A kind of cationic polyurethane resin for water-based wood primer and preparation method thereof
A polyurethane resin, cationic technology, applied in the direction of polyurea/polyurethane coatings, coatings, etc., can solve the problems of water resistance and adhesion defects, high synthesis difficulty, and achieve excellent anti-bleeding oil and anti-pigment bleed performance, moisturizing Good wettability and good emulsion stability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
preparation example Construction
[0039] refer to figure 1 , a kind of preparation method that the present invention proposes is used for waterborne woodware primer cationic polyurethane resin, comprises the following steps:
[0040] S1, heating and melting the polyester diol, keeping it warm, and then vacuum dehydrating to obtain the macromolecular polyester diol A1;
[0041] S2. Add diisocyanate to macromolecular polyester diol A1, heat up, keep warm, add non-hydrophilic small molecule chain extender, crosslinking agent and acetone after cooling down, then add catalyst, heat up, keep warm, and obtain a prepolymer A2;
[0042] S3. After cooling the prepolymer A2, dropwise add a solution containing a cationic hydrophilic chain extender, heat up, and keep warm to obtain the prepolymer A3;
[0043] S4. After neutralizing the prepolymer A3, add water for emulsification and dispersion, and vacuum distillation to obtain a cationic polyurethane resin for water-based wood primer.
Embodiment 1
[0046] A kind of preparation method that the present invention proposes is used for waterborne woodware primer cationic polyurethane resin, comprises the following steps:
[0047] S1. Heat 20 parts by weight of terephthalic anhydride polyester diol with a number average molecular weight of 3200 to 140° C. to melt, keep it warm for 1 hour, and then vacuum dehydrate to obtain macromolecular polyester diol A1;
[0048] S2. Add 33 parts of diphenylmethane diisocyanate to macromolecular polyester diol A1, raise the temperature to 112°C, keep it warm for 1 hour, cool down to 60°C, add 6 parts of 1,4-butanediol and 3 parts of trihydroxy Methyl propane and 20 parts of acetone, then add 0.3 part of stannous octoate, heat up to 55 ° C, keep warm for 4 hours, and obtain prepolymer A2;
[0049] S3. After cooling the prepolymer A2 to 30°C, add dropwise a solution containing a cationic hydrophilic chain extender, wherein the solution containing a cationic hydrophilic chain extender consists...
Embodiment 2
[0052] A kind of preparation method that the present invention proposes is used for waterborne woodware primer cationic polyurethane resin, comprises the following steps:
[0053] S1. Mix 50 parts by weight of terephthalic anhydride polyester diol with a number average molecular weight of 2500 and 26 parts of polyadipate-1,4-butylene glycol with a number average molecular weight of 1000 Afterwards, heat up to 70°C to melt, keep warm for 5 hours, and then vacuum dehydrate to obtain macromolecular polyester diol A1;
[0054] S2. Add 52 parts of 4,4-dicyclohexylmethane diisocyanate into macromolecular polyester diol A1, raise the temperature to 65°C, keep it warm for 4 hours, cool down to 40°C, add 11 parts of neopentyl glycol, 2 parts of three Methylol propane and 30 parts of acetone, then add 0.05 part of dibutyltin dilaurate, heat up to 90°C, keep warm for 1 hour, and obtain prepolymer A2;
[0055] S3. After cooling the prepolymer A2 to 40°C, add dropwise a solution containin...
PUM
Property | Measurement | Unit |
---|---|---|
particle size | aaaaa | aaaaa |
water absorption | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap