A method for manufacturing a roll-pressed non-asbestos composite board

A manufacturing method and technology for composite panels, which are applied in the fields of heat preservation, heat insulation, insulation and compression resistant panels, can solve the problems of substandard strength and low performance of heat insulation and heat preservation materials, and achieve the effects of high elasticity and good recovery force.

Active Publication Date: 2018-04-06
NINGBO HAISHAN CLORING SEALING PROD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Solve the problem that the existing asbestos substitute board heat insulation material has low performance and the strength cannot meet the standard

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] Example 1: A method for manufacturing a roll-pressed asbestos-free composite board, comprising the following steps: Step A): In parts by weight, take 10 parts of nitrile rubber and 10 parts of 244 neoprene rubber, and use a rubber mixer to first To described nitrile rubber mixing 1 time, then to described 244 neoprene rubber mixing 3 times, then described nitrile rubber and described 244 neoprene mixing rubber mixing, obtain parts by weight as 20 parts of film, and the thickness of the film is not more than 0.5mm. During the rubber mixing process, the temperature of the rollers in the rubber mixing machine is not higher than 55 ° C. Finally, take 35 parts of toluene solution and put the film Put it into the toluene solution and soak for at least 48 hours until the film is completely swollen to form a glue; Step B): In parts by weight, take 20 parts of the glue and 5 parts of the Put the toluene solution into the mixer, and the mixer alternately performs forward and reve...

Embodiment 2

[0014]Example 2: A method for manufacturing a roll-pressed asbestos-free composite board, comprising the following steps: Step A): In parts by weight, take 10 parts of nitrile rubber and 10 parts of 244 neoprene rubber, and use a rubber mixer to first To described nitrile rubber mixing 1 time, then to described 244 neoprene rubber mixing 3 times, then described nitrile rubber and described 244 neoprene mixing rubber mixing, obtain parts by weight as 20 parts of film, and the thickness of the film is not more than 0.5mm. During the rubber mixing process, the temperature of the rollers in the rubber mixing machine is not higher than 55 ° C. Finally, take 35 parts of toluene solution and put the film Put it into the toluene solution and soak for at least 48 hours until the film is completely swollen to form a glue; Step B): In parts by weight, take 20 parts of the glue and 5 parts of the Put the toluene solution into the blender, and the blender alternately performs forward and r...

Embodiment 3

[0015] Example 3: A method for manufacturing a roll-pressed asbestos-free composite board, including the following steps: Step A): In parts by weight, take 10 parts of nitrile rubber and 10 parts of 244 neoprene rubber, and use a rubber mixer to first To described nitrile rubber mixing 1 time, then to described 244 neoprene rubber mixing 3 times, then described nitrile rubber and described 244 neoprene mixing rubber mixing, obtain parts by weight as 20 parts of film, and the thickness of the film is not more than 0.5mm. During the rubber mixing process, the temperature of the rollers in the rubber mixing machine is not higher than 55 ° C. Finally, take 35 parts of toluene solution and put the film Put it into the toluene solution and soak for at least 48 hours until the film is completely swollen to form a glue; Step B): In parts by weight, take 20 parts of the glue and 5 parts of the Put the toluene solution into the mixer, and the mixer is alternately forward and reverse eve...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
porosityaaaaaaaaaa
Login to View More

Abstract

A method for manufacturing a roll-pressed non-asbestos composite board, relating to a composite board, comprising 9 steps, the main feature is to prepare a large material layer from toluene, nitrile rubber, 244 neoprene, mineral fiber and aramid fiber; Leather prepared from toluene, nitrile rubber, 244 neoprene, zinc oxide, stearic acid, 2‑mercaptobenzothiazole, N‑phenyl‑2‑naphthylamine, talc, light calcium and mineral fibers layer; and then use the rolling method to roll the five layers of large material layer, leather material layer, support layer, leather material layer and large material layer into a composite board. Compared with the prior art, the beneficial effect of the present invention is that the composite board manufactured by the method of the present invention has the performance of heat insulation, insulation and heat preservation not inferior to asbestos boards, and at the same time, compared with other thermal insulation boards, the composite board is also It has the characteristics of compression resistance, extrusion resistance, high elasticity and good resilience. It solves the problem that the performance of the existing asbestos substitute board heat insulation material is low, and the strength cannot reach the standard.

Description

technical field [0001] The invention relates to a composite plate, in particular to a thermal insulation, insulation, heat insulation and compression resistant plate which can replace the asbestos plate. Background technique [0002] Now most of the pressure-resistant panels used for heat insulation, insulation and heat preservation are usually panels made of asbestos. Asbestos panels have been used for more than 100 years. Countries have legally or de facto banned and restricted the use of panels containing asbestos. In order to replace asbestos boards, various non-asbestos boards have been launched one after another. At present, most of the so-called non-asbestos fiber boards in China are made of sepiolite as the main material. However, sepiolite is a material symbiotic with asbestos, so it is not recognized by foreign companies and environmental protection organizations. At the same time, the performance of sepiolite products is also low, especially the leakage rate and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B37/02B32B25/04B32B25/14B32B15/06B32B15/18C08L9/02C08L11/00C08K13/04C08K7/08C08K7/10C08K3/22C08K5/47C08K3/34C08K3/26C08K5/18B29D7/00
Inventor 施燕君
Owner NINGBO HAISHAN CLORING SEALING PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com