed sulfur and conductive carbon black, and carrying out heat treatment fusion for uniform mixing to obtain sulfur and carbon black composite powder; and dissolving metal salt and hexamethylenetetramine in water, adding polyvinylpyrrolidone and the sulfur and carbon black composite powder, stirring, carrying out ultrasonic treatment to obtain a black mixed liquor, carrying out hydrothermal treatment on the black mixed liquor at 80-100DEG C for 2-5h, cooling, centrifuging, and drying to obtain the material. The metal hydroxide coated carbon and sulfur lithium-sulfur battery positive electrode material prepared in the invention inhibits the shuttle effect of polysulfide, improves the conductive performance of sulfur, and improves the cycle performances of batteries. The metal hydroxide coated carbon and sulfur lithium-sulfur battery positive electrode material is used to make a lithium-sulfur positive electrode, the lithium-sulfur positive electrode is applied in a lithium-sulfur battery, and the lithium-sulfur battery has high capacity and protruding cycle performances.

Description

technical field [0001] The invention relates to the field of preparation of lithium-sulfur battery positive electrode materials, in particular to a lithium-sulfur battery positive electrode material with metal hydroxide-coated carbon and sulfur, a preparation method and application thereof. Background technique [0002] The crisis of non-renewable energy sources such as fossil fuels is inevitable, and the environmental pollution caused by fossil fuels has become a global problem. Therefore, the development of non-polluting new energy sources is imminent. Energy saving and environmental protection requirements have promoted the development of electric vehicles. The application of electric vehicles requires the power batteries used to have high energy and power density, long service life and acceptable safety performance. Today, lithium-ion batteries have been widely used in portable electronic devices, but traditional lithium-ion batteries, such as commercialized LiCoO 2 The...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/38H01M4/62H01M10/0525B82Y30/00B82Y40/00
CPCB82Y30/00B82Y40/00H01M4/38H01M4/625H01M4/628H01M10/0525Y02E60/10
Inventor 王秀丽牛晓青涂江平夏新辉谷长栋
Owner 杭州亿昇达新能源科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap